摘要:
The present invention relates to a polyethylene composition comprising a base resin which comprises (a) an ethylene homo- or copolymer fraction (A); and (b) an ethylene homo- or copolymer fraction (B), wherein (i) fraction (A) has a lower weight average molecular weight than fraction (B); (ii) the base resin has a density of 932 to 938 kg/m3; (iii) the polyethylene composition has an MFR5 of 0.1 to 0.6 g/10 min; and (iv) the polyethylene composition has a shear stress η2.7 kPa of 85 to 230 kPas. Furthermore, the present invention relates to an article, preferably a pipe comprising said composition and to the use of said composition for the production of an article, preferably a pipe.
摘要:
The present invention relates to a polyethylene composition comprising a base resin which comprises (a) an ethylene homo- or copolymer fraction (A); and (b) an ethylene homo- or copolymer fraction (B), wherein (i) fraction (A) has a lower weight average molecular weight than fraction (B); (ii) the base resin has a density of 932 to 938 kg/m3; (iii) the polyethylene composition has an MFR5 of 0.1 to 0.6 g/10 min; and (iv) the polyethylene composition has a shear stress η2.7 kPa of 85 to 230 kPas. Furthermore, the present invention relates to an article, preferably a pipe comprising said composition and to the use of said composition for the production of an article, preferably a pipe.
摘要:
The present invention relates to a polyolefin composition comprising: a) an olefin homo- or copolymer (A), and b) activated carbon (B) as a taste and/or odor reducing agent, to the use of such a polyolefin composition, and to a pipe material and pipe having reduced taste and/or odor development comprising the above polyolefin composition.
摘要:
The present invention relates to a polyethylene composition comprising a base resin which comprises (a) an ethylene homo- or copolymer fraction (A); and (b) an ethylene homo- or copolymer fraction (B), wherein (i) fraction (A) has a lower average molecular weight than fraction (B); (ii) the base resin has a density of 940 to 947 kg/m3; (iii) the polyethylene composition has an MFR5 of 0.1 to 0.5 g/10 min; and (iv) the polyethylene composition has an SHI(2.7/210) of 10 to 49. Furthermore, the present invention relates to an article, preferably a pipe comprising said composition and to the use of said composition for the production of an article, preferably a pipe.
摘要:
The present invention relates to a polyolefin composition comprising: a) an olefin homo- or copolymer (A), and b) activated carbon (B) as a taste and/or odour reducing agent, to the use of such a polyolefin composition, and to a pipe material and pipe having reduced taste and/or odour development comprising the above polyolefin composition.
摘要:
The present invention relates to a polyethylene composition comprising a base resin which comprises (a) an ethylene homo- or copolymer fraction (A); and (b) an ethylene homo- or copolymer fraction (B), wherein (i) fraction (A) has a lower average molecular weight than fraction (B); (ii) the base resin has a density of 940 to 947 kg/m3; (iii) the polyethylene composition has an MFR5 of 0.1 to 0.5 g/10 min; and (iv) the polyethylene composition has an SHI(2.7/210) of 10 to 49. Furthermore, the present invention relates to an article, preferably a pipe comprising said composition and to the use of said composition for the production of an article, preferably a pipe.
摘要:
The present invention relates to a polyolefin composition comprising a crosslinkable polyolefin with hydrolysable silane groups and a silanol condensation catalyst, and (A) a compound containing one or more POm(OnR)(OoR)(OpR″) groups, wherein R, R′, and R″ are the same or different organic residues; m is 0 or 1; n, o, and p each are 0 or 1; and n+o+p=1 to 3; a master batch for a crosslinkable polyolefin composition comprising a polymer and a silanol condensation catalyst and component (A), a stabilized polyolefin containing cross-linked silane groups wherein cross-linking has been performed by the use of a silanol condensation catalyst, further comprising component (A), and to the use of component (A) for stabilizing a polyolefin composition comprising a crosslinkable polyolefin with hydrolysable silane groups and a silanol condensation catalyst. The polyolefin composition of the invention can be used for pipe, wire & cable, film, fibre and moulding applications.
摘要翻译:本发明涉及包含具有可水解硅烷基团的可交联聚烯烃和硅烷醇缩合催化剂的聚烯烃组合物,和(A)含有一个或多个PO(O)N 其中R,R'和R“是相同或不同的有机残基; R 1,R 2,R 3,R 3, m为0或1; n,o和p各自为0或1; 和n + o + p = 1〜3; 包含聚合物和硅烷醇缩合催化剂和组分(A)的可交联聚烯烃组合物的母料,含有交联硅烷基团的稳定的聚烯烃,其中通过使用硅烷醇缩合催化剂进行交联,还包含组分 (A),以及组分(A)用于稳定含有可水解硅烷基团的可交联聚烯烃的聚烯烃组合物和硅烷醇缩合催化剂的用途。 本发明的聚烯烃组合物可用于管道,电线和电缆,膜,纤维和模塑应用。
摘要:
The present invention deals with the use of pipes made of cross-linked polyethylene for transporting water containing chlorine dioxide. Cross-linked polyethylene has a resistance of more than 3500 hours against water treated with chlorine dioxide when tested according to a modified method of ASTM F2263-03. Especially, the pipes made of cross-linked polyethylene can be used for transporting drinking water which had been disinfected by using chlorine dioxide.
摘要:
The invention relates to a polymer composition with improved DC electrical properties and to a cable surrounded by at least one layer comprising the polymer composition.
摘要:
The invention relates to a polymer composition with improved DC electrical properties, to the use of the composition for producing a cable layer and to a cable surrounded by at least one layer comprising the polymer composition.