摘要:
Provided is an ethylene copolymer having 40 wt. % to 70 wt. % of units derived from ethylene and at least 30 wt. % of units derived from at least one α-olefin having 3 to 20 carbon atoms and has the following properties: (a) a weight-average molecular weight (Mw), as measured by GPC, in the range of about 50,000 to about 200,000 g/mol; (b) a melting point (Tm) in ° C., as measured by DSC, that satisfies the relation: Tm>3.4×E−180 where E is the weight % of units derived from ethylene in the copolymer; (c) a ratio of Mw/Mn of about 1.8 to about 2.5; (d) a content of Group 4 metals of no more than 5 ppm; and (e) a ratio of wt ppm Group 4 metals/wt ppm Group 5 metals of at least 3. Also provided are methods for making an ethylene copolymer and compositions comprising an ethylene copolymer.
摘要:
This invention relates to an in-reactor polymer blend comprising: (a) a first ethylene-containing polymer having a density of greater than 0.90 g/cm3 and a Mw of more than 20,000 g/mol and (b) a second ethylene-containing polymer having a density of less than 0.90 g/cm3 wherein the polymer blend has a Tm of at least 90° C. (DSC second melt), a density of less than 0.92 g/cm3, and the densities of the first and second polymers differ by at least 1%.
摘要翻译:本发明涉及一种反应器内聚合物共混物,其包含:(a)密度大于0.90g / cm 3,Mw大于20,000g / mol的第一含乙烯聚合物和(b)第二含乙烯的聚合物 聚合物的密度小于0.90g / cm 3,其中聚合物共混物具有至少90℃的Tm(DSC第二熔体),小于0.92g / cm 3的密度和第一和第二聚合物的密度 至少1%不等。
摘要:
A homogeneous polymer blend comprises a thermoplastic first polymer having a crystallinity of at least 30%; and a second polymer having a crystallinity of more than 5% and being at least partially cross-linked.
摘要:
The present invention also discloses a heterogeneous blend composition comprising; a) from 1% to 99% by weight of the blend of a first polymer component comprising a copolymer of 5% to 35% by weight of the first polymer component consisting predominantly of alpha olefin derived units and 65% to 95% by weight of the first polymer component of propylene derived units having a crystallinity of 0.1% to about 25% from isotactic polypropylene sequences, a melting point of from 45° C. to 105° C., and wherein the Melt Flow Rate (MFR@230° C.) of the first polymer component is between 300 g/10 min to 5000 g/10 min b) from 1% to 99% by weight of the blend of a second polymer component comprising isotactic polypropylene and random copolymers of isotactic propylene, wherein the percentage of the copolymerized alpha-olefin in the copolymer is between 0.0% and 9% by weight of the second polymer component and wherein the second polymer component has a melting point greater than about 110° C., wherein the first polymer component has less than 1000 ppm of reaction products arising from the chemical reaction of a molecular degradation agent.
摘要:
This invention relates to a propylene polymer comprising a component having a crystallinity of 10% or less and a component having a crystallinity of 20% or more, said propylene polymer having: a) a melting point of X° C. or more where X=−0.0038(Tp)2+0.36(Tp)+150, where Tp is the temperature of polymerization in ° C.; b) an Mw of 10,000 g/mol or more; c) a heat of fusion of from 1-70 J/g; d) Stereodefects per 10,000 monomer units of Y or less where Y=2.35(Tp)−100 (where Tp is the temperature of polymerization in ° C.) for the portion of the blend that is insoluble in hexane at 23° C.; e) a dot T-Peel on Kraft paper of 1 N or more; and f) a branching factor of 0.98 or less, where the branching factor is the ratio of g′ measured at Mz to g′ measured at Mw, and process to produce such polymers.
摘要:
This invention relates to the preparation of thermoplastic vulcanizates (TPVs) with unique morphological features, more specifically, this invention relates to a method for preparing TPV compositions wherein the mixing of plastomers and elastomers are carried out in solvent with curatives to induce cross-linking.
摘要:
This invention relates to processes to produce liquid poly-alpha-olefins (PAOs) having a kinematic viscosity at 100° C. of more than 20 cSt in the presence of a metallocene catalyst with a non-coordinating anion activator and hydrogen.
摘要:
This invention relates to a process to polymerize olefins comprising contacting a catalyst or catalyst system with olefin(s) in the presence of a fluorocarbon at a temperature above the onset melting point of the polymer.This invention also relates to a solution process to polymerize olefins comprising contacting a catalyst or catalyst system with olefin(s) in the presence of a fluorocarbon at a temperature above the onset melting point of the polymer.
摘要:
In a process for producing a propylene-based olefin homopolymer or copolymer, a monomer composition comprising propylene is contacted with a polymerization catalyst system under homogeneous polymerization conditions (such as solution, supersolution or supercritical conditions), wherein the polymerization catalyst system includes an activator and a bridged bis-indenyl transition metal (group 4) compound substituted with a carbazole (unsubstituted or substituted) at the 4 position.
摘要:
This invention relates to a multiple phase polymerization process to produce polyolefins comprising contacting olefins and a homogeneous catalyst or catalyst system at a temperature between the melting point of the dry polymer and 80° C. below the melting point of the dry polymer in the presence of a fluorinated hydrocarbon. This invention also relates to a process to produce polyethylene comprising contacting a homogeneous catalyst or catalyst system with ethylene and from 0 to 40 weight % of one or more C3 to C40 olefin comonomer(s) in the presence of a fluorinated hydrocarbon and optionally a hydrocarbon solvent at a temperature below the reaction medium melting point. This invention also relates to a process to produce polypropylene comprising contacting a homogeneous catalyst or catalyst system with propylene and from 0 to 50 weight % of one or more of ethylene and C4 to C40 olefin comonomer(s) in the presence of a fluorinated hydrocarbon and optionally a hydrocarbon solvent at a temperature below the reaction medium melting point.