公开(公告)号：US07923067B2

公开(公告)日：2011-04-12

申请号：US11597942

申请日：2005-05-27

申请人： Naokuni Muramatsu ,  Ken Suzuki ,  Akihisa Inoue ,  Hisamichi Kimura

发明人： Naokuni Muramatsu ,  Ken Suzuki ,  Akihisa Inoue ,  Hisamichi Kimura

IPC分类号： B05D7/00

CPC分类号： C25D11/26

摘要： A method of coloring a surface of a zirconium-based metallic glass component that includes the step of imparting interference colors by carrying out an anodizing process using an alkaline solution to form a film having a thickness of 300 nm or less on the surface of the zirconium-based metallic glass component.

摘要翻译： 一种使锆系金属玻璃成分的表面着色的方法，其特征在于，包括通过使用碱溶液进行阳极氧化处理而赋予干涉色的步骤，以在锆的表面形成厚度为300nm以下的膜 的金属玻璃组件。

公开(公告)号：US20080034796A1

公开(公告)日：2008-02-14

申请号：US11628122

申请日：2005-05-27

申请人： Naokuni Muramatsu ,  Ken Suzuki ,  Akihisa Inoue ,  Hisamichi Kimura

发明人： Naokuni Muramatsu ,  Ken Suzuki ,  Akihisa Inoue ,  Hisamichi Kimura

IPC分类号： C03B11/00 ,  C03B19/02 ,  C03C17/00

CPC分类号： B21D37/01 ,  B21D37/20 ,  B21J1/006 ,  B22D17/00 ,  B22D17/10 ,  B22D17/14 ,  C22C45/10 ,  Y10T29/49984

摘要： A method of forming a metallic glass includes the steps of, molding a metallic glass into a pre-formed semi-article by performing pre-forming by die casting, and performing warm press forming on the pre-formed semi-article by heating the pre-formed semi-article to a supercooled liquid temperature range.

摘要翻译： 形成金属玻璃的方法包括以下步骤：通过压铸进行预成型，将金属玻璃成型为预成型的半成品，并通过加热预成型的半成品对预成型的半制品进行热压成型 成型的半制品达到过冷液体温度范围。

公开(公告)号：US08865253B2

公开(公告)日：2014-10-21

申请号：US13009082

申请日：2011-01-19

申请人： Naokuni Muramatsu ,  Ken Suzuki ,  Akihisa Inoue ,  Hisamichi Kimura

发明人： Naokuni Muramatsu ,  Ken Suzuki ,  Akihisa Inoue ,  Hisamichi Kimura

IPC分类号： C25D11/26

CPC分类号： C25D11/26

摘要： A method of coloring a surface of a zirconium-based metallic glass component that includes the step of imparting interference colors by carrying out an anodizing process using an alkaline solution to form a film having a thickness of 300 nm or less on the surface of the zirconium-based metallic glass component.

摘要翻译： 一种使锆系金属玻璃成分的表面着色的方法，其特征在于，包括通过使用碱溶液进行阳极氧化处理而赋予干涉色的步骤，以在锆的表面形成厚度为300nm以下的膜 的金属玻璃组件。

公开(公告)号：US07708844B2

公开(公告)日：2010-05-04

申请号：US11628122

申请日：2005-05-27

申请人： Naokuni Muramatsu ,  Ken Suzuki ,  Akihisa Inoue ,  Hisamichi Kimura

发明人： Naokuni Muramatsu ,  Ken Suzuki ,  Akihisa Inoue ,  Hisamichi Kimura

IPC分类号： C22F1/02 ,  C22F1/18

CPC分类号： B21D37/01 ,  B21D37/20 ,  B21J1/006 ,  B22D17/00 ,  B22D17/10 ,  B22D17/14 ,  C22C45/10 ,  Y10T29/49984

摘要： A method for forming a metallic glass, which comprises a step of subjecting a metallic glass to a rough forming by die casting, to prepare a roughly formed article, and a step of heating the roughly formed article to a temperature region corresponding to an undercooled liquid thereof, followed by subjecting the heated article to warm press forming.

摘要翻译： 一种用于形成金属玻璃的方法，其包括通过压铸对金属玻璃进行粗糙成形的步骤，以制备粗略成型的制品，以及将粗略形成的制品加热到对应于过冷却液体的温度区域的步骤 然后将受热制品经受热压成型。

公开(公告)号：US20080038460A1

公开(公告)日：2008-02-14

申请号：US11597942

申请日：2005-05-27

申请人： Naokuni Muramatsu ,  Ken Suzuki ,  Akihisa Inoue ,  Hisamichi Kimura

发明人： Naokuni Muramatsu ,  Ken Suzuki ,  Akihisa Inoue ,  Hisamichi Kimura

IPC分类号： B05D3/02 ,  C23C8/12 ,  C25D11/26

CPC分类号： C25D11/26

摘要： A method of coloring a surface of a zirconium-based metallic glass component includes the step of imparting interference colors by carrying out an anodizing process using an alkaline solution to form a film having a thickness of 300 nm or less on the surface of the zirconium-based metallic glass component.

