摘要:
Provided is a composition for forming a photocatalytic coating layer, a process for preparing said composition, a self-cleaning article comprising a photocatalytic coating layer comprising said composition and a process for preparing said self-cleaning article. The composition may be used to prepare a self-cleaning article having excellent anticorrosion and processability by one coating and drying procedure, without several coating and drying procedures.
摘要:
Provided is a composition for forming a photocatalytic coating layer, a process for preparing said composition, a self-cleaning article comprising a photocatalytic coating layer comprising said composition and a process for preparing said self-cleaning article. The composition may be used to prepare a self-cleaning article having excellent anticorrosion and processability by one coating and drying procedure, without several coating and drying procedures.
摘要:
A method of treating a surface of a substrate using modified urushiol derived from Toxicodendron vernicifluum is provided. More particularly, the reactivity of a hydroxyl group of urushiol extracted from fresh Toxicodendron vernicifluum is removed before the lacquer is used as a UV coating agent for a substrate such as a steel sheet. Therefore, the substrate may have high antibacterial activity, and excellent appearance and functionalities such as far-infrared radiation, blocking of electromagnetic waves, enhanced corrosion resistance, high crosslinking speed when a low content of a photoinitiator is used, excellent surface gloss and high scratch resistance.
摘要:
A method of treating a surface of a substrate using modified urushiol derived from Toxicodendron vernicifluum is provided. More particularly, the reactivity of a hydroxyl group of urushiol extracted from fresh Toxicodendron vernicifluum is removed before the lacquer is used as a UV coating agent for a substrate such as a steel sheet. Therefore, the substrate may have high antibacterial activity, and excellent appearance and functionalities such as far-infrared radiation, blocking of electromagnetic waves, enhanced corrosion resistance, high crosslinking speed when a low content of a photoinitiator is used, excellent surface gloss and high scratch resistance.
摘要:
Provided is a resin composition for surface treatment of a steel sheet including a binder resin, graphene and a solvent. More particularly, as only a small amount of the graphene is included in the resin composition used for surface treatment of a steel sheet, a user-required electrical conductivity can be provided to the steel sheet.
摘要:
Provided is a resin composition for surface treatment of a steel sheet including a binder resin, graphene and a solvent. More particularly, as only a small amount of the graphene is included in the resin composition used for surface treatment of a steel sheet, a user-required electrical conductivity can be provided to the steel sheet.
摘要:
A heat-dissipating black resin composition having excellent physical properties such as heat-dissipation, workability, corrosion resistance, solvent resistance, coating adherence and gloss, and being free from chromium and used for surface treatment of a zinc coated steel sheet and a zinc coated steel sheet treated thereby. The composition includes, based on 100 parts by weight: 10 to 60 parts by weight of a resin composition which at least one main resin and a melamine-based curing agent are mixed in a weight ratio of 10:2-7, the main resin being selected from the group consisting of polyester, epoxy, polyolefin, polyurethane, fluorine, phenol, acryl and polycarbonate resins; 1 to 10 parts by weight of at least one pigment selected from the group consisting of carbon black and carbon nano tube; 1 to 10 parts by weight of a matting agent; and a solvent.
摘要:
Provided are a polymer capsule in which an organic corrosion inhibitor is encapsulated, a method of preparing the same, a composition having the same, and a steel sheet whose surface is treated using the same. The polymer capsule prepared to include a core layer polymer having a hydrophilic acid group and at least one shell layer surrounding the core layer through continuous emulsion polymerization may have an organic corrosion inhibitor effectively encapsulated. The corrosion inhibitor may be released from the capsule in a corrosive environment, thereby enhancing corrosion resistance of the steel sheet.
摘要:
A core formed from powder, such as a stator core for use in a motor for a vehicle, wherein the core is formed from metallic powder and includes an outer part disposed at an outside of the motor, an inner part disposed at an inside of the motor, and a winding part which connects the outer part and the inner part and on which a wire is wound, and to a motor for a vehicle using the same. The winding part is formed to have rounded corners and a height lower than the height of the inner part, and a connection part is obliquely formed between the winding part and the inner part so that the winding part and the inner part are naturally connected.
摘要:
A coating composition for zinc- and zinc alloy-coated steel sheets includes: 1 to 30% by weight of hypophosphorous acid, 0.1 to 10% by weight of manganese, 0.01 to 5% by weight of a polyvinyl compound, zinc oxide and the balance of water, and further comprises 20% by weight or less of alcohol, when necessary, wherein the zinc oxide is included in such a content that, when 50 Ml (milliliters) of the coating composition is neutralized and titrated with 0.1N NaOH, the NaOH used for the neutralization titration is present in an amount of 10.0 Ml (milliliters) or less, and a content of free acid in the coating composition is adjusted to such an amount that, when 50 Ml (milliliters) of the coating composition is neutralized and titrated with 0.1N NaOH, the NaOH used for the neutralization titration is present in an amount of 10.0 Ml (milliliters) or less. The coating film formed on the steel sheet using the coating composition shows excellent properties such as lubricating property, adhesion and coating removal property, and also has a fine surface appearance.