A wire, strip or reshaped part is produced from an alloy based on platinum, palladium or a mixture of platinum and palladium and hardened by oxide dispersion. The wire, strip or reshaped part cross-section exhibits a peripheral zone in which at least one relatively easily volatilized oxide generator is depleted by at least 25%. In addition, a process is provided for production of such a wire, strip or reshaped part, in which a porous skin is produced thermally on the wire, strip or reshaped part, and the porous skin is compacted by conversion into a soft or impermeable skin.
摘要:
An electrode system with a current feedthrough through a ceramic discharge vessel is provided which, on one hand, increases the visible output of lamps and, on the other hand, allows smaller dimensions. For this purpose, the current feedthrough is made of rhenium or a platinum-group metal. In this way, improved color reproduction is also achievable. In preferred embodiments: (a) the current feedthrough is made of rhenium or a rhenium alloy or a platinum-group metal or a platinum-group metal alloy and the current feedthrough is brazed flush in the discharge vessel, (b) the discharge vessel has no shaft, and/or (3) the current feedthrough is in the form of one or more joined spheres.
摘要:
An electrode system with a current feedthrough through a ceramic discharge vessel is provided which, on one hand, increases the visible output of lamps and, on the other hand, allows smaller dimensions. For this purpose, the current feedthrough is made of rhenium or a platinum-group metal. In this way, improved color reproduction is also achievable. In preferred embodiments: (a) the current feedthrough is made of rhenium or a rhenium alloy or a platinum-group metal or a platinum-group metal alloy and the current feedthrough is brazed flush in the discharge vessel, (b) the discharge vessel has no shaft, and/or (3) the current feedthrough is in the form of one or more joined spheres.
摘要:
A wire is provided for producing a sliding contact, wherein at least an inner core of the wire consists of a copper-silver alloy. A sliding contact is also provided having at least one such wire, wherein a counter-contact is provided whose conductive surface has at least one of the wires touch against it. The spring force of the wire acting on the conductive surface of the counter-contact effects electrical contacting between the wire and the counter-contact and the counter-contact is mobile with respect to the wire, such that the surface of the wire slides over the counter-contact when the counter-contact moves. Components having the sliding contact are also provided, including a potentiometric sensor, potentiometer, sliding dolly regulator, position sensor, rotary switch, electrical motor, generator, wind turbine, slip ring system, actuator, or current collector.
摘要:
A solid body of a metal alloy comprising less than 99% by weight of noble metal and more than 1% by weight of dispersion-strengthening metals is converted for production of a dispersion-strengthened platinum material by at least 90% oxidation of the dispersion-strengthening metals into a dispersion-strengthened platinum material. The dispersion-strengthened platinum material contains a noble metal component of platinum or a platinum alloy amounting to between 95 and 99% by weight and a dispersion-strengthening agent. The noble metal component includes at least 55% by weight Pt, 0 to 30% by weight Rh, 0 to 30% by weight Au, and 0 to 40% by weight Pd. The remaining proportion by mass of more than 1% by weight is a dispersion-strengthening agent, which contains at least one metal oxidized at least 90% by weight with oxygen, the metal being selected from the group of Ce, Zr, Sc, and Y.
摘要翻译:将包含小于99重量%的贵金属和大于1重量%的分散强化金属的金属合金的固体转化为通过分散强化金属的至少90%的氧化来生产分散强化的铂材料, 将金属加强成分散强化的铂材料。 分散强化的铂材料含有铂或铂合金的贵金属组分,其含量为95-99%(重量),和分散强化剂。 贵金属组分包括至少55重量%的Pt,0至30重量%的Rh,0至30重量%的Au和0至40重量%的Pd。 剩余的重量比大于1%的分散强化剂是含有至少一种与氧氧化至少90重量%的金属的分散强化剂,该金属选自Ce,Zr,Sc和 Y.
摘要:
A metal fiber based on one or several elements from the group of platinum, palladium, rhodium, ruthenium, and iridium with 0 to 30% by weight of one or several additional alloy elements from the group of nickel, cobalt, gold, rhenium, molybdenum, and tungsten, contains 1 to 500 ppm by weight of boron or phosphorus. A non-woven material or netting, in particular for the production of nitrogen oxide or for the production of hydrocyanic acid, is made of such fibers. For the production of fibers based on noble metals having up to 30% by weight of additional alloy metals by drawing the fibers from a melt, the melting point of the metal is reduced by at least 400 ° C., before drawing of the fibers, by additionally alloying with boron or phosphorus, and the boron or the phosphorus is removed again from the fibers.
摘要:
A hydrogen permeation membrane including a niobium alloy with 5-25 wt. % of at least one element from the group consisting of palladium, ruthenium, rhenium, platinum, gold, and rhodium.
摘要:
Methods for reducing the evaporation rate of platinum and Pt alloys upon their use at high temperatures >1,200° C. in an oxidizing atmosphere include the steps: (A) providing a component made of platinum or a platinum alloy; (B) wrapping the outer surface of the component with a flexible bandage having open porosity and provided with an oxide ceramic material and/or a glass-forming material; (C) using the component at operating temperatures >1,200° C. Methods for scavenging noble metal oxides evaporating or sublimating from the surface of platinum or Pt alloys include: (A) providing a component made of platinum or a platinum alloy; (B) wrapping the outer surface of the component with a flexible bandage having open porosity; and (C) using the component at operating temperatures >1,200° C. Correspondingly wrapped components are also provided.
摘要:
Castings made of boron-containing alloys based on at least one platinum group metal are treated by thermal ageing in the presence of oxygen and at temperatures below the melting point of the alloy. This enables the alloys to be processed at temperatures customary in the jewelry industry. The treated castings can also be processed into medical technology products.
摘要:
The addition of 0.5 to 30 ppm boron and 0.5 to 20 ppm calcium to iridium and the Zr- and Hf-free alloys thereof and rhodium and the Zr- and Hf-free alloys thereof surprisingly increases the creep rupture strength at high temperatures, in particular around 1,800° C.