摘要:
A nanoparticle containing monoclinic lutetium oxide. A method of: dispersing a lutetium salt solution in a stream of oxygen gas to form droplets, and combusting the droplets to form nanoparticles containing lutetium oxide. The combustion occurs at a temperature sufficient to form monoclinic lutetium oxide in the nanoparticles. An article containing lutetium oxide and having an average grain size of at most 10 microns.
摘要:
A method for making a rare earth doped polycrystalline ceramic laser gain medium by hot pressing a rare earth doped polycrystalline powder where the doping concentration is greater than 2% and up to 10% and where the grain size of the final ceramic is greater than 2 μm. The polycrystalline powder can be Lu2O3, Y2O3, or Sc2O3, and the rare earth dopant can be Yb3+, Er3+, Tm3+, or Ho3+. Also disclosed is the related rare earth doped polycrystalline ceramic laser gain medium prepared by this method.
摘要:
A nanoparticle containing monoclinic lutetium oxide. A method of: dispersing a lutetium salt solution in a stream of oxygen gas to form droplets, and combusting the droplets to form nanoparticles containing lutetium oxide. The combustion occurs at a temperature sufficient to form monoclinic lutetium oxide in the nanoparticles. An article containing lutetium oxide and having an average grain size of at most 10 microns
摘要:
A nanoparticle containing monoclinic lutetium oxide. A method of: dispersing a lutetium salt solution in a stream of oxygen gas to form droplets, and combusting the droplets to form nanoparticles containing lutetium oxide. The combustion occurs at a temperature sufficient to form monoclinic lutetium oxide in the nanoparticles. An article containing lutetium oxide and having an average grain size of at most 10 microns
摘要:
A nanoparticle containing monoclinic lutetium oxide. A method of: dispersing a lutetium salt solution in a stream of oxygen gas to form droplets, and combusting the droplets to form nanoparticles containing lutetium oxide. The combustion occurs at a temperature sufficient to form monoclinic lutetium oxide in the nanoparticles. An article containing lutetium oxide and having an average grain size of at most 10 microns.
摘要:
Method of Making particles including a YAG core and a coating of sintering aid deposited thereon. The particles and agglomerates thereof maybe formed as a powder. The coated YAG-containing particles are well-suited to production of polycrystalline YAG-containing ceramics. The coated YAG-containing particles may be fabricated using a novel fabrication method which avoids the need for formation of a homogeneous powder mixture of YAG and sintering aid. The mixture may be sprayed into a drying column and dried to produce coated particles. Alternatively, the YAG particles and sintering aid or sintering aid precursor solution may be separately introduced to the drying column and dried to form coated YAG-containing particles.
摘要:
Method of Making particles including a YAG core and a coating of sintering aid deposited thereon. The particles and agglomerates thereof maybe formed as a powder. The coated YAG-containing particles are well-suited to production of polycrystalline YAG-containing ceramics. The coated YAG-containing particles may be fabricated using a novel fabrication method which avoids the need for formation of a homogeneous powder mixture of YAG and sintering aid. The mixture may be sprayed into a drying column and dried to produce coated particles. Alternatively, the YAG particles and sintering aid or sintering aid precursor solution may be separately introduced to the drying column and dried to form coated YAG-containing particles.
摘要:
A transparent polycrystalline ceramic having scattering and absorption loss less than 0.2/cm over a region comprising more than 95% of the originally densified shape and a process for fabricating the same by hot pressing. The ceramic can be any suitable ceramic such as yttria (Y2O3) or scandia (Sc2O3) and can have a doping level of from 0 to 20% and a grain size of greater than 30 although the grains can also be smaller than 30 μm. Ceramic nanoparticles can be coated with a sintering aid to minimize direct contact of adjacent ceramic powder particles and then baked at high temperatures to remove impurities from the coated particles. The thus-coated particles can then be densified by hot pressing into the final ceramic product. The invention further provides a transparent polycrystalline ceramic solid-state laser material and a laser using the hot pressed polycrystalline ceramic.
摘要:
A transparent polycrystalline ceramic having scattering and absorption loss less than 0.2/cm over a region comprising more than 95% of the originally densified shape and a process for fabricating the same by hot pressing. The ceramic can be any suitable ceramic such as yttria (Y2O3) or scandia (Sc2O3) and can have a doping level of from 0 to 20% and a grain size of greater than 30 μm, although the grains can also be smaller than 30 μm. Ceramic nanoparticles can be coated with a sintering aid to minimize direct contact of adjacent ceramic powder particles and then baked at high temperatures to remove impurities from the coated particles. The thus-coated particles can then be densified by hot pressing into the final ceramic product. The invention further provides a transparent polycrystalline ceramic solid-state laser material and a laser using the hot pressed polycrystalline ceramic.
摘要:
A method of preparing a fine powder of calcium lanthanoid sulfide is disclosed. The method includes spraying soluble calcium and lanthanoid salts into at least one precipitating solution to form a precipitate comprising insoluble calcium and lanthanoid salts, optionally, oxidizing the precipitate comprising insoluble calcium and lanthanoid salts, and sulfurizing the optionally oxidized precipitate to form a fine powder of calcium lanthanoid sulfide. An alternative method for forming the powder is by flame pyrolysis. The calcium lanthanoid sulfide powder produced by either method can have an impurity concentration of less than 100 ppm, a carbon concentration of less than 200 ppm, a BET surface area of at least 50 m2/g, and an average particle size of less than 100 nm.