摘要:
Solid supported catalysts for catalytic reduction of nitrogen oxide in waste gases utilizing ammonia as the reducing agent, the catalyst comprising at least one metallic oxide, sulfate or phosphate of a first transition metal supported on an alumina or silica-alumina carrier; the carrier containing from 0.03 to 20% by weight sulfur, based on the weight of the carrier, calculated as a sulfate or sulfite radical.
摘要:
An alumina sol, containing a small amount of water of crystallization inside the crystal lattice of boehmite, having high mechanical strength, properties suitable for use as an alumina adsorbent or carrier, and the ability to be formed without additional concentration. The alumina sol comprises a fibrous boehmite having the molecular formula Al2O3.1.05-1.30 H2O with the weight average diameter and the weight average length being respectively in the range of 3 to 50 nm and in the range of 30 to 3000 nm, and has an alumina concentration of 15 to 60% by weight.
摘要翻译:在勃姆石的晶格内部含有少量结晶水的氧化铝溶胶,具有高机械强度,适合用作氧化铝吸附剂或载体的性能,以及无需另外浓缩而形成的能力。 氧化铝溶胶包含具有分子式Al 2 O 3 .1.05-1.30H 2 O的纤维勃姆石,重均分子量和重均分子量分别为3〜50nm,范围为30〜3000nm,具有 氧化铝浓度为15〜60重量%。
摘要:
A titanium oxide sol comprising a disperse medium and generally rectangular, non-spherical particles of titanium oxide dispersed in the disperse medium, with narrow scatteres in particle size and configuration. The sol is excellent in dispersibility, long-term stability and light-resistance and, is stable in a wide pH range without causing agglomeration. Moreover, it is excellent in absorbance of ultraviolet ray and in transmittance of visible light. The sol may be prepared by a process wherein hydrogen peroxide is added to a gel or sol of hydrated titanium oxide to dissolve the hydrated titanium oxide in said gel or sol, and the resulting aqueous titanic acid solution is heated in the presence of at least one compound selected from inorganic compounds of metals belonging the Group II, III, IV, V, VI and VIII of the periodic table.
摘要:
Transparent conductive coatings excellent in transparency are provided on substrates such as glass, plastics, etc. by the use of conductive coating materials obtained by maintaining aqueous solutions of hydrolyzable tin containing or indium containing compounds at pH of 8-12, and gradually hydrolyzing said compounds in the solutions to form sols containing colloidal particles, followed by drying and calcining.
摘要:
In accordance with the present invention, there are provided coating liquids for forming conductive coatings, which comprise (i) a zirconium oxysalt, (ii) a conductive substance and, if necessary, (iii) at least one member selected from non-sedimentary silica dispersion and silicon alkoxide or its derivative. The coating liquids, when coated on substrates, form thereon transparent conductive coatings which are excellent in transparency, scratch resistance, permanence properties and adhesion to the substrates and, moreover, excellent in antistatic effect. In particular, when the coating liquids for forming conductive coatings mentioned above are coated by the spray method on appropriate substrates followed by drying and/or heating, there are obtained face-plates for display devices, which have excellent regular reflection reducing effect (non-glare) and antistatic effect.
摘要:
An image forming apparatus includes a fixing device having a pressure roller. The surface of the pressure roller is coated with a PFA resin and has an average surface roughness Ra of 0.05 to 0.13 μm. A thermister is provided to detect the surface temperature of the pressure roller. The thermister includes a metal plate, a resister element attached to the metal plate, and a pair of fluorocarbon-resin films sandwiching the metal plate and the resister element. The fluorocarbon-resin film has a thickness of 15 μm to 80 μm.
摘要:
In accordance with the present invention, there are provided coating liquids for forming conductive coatings, which comprise (i) a zirconium oxysalt, (ii) a conductive substance and, if necessary, (iii) at least one member selected from non-sedimentary silica dispersion and silicon alkoxide or its derivative. The coating liquids, when coated on substrate, form thereon transparent conductive coatings which are excellent in transparency, scratch resistance, permanence properties and adhesion to the substrates and, moreover, excellent in antistatic effect. In particular, when the coating liquids for forming conductive coatings mentioned above are coated by the spray method on appropriate substrates followed by drying and/or heating, there are obtained face-plates for display devices, which have excellent regular reflection reducing effect (non-glare) and antistatic effect.
摘要:
Transparent conductive coatings excellent in transparency are provided on substrates such as glass, plastics, etc. by the use of conductive coating materials obtained by maintaining aqueous solutions of hydrolyzable tin containing or indium containing compounds at pH of 8-12, and gradually hydrolyzing said compounds in the solutions to form sols containing colloidal particles, followed by drying and calcining.
摘要:
In a process for preparing spherical particles of a metal oxide or hydroxide having a particle size of from 0.1 to 10 .mu.m by adding a corresponding metal alkoxide to a dispersion of water-alcohol system having dispersed therein a metal oxide or hydroxide as a seed, under alkaline conditions and allowing a decomposition product from said metal alkoxide to attach onto said seed to effect particle growth of the seed, the improvement which comprises maintaining said dispersion at a substantially constant pH within the range between 10 and 13 during the addition of the metal alkoxide to said dispersion and the subsequent particle growth of the seed, thereby to prepare mono-dispersed particles substantially free from particle aggregation having a sharp particle size distribution of a standard deviation of not greater than 0.5. The white particles so prepared may be, after separation, heat treated to provide black particles. The white or black particles may be coated with a synthetic resin in the surface. The products are useful particularly as spacers for liquid crystal display devices.
摘要:
Impregnation of a crystalline aluminosilicate-containing cracking catalyst with a metal component of Group IVB enhances the catalytic activity, gasoline selectivity and thermal and hydrothermal stability of the catalyst, and further improves the catalyst's capacity of producing a high-octane gasoline.