摘要翻译： 对锆系金属玻璃部件的表面进行着色的方法包括通过使用碱性溶液进行阳极氧化处理来赋予干涉色的步骤，以在锆 - 金属玻璃部件的表面上形成厚度为300nm以下的膜， 金属玻璃组件。

公开(公告)号：US20080014447A1

公开(公告)日：2008-01-17

申请号：US11597943

申请日：2005-05-27

申请人： Naokuni Muramatsu ,  Ken Suzuki ,  Akihisa Inoue ,  Hisamichi Kimura

发明人： Naokuni Muramatsu ,  Ken Suzuki ,  Akihisa Inoue ,  Hisamichi Kimura

IPC分类号： B32B9/00 ,  B32B15/01 ,  C23C26/00

CPC分类号： C23C26/00

摘要： A method of forming a film on a zirconium-based metallic glass surface, including the steps of forming a film including oxygen, silicon and zirconium, which has a post-drying thickness of 10 μm or less, by drying an alcohol solution containing silicon dioxide in a content of 3% or more and less than 25%, after the alcohol solution is applied to a surface of a zirconium-based metallic glass.

摘要翻译： 在锆系金属玻璃表面上形成膜的方法，包括通过干燥含有二氧化硅的醇溶液形成干燥后厚度为10μm以下的氧，硅和锆的膜的步骤 在醇溶液施加到锆基金属玻璃的表面之后，含量为3％以上且小于25％。

公开(公告)号：US20120148441A1

公开(公告)日：2012-06-14

申请号：US13391139

申请日：2010-09-13

申请人： Naokuni Muramatsu ,  Hisamichi Kimura ,  Akihisa Inoue

发明人： Naokuni Muramatsu ,  Hisamichi Kimura ,  Akihisa Inoue

IPC分类号： C22C9/00 ,  C22F1/08 ,  B22D25/02

CPC分类号： H01B1/026 ,  C22C1/02 ,  C22C9/00 ,  C22F1/08

摘要： The zirconium content of the alloy composition of a copper alloy wire is 3.0 to 7.0 atomic percent; and the copper alloy wire includes copper matrix phases and composite phases composed of copper-zirconium compound phases and copper phases. The copper matrix phases and the composite phases form a matrix phase-composite phase fibrous structure and are arranged alternately parallel to an axial direction as viewed in a cross-section parallel to the axial direction and including a central axis. The copper-zirconium compound phases and the copper phases in the composite phases also form a composite phase inner fibrous structure and are arranged alternately parallel to the axial direction at a phase pitch of 50 nm or less as viewed in the above cross-section. This double fibrous structure presumably makes the copper alloy wire densely fibrous to provide a strengthening mechanism similar to the rule of mixture for fiber-reinforced composite materials.

摘要翻译： 铜合金线的合金组成的锆含量为3.0〜7.0原子％ 铜合金线包括铜基体相和由铜 - 锆化合物相和铜相组成的复合相。 铜基质相和复合相形成基体相 - 复合相纤维结构，并且在与轴向平行的横截面中观察并且包括中心轴线在轴向方向上交替平行布置。 复合相中的铜 - 锆化合物相和铜相也形成复合相内纤维结构，并且如上述横截面所示，以50nm以下的相位间距与轴向交替平行排列。 这种双重纤维结构可能使铜合金丝线密集纤维化，以提供类似于纤维增强复合材料的混合规则的强化机理。

公开(公告)号：US20070215306A1

公开(公告)日：2007-09-20

申请号：US11159833

申请日：2005-06-23

申请人： Naokuni Muramatsu ,  Akihisa Inoue ,  Hisamichi Kimura

发明人： Naokuni Muramatsu ,  Akihisa Inoue ,  Hisamichi Kimura

IPC分类号： B22D17/12 ,  B22D27/04

CPC分类号： B22D21/022 ,  B22D17/12 ,  B22D17/14 ,  B22D17/2038 ,  B22D17/2069 ,  B22D17/2209 ,  B22D17/30 ,  B22D27/02

摘要： A diecast machine comprises: a sleeve extending in a vertical direction; a plunger moving upward in the vertical direction inside the sleeve; a mold disposed above an upper side of the sleeve; and a metal material heater configured to heat a metal material disposed on the plunger and melting the metal material.

