摘要:
An apparatus for polishing wafers and a process for polishing wafers are provided. The apparatus for polishing a wafer which polishes the wafer W held by a carrier plate which rotates around an axis, by pressing and rubbing the wafer to a polishing pad disposed to a polishing platen 12 which rotates around another axis which differs from said axis, in which the polishing pad 11 is equipped with plural areas including a first area 11a and a second area 11b having hardness different from each other, each of the first 11a area and second area 11b being formed at a distribution and/or an area ratio such that the rate of the time or distance that the wafer W passes through the first area 11a during polishing to the time or distance that the wafer W passes through the second area 11b during polishing becomes a predetermined value.
摘要:
An object of the present invention is to provide a method for etching a single wafer, which effectively realizes a high flatness of wafer and an increase in productivity thereof. In a method for etching a single wafer, a single thin disk-like wafer sliced from a silicon single crystal ingot is spun, and a front surface of the wafer is etched with an etching solution supplied thereto. In the method, a plurality of supply nozzles are disposed above and opposite to the front surface of the wafer at different portions in the radial direction of the wafer, respectively; and then one or more conditions selected from the group consisting of temperatures, kinds, and supply flow rates of etching solutions from the plurality of supply nozzles are changed.
摘要:
An object of the present invention is to provide a single wafer etching apparatus realizing a high flatness of wafers and an increase in productivity thereof. In the single wafer etching apparatus, a single thin disk-like wafer sliced from a silicon single crystal ingot is mounted on a wafer chuck and spun thereon, and an overall front surface of the wafer is etched with an etching solution supplied thereto by centrifugal force generated by spinning the wafer 11. The singe wafer etching apparatus includes a plurality of supply nozzles 26, 27 capable of discharging the etching solution 14 from discharge openings 26a, 27a onto the front surface of the wafer 11, nozzle-moving devices each capable of independently moving the plurality of supply nozzles 28, 29, and an etching solution supplying device 30 for supplying the etching solution 14 to each of the plurality of supply nozzles and discharging the etching solution 14 from each of the discharge openings to the front surface of the wafer 11.
摘要:
An alkali etchant for controlling surface roughness of a semiconductor wafer, which is a sodium hydroxide solution or a potassium hydroxide solution having a weight concentration of 55 wt % to 70 wt %.
摘要:
A process for producing a silicon wafer comprising a single-wafer etching step of performing an etching by supplying an etching solution through a supplying-nozzle to a surface of a single and a thin-discal wafer obtained by slicing a silicon single crystal ingot and rotating the wafer to spread the etching solution over all the surface of the wafer; and a grinding step of grinding the surface of the wafer, in this order, wherein the etching solution used in the single-wafer etching step is an aqueous acid solution which contains hydrogen fluoride, nitric acid, and phosphoric acid in an amount such that the content of which by weight % at a mixing rate of fluoric acid:nitric acid:phosphoric acid is 0.5 to 40%:5 to 50%:5 to 70%, respectively.
摘要:
The manufacturing method of the present invention provides a silicon wafer, both sides of the wafer having a highly accurate flatness and small surface roughness, which is a single surface mirror-polished wafer with the front and rear surfaces of the wafer identifiable by visual observation, and excellent in flatness when held by a stepper chuck and the like. The manufacturing method of the present invention includes an etching process, a lapping process, and a double surface polishing process to simultaneously polish the front and rear surfaces of a wafer after the etching process. The polishing removal depth (A) of the wafer front surface is 5 to 10 μm in the double surface simultaneous polishing process, and the polishing removal depth (B) in the rear surface is 2 to 6 μm, and a difference between the polishing removal depth A and the polishing removal depth B is 3 to 4 μm.
摘要:
An object of the present invention is to provide a method for etching a single wafer, which effectively realizes a high flatness of wafer and an increase in productivity thereof. In a method for etching a single wafer, a single thin disk-like wafer sliced from a silicon single crystal ingot is spun, and a front surface of the wafer is etched with an etching solution supplied thereto. In the method, a plurality of supply nozzles are disposed above and opposite to the front surface of the wafer at different portions in the radial direction of the wafer, respectively; and then one or more conditions selected from the group consisting of temperatures, kinds, and supply flow rates of etching solutions from the plurality of supply nozzles are changed.
摘要:
A method for manufacturing a silicon wafer comprises a slicing step of a silicon single crystal ingot to obtain sliced wafers, a single-side grinding step to grind only one side of a wafer, and a smoothing step to smooth the other side of the wafer by controlling application of etchant depending on surface profile of the other side of the wafer. According to a method of the present invention a silicon wafer that has high flatness, is removed machine working damage, and is reduced of profile change of chamfer to be minimal can be manufactured.
摘要:
The processing method of a silicon wafer of the present invention includes an etching process (13) in which acid etching solution and alkali etching solution are stored in plural etching tanks, respectively and a wafer having degraded superficial layers gone through a cleaning process (12) subsequent to a lapping process (11) is immersed into the acid etching solution and the alkali etching solution in order, a front surface mirror-polishing process (18) to mirror-polish one surface of the etched wafer, and a cleaning process (19) to clean the front surface mirror-polished wafer, wherein the etching process is performed by the alkali etching after the acid etching, and wherein the acid etching solution contains phosphoric acid equal to or more than 30 percent by weight in the acid aqueous water solution 100 percent by weight mainly composed of hydrofluoric acid and nitric acid. The processing method of the present invention maintains the flatness after lapping, and at the same time, can reduce the surface roughness. Further, in the wafer in which the front surface is mirror-polished, a good flatness is obtained, and moreover, the rear surface roughness becomes small.
摘要:
A method for manufacturing an epitaxial wafer that can reduce occurrence of a surface defect or a slip formed on an epitaxial layer is provided. The manufacturing method is characterized by comprising: a smoothing step of controlling application of an etchant to a wafer surface in accordance with a surface shape of a silicon wafer to smooth the wafer surface; and an epitaxial layer forming step of forming an epitaxial layer formed of a silicon single crystal on the surface of the wafer based on epitaxial growth.