摘要:
There is disclosed a method for manufacturing an Fe-based sintered alloy which is superb in machinability. This process comprises the steps of coating a paste-like coating agent including a compound of boron to a surface of a compact of Fe-based or Fe, Cu-based sintered alloy powder including carbon or a pre-sintered compact obtained by heating the compact at a diffusion temperature or less of carbon, and sintering a resultant compact or a pre-sintered compact at a diffusion temperature or more of carbon. An Fe-based sintered alloy manufactured through this process and a bearing cap made of such an Fe-based sintered alloy are also disclosed. In the invention, a film including a compound of boron and pyrolytic resin can be used instead of the paste-like coating agent.
摘要:
There is provided a connecting rod including a connecting rod body and a cap having excellent alignment properties, and a method of producing such a connecting rod. A connecting rod body and a cap are produced through the steps of molding green compacts respectively corresponding to the connecting rod body and the cap; sintering and unifying both the green compacts; forging the resultant sintered product in a mold; and fracturing the resultant forged product. The green compact corresponding to the cap and/or the green compact corresponding to the connecting rod body includes opposite circumferential end faces formed with one or more projection. A clearance c is formed between both circumferential end faces of the sintered product due to the projection. With this clearance c, both the circumferential end faces are formed with recesses and projections which are fitted to each other during the forging process and which are relatively large and thus have large biting amounts. During the fracturing process, the recesses and the projections are separated into two pieces.
摘要:
Disclosed is a sintered iron alloy, a method of manufacturing the same, a powdered mixture used for manufacturing the same and a method of modifying the surface of the iron alloy. The sintered iron alloy is produced by compacting a powdered mixture comprising: boron or boron compound which is selected from the group consisting of boron oxide, boron sulfide, boron halide, boron hydride, boric acid, borate and tetrafluoroborate; 0.1 to 2.0% by weight of graphite; and iron, and sintering it. Alternatively, the iron alloy is produced by impregnating a modifier containing boron or boron compound, into a green compact, a presintered compact or sintered body which contains iron and carbon, and heating it.
摘要:
Disclosed is a manufacturing process of a sintered connecting rod assembly comprising a first member with a projection and a second member with a concavity in which the first member and the second member are mated with each other by engaging the projection with the concavity. A powdered raw material is compacted into a first compact and a second compact for the first and second members, wherein the projection of the first compact has a width slightly larger than the width of the concavity of the second compact. Then the projection of the first compact is engaged with the concavity of the second compact to mate the first compact with the second compact, thereby the projection and the concavity are tightly pressed against each other. After sintering the mated first and second compacts, they are forced to release the projection from the concavity. The die for compacting the raw material has a whole cavity and a removable core for dividing the whole cavity into two cavities.
摘要:
A plurality of blanks divided at a division end face 5 or a blank-bonded product comprising a plurality of blanks sintered and bonded together are or is compressed in the same mold, so that they are plastically deformed until the division end faces 5 are cohered. Thereafter, a load is applied to the plastically worked product in a direction of breaking of the division end faces 5 to break the division end faces 5 and divide the plastically worked product into a plurality of members. In this manner, a split type mechanical part having irregularities meshed with each other on mating faces and easily positionable relative to each other can be produced with a good dimentional accuracy.
摘要:
A method of manufacturing sintered Al-Si series alloy parts having complex configurations such as scroll shaped parts wherein Al-Si series alloy powder solidified via rapid cooling prepared by adding effective components such as Si, Cu, Mg, Fe, Mn, Zr and Ce to Al is compression molded, the molded body is sintered by heating via an electrical current conduction in a form of a plasma discharge and then the sintered body is worked by pressing, thereby the parts having complex configurations of light weight, high mechanical strength and toughness is manufactured with a simple installation and reduced processing manhours, and with a high efficiency and at a low cost.
摘要:
A fluid dynamic pressure bearing composed of a cylindrical sintered compact includes: a thrust region which is formed on an end surface of the bearing and receives at least a thrust load; a roughed portion having small peaks and valleys formed on the thrust region; and thrust recesses for generating thrust fluid dynamic pressure, which are formed on the thrust region.
摘要:
In a method of manufacturing a sheet member comprising: obtaining a sintered compact by sintering a sheet-like compact having a reduced-thickness portion and an enlarged-thickness portion; and then repressing the sintered compact into a sheet member, a difference in density between the reduced-thickness portion and the enlarged-thickness portion of the sintered compact after repressing is adjusted to be in a range of .+-.1.5%. By doing so, the accuracy of flatness is enhanced and the amount of distortion, which would otherwise remain in the sheet member, is reduced because the sheet member is formed by sintering the sheet-like compact. In addition, the deformation caused by heating is greatly restricted. Accordingly, the prospect of the sheet member of the present invention is bright as a heat dissipating plate.
摘要:
The present invention relates to a method for producing, without quench-hardening process, a ferrous sintered alloy having satisfactory strength which is equal to that of the conventional ferrous sintered quenched material, and the method comprises the steps of: preparing a powder mixture by adding, in weight ratios, 1 to 2% of copper powder, 1 to 3% of Ni powder, and graphite to a ferrous alloy powder consisting of 3 to 5% of Ni, 0.4 to 0.7% of Mo, and the remainder Fe, the quantity of said graphite being determined such that the C-content after sintering is 0.2 to 0.7%; compacting said powder mixture in a tool to form a green compact; sintering said green compact in a non-oxidizing atmosphere at a temperature in the range of 1130.degree. to 1230.degree. C.; and cooling the sintered product in the sintering furnace at a rate of 5.degree. C./min. to 20.degree. C./min.
摘要:
A fluid dynamic pressure effect can be sufficient without receiving a large effect of viscous friction of lubricating oil with changes in the environmental temperature in which it is used, and smooth starting of the rotating shaft can be ensured by regulating the gap between the rotating shaft and bearing within a suitable range. An outer diameter of the bearing, D, a length in an axial direction of the bearing, L, a gap at a radial side which is between the rotating shaft and the bearing, C, and an inclining height of the bearing end surface to which the flange is faced, δ, satisfy the expression L/D
摘要翻译:流体动力学效应可以充分发挥润滑油在使用环境温度变化的作用下的粘性摩擦力的大的影响,通过调整旋转轴与旋转轴之间的间隙可以确保旋转轴的平滑启动 在适当的范围内。 轴承的外径D,轴承的轴向长度L,在旋转轴与轴承之间的径向侧的间隙C和轴承端面的倾斜高度,其中 法兰面对,δ,满足表达式L / D