摘要翻译： 压铸机包括：沿垂直方向延伸的套筒; 柱塞沿垂直方向向上移动的柱塞; 设置在所述套筒的上侧上方的模具; 以及金属材料加热器，其构造成加热设置在柱塞上的金属材料并熔化金属材料。

公开(公告)号：US09175406B2

公开(公告)日：2015-11-03

申请号：US12530920

申请日：2007-03-13

申请人： Xin Min Wang ,  Naokuni Muramatsu ,  Junsuke Kiuchi ,  Hiroshi Suzuki ,  Tatsue Arakawa ,  Hisamichi Kimura ,  Akihisa Inoue ,  Eiichi Makabe

发明人： Xin Min Wang ,  Naokuni Muramatsu ,  Junsuke Kiuchi ,  Hiroshi Suzuki ,  Tatsue Arakawa ,  Hisamichi Kimura ,  Akihisa Inoue ,  Eiichi Makabe

IPC分类号： C25D5/34 ,  C23C28/00 ,  C25D5/54 ,  C23G1/02 ,  C23C18/16 ,  C23C18/18 ,  C23C18/31 ,  C23G1/08 ,  C23G1/10 ,  C25D5/36 ,  C25D5/38 ,  C25D5/40 ,  C25D5/48

CPC分类号： C23G1/02 ,  C23C18/165 ,  C23C18/1844 ,  C23C18/31 ,  C23G1/086 ,  C23G1/10 ,  C23G1/103 ,  C23G1/106 ,  C25D5/34 ,  C25D5/36 ,  C25D5/38 ,  C25D5/40 ,  C25D5/48 ,  C25D5/54

摘要： There is provided a metallic glass component with its surface layer having both durability of a film and chromatic color properties, and a method for forming the surface layer. Surface active treatment is performed wherein the surface of the metallic glass component is reacted with a mixed aqueous solution of nitric acid and hydrofluoric acid to remove an oxide film and to provide an anchor bond shape on the surface of a metallic glass component, and electroplating or electroless plating is then performed, to form a plating film on the surface of the metallic glass component. It is thereby possible to form a surface layer of a metallic glass which has both durability and a chromatic color.

摘要翻译： 提供一种其表面层具有薄膜的耐久性和彩色特性的金属玻璃组分和形成表面层的方法。 进行表面活性处理，其中金属玻璃组分的表面与硝酸和氢氟酸的混合水溶液反应以除去氧化物膜，并在金属玻璃组分的表面上提供锚结合形状，以及电镀或 然后进行化学镀，以在金属玻璃组分的表面上形成镀膜。 从而可以形成具有耐久性和有色颜色的金属玻璃的表面层。

公开(公告)号：US09165695B2

公开(公告)日：2015-10-20

申请号：US13391139

申请日：2010-09-13

申请人： Naokuni Muramatsu ,  Hisamichi Kimura ,  Akihisa Inoue

发明人： Naokuni Muramatsu ,  Hisamichi Kimura ,  Akihisa Inoue

IPC分类号： H01B1/02 ,  C22C1/02 ,  C22C9/00 ,  C22F1/08

CPC分类号： H01B1/026 ,  C22C1/02 ,  C22C9/00 ,  C22F1/08

摘要： The zirconium content of the alloy composition of a copper alloy wire is 3.0 to 7.0 atomic percent; and the copper alloy wire includes copper matrix phases and composite phases composed of copper-zirconium compound phases and copper phases. The copper matrix phases and the composite phases form a matrix phase-composite phase fibrous structure and are arranged alternately parallel to an axial direction as viewed in a cross-section parallel to the axial direction and including a central axis. The copper-zirconium compound phases and the copper phases in the composite phases also form a composite phase inner fibrous structure and are arranged alternately parallel to the axial direction at a phase pitch of 50 nm or less as viewed in the above cross-section. This double fibrous structure presumably makes the copper alloy wire densely fibrous to provide a strengthening mechanism similar to the rule of mixture for fiber-reinforced composite materials.

摘要翻译： 铜合金线的合金组成的锆含量为3.0〜7.0原子％ 铜合金线包括铜基体相和由铜 - 锆化合物相和铜相组成的复合相。 铜基质相和复合相形成基体相 - 复合相纤维结构，并且在与轴向平行的横截面中观察并且包括中心轴线在轴向方向上交替平行布置。 复合相中的铜 - 锆化合物相和铜相也形成复合相内纤维结构，并且如上述横截面所示，以50nm以下的相位间距与轴向交替平行排列。 这种双重纤维结构可能使铜合金丝线密集纤维化，以提供类似于纤维增强复合材料的混合规则的强化机理。