摘要:
A production method for producing molded articles from fiber composites, superparamagnetic particles are selected which become coupled to an external alternating magnetic field. These superparamagnetic particles are added to a resin portion of a strip-shaped starting material further comprising reinforcing fibers. The strip-shaped starting material is then continuously advanced, and, while being advanced, heated by coupling-in an external alternating magnetic field to which the superparamagnetic particles in the resin portion become coupled. Next, the heated starting material is continuously molded into a molded article; and the resin portion in the molded particle is cured.
摘要:
A pipe or hose composed of a polyamide moulding composition whose molecular weight has been increased by condensation, via addition of a compound having at least two carbonate units in a quantitative proportion of from 0.005 to 10% by weight, based on polyamide, where a) a starting polyamide moulding composition was provided, b) a mixture of the starting polyamide moulding composition and of the compound having at least two carbonate units was produced, c) the premix was, if desired, stored and/or transported, and d) the premix was then processed to give the moulding, this step being the first in which the increase of molecular weight by condensation occurred, the moulding being a pipe or hose whose external diameter is at least 25 mm is used as inliner for a pipeline.
摘要:
A pipe or hose composed of a polyamide moulding composition whose molecular weight has been increased by condensation, via addition of a compound having at least two carbonate units in a quantitative proportion of from 0.005 to 10% by weight, based on polyamide, where a) a starting polyamide moulding composition was provided, b) a mixture of the starting polyamide moulding composition and of the compound having at least two carbonate units was produced, c) the premix was, if desired, stored and/or transported, and d) the premix was then processed to give the moulding, this step being the first in which the increase of molecular weight by condensation occurred, the moulding being a pipe or hose whose external diameter is at least 25 mmis used as inliner for a pipeline.
摘要:
Components made from at least two molded materials A and B which are firmly bonded together, and in whicha) the molded material A is composed of a matrix of polyamide or of a polyamide-containing molding composition and of a continuous, fibrous reinforcement embedded therein, andb) the molded material B is the rubber obtained after peroxidic vulcanization of a rubber composition which is applied to A, the rubber composition containing the following components:i) about 100 parts by weight of a rubber having carboxyl or anhydride functional groups;ii) about 10 to 300 parts by weight of fillers; andiii) about 1 to 10 parts by weight of peroxidic vulcanizing agents.
摘要:
A multilayered lightweight building board, comprising a support core, two cover layers on the support core, where the support core is made of laterally fused-together tubes. The tubes have an inner layer, and an outer layer, where the outer layer has a softening point 10-90.degree. C. lower than the softening point of the inner layer. The lightweight building board is made from compatible thermoplastic materials, so they can be mechanically recycled by the customary processing methods for thermoplastics.
摘要:
In a production method for producing molded articles from fiber composites, superparamatic particles are selected which become coupled to an external alternating magnetic field. These superparamagnatic particles are added to a resin portion of a strip-shaped starting material further comprising reinforcing fibers. The strip-shaped starting material is then continuously advanced, and, while being advanced, heated by coupling-in an external alternating magnetic field to which the superparamagnatic particles in the resin portion become coupled. Next, the heated starting material is continuously molded into a molded article; and the resin portion in the molded particle is cured.
摘要:
A pipe or hose composed of a polyamide moulding composition whose molecular weight has been increased by condensation, via addition of a compound having at least two carbonate units in a quantitative proportion of from 0.005 to 10% by weight, based on polyamide, where a) a starting polyamide moulding composition was provided, b) a mixture of the starting polyamide moulding composition and of the compound having at least two carbonate units was produced, c) the premix was, if desired, stored and/or transported, and d) the premix was then processed to give the moulding, this step being the first in which the increase of molecular weight by condensation occurred, the moulding being a pipe or hose whose external diameter is at least 25 mm is used as inliner for a pipeline.
摘要:
A fiber-reinforced molding composition, comprising:a) 97 to 50% by weight, relative to the sum of (a) and (b), of a mixture of 30 to 100 parts by weight of a polyphenylene ether, 0 to 70 parts by weight of a styrene polymer, 0 to 10 parts by weight of a polyoctenylene and 0.1 to 2.5 parts by weight of an .alpha.,.beta.-unsaturated carboxylic acid derivative or a precursor thereof;b) 3 to 50% by weight of carbon fibers and/or glass fibers whose surfaces bear functional groups which are capable of entering into chemical coupling reactions with the .alpha.,.beta.-unsaturated carboxylic acid derivatives; and optionallyc) dyes, pigments, plasticizers, flame retardant additives, processing auxiliaries, other customary additives or combinations thereof.