摘要:
Disclosed is an annealing separator for production for grain-oriented electrical steel sheet, containing one or more compound selected from the following general formula; �Mg.sub.1-x M.sup.3+.sub.x !O �Mg.sub.1-x M.sup.2+.sub.x !O or �Mg.sub.1-x M.sup.2+.sub.x1 M.sup.3+.sub.x2 !O where M.sup.2+ is at least one bivalent element selected from the group consisting of Be, Ca, Ba, Sr, Sn, Mn, Fe, Co, Ni, Cu, Zn; M.sup.3+ is at least one tervalent element selected from the group consisting of Al, Fe, Cr, Co, B, Ti, Sb; 0.01.ltoreq.x.ltoreq.0.40; x=x1+x2 This annealing separator having a lower melting point and higher degree of reactivity is applied on the decarburization annealed strip, and improves the properties of the glass film, especially uniform film appearance and good sealing effect, and magnetic properties.
摘要翻译:公开了一种含有一种或多种选自以下通式的化合物的晶粒取向电工钢板的退火分离剂:[Mg1-xM3 + x] O [Mg1-xM2 + x] O或[Mg1-xM2 + x1M3 + x2]其中M2 +为选自Be,Ca,Ba,Sr,Sn,Mn,Fe,Co,Ni,Cu,Zn中的至少一种二价元素; M3 +是选自Al,Fe,Cr,Co,B,Ti,Sb中的至少一种三价元素;0.01≤x≤0.40; x = x1 + x2在脱碳退火带上施加具有较低熔点和较高反应性的退火分离剂,并且改善玻璃膜的性能,特别是膜的外观均匀,密封效果好,磁性能好。
摘要:
A process for producing a grain-oriented electrical steel sheet excellent in the glass film and the magnetic properties by coating a steel sheet with an annealing separator, finish annealing the steel sheet, and baking an insulating coating agent, which comprises coating the steel sheet having been decarburization annealed with an annealing separator prepared by allowing 100 parts by weight of MgO to contain, in the course from the step of producing MgO to the stage of preparing a slurry in the step of coating the steel sheet with MgO, halogens selected from F, Cl, Br and I or compounds of the halogens in an amount of 0.015 to 0.120 part by weight in terms of F, Cl, Br and I, and finish annealing the steel sheet.
摘要:
A grain oriented electrical steel sheet having no significant glass film and having a high magnetic flux density and an excellent iron loss property, comprising, in terms of by weight, 2.5 to 4.5% of Si, the steel sheet having, as oxides on its surface, a glass film comprising 0.6 g/m.sup.2 or less in total of forsterite and spinel composed of MgO, SiO.sub.2 and Al.sub.2 O.sub.3 and an insulating coating having a thickness of 6 .mu.m or less, the face tension imparted on the surface of the steel sheet by the coating being in the range of from 0.5 to 2.0 kg/mm.sup.2. In the final box annealing of the steel sheet after primary recrystallization annealing, use is made of an annealing separator comprising 100 parts by weight of MgO and, added thereto, 2 to 30 parts by weight of at least one member selected from the group consisting of chlorides, carbonates, nitrates, sulfates and sulfides of Li, K, Bi, Na, Ba, Ca, Mg, Zn, Fe, Zr, Sr, Sn, Al, etc., and the heating in the final box annealing is effected in an atmosphere comprising N.sub.2 and H.sub.2 with the nitrogen content being 30% or more at a heating rate of 20.degree. C./hr or less, and a seam or spotty flaw is imparted at an angle of 45.degree. to 90.degree. to the rolling direction of the steel sheet.
摘要翻译:一种不具有显着玻璃膜并且具有高磁通密度和优异的铁损特性的晶粒取向电工钢板,其中,按重量计包含2.5至4.5%的Si,该钢板在其表面上具有氧化物 ,由MgO,SiO 2和Al 2 O 3组成的镁橄榄石和尖晶石的总计为0.6g / m 2以下的玻璃膜和厚度为6μm以下的绝缘涂层,通过以下方式赋予钢板表面的表面张力 涂层在0.5至2.0kg / mm 2的范围内。 在一次再结晶退火后的钢板的最终退火中,使用包含100重量份MgO的退火分离剂,向其中加入2〜30重量份的选自以下的至少一种: Li,K,Bi,Na,Ba,Ca,Mg,Zn,Fe,Zr,Sr,Sn,Al等的氯化物,碳酸盐,硝酸盐,硫酸盐和硫化物,最终箱退火中的加热是 包含N 2和H 2的气氛,氮含量在20℃/小时以下的加热速率为30%以上,接缝或斑点缺陷与轧制方向成45度〜90度的角度 的钢板。
摘要:
The invention provides a method of producing a grain-oriented electrical steel sheet of the complete solid solution nitrided type that is good in glass film formation and excellent in magnetic properties, which method comprises: C: 0.025 to 0.09%, hot-rolling the steel slab containing Si: 2.5 to 4.0% and acid-soluble Al into a hot-rolled steel strip; controlling the rate at which N contained in the hot-rolled steel strip is precipitated as AlN to a precipitation rate of 20% or less; conducting hot-rolled strip annealing and cold rolling conducting decarburization-annealing combined with primary recrystallization by during the former part of the process in an atmosphere whose PH2O/PH2 is 0.30 to 0.70 and then during the latter part thereof in an atmosphere whose PH2O/PH2 is 0.20 or less, thereby making the circular equivalent average grain diameter of the primary recrystallization grains 7 μm to less than 18 μm; nitriding the strip as it travels in a mixed gas of hydrogen, nitrogen and ammonia; controlling the steel strip oxygen concentration before secondary recrystallization annealing calculated based on strip thickness of 0.30 mm (oxygen content: So) to 450 ppm to 700 ppm inclusive; applying a coat of annealing separator; and then conducting secondary recrystallization annealing in an atmosphere that, while the temperature at the hottest coil outer periphery point is between room temperature and 950° C., is controlled to a nitrogen atmosphere containing oxygen: 25 to 75% wherein the balance is hydrogen and PH2O/PH2 is 0.01 to 0.15.
摘要:
The invention provides a method of producing a grain-oriented electrical steel sheet of the complete solid solution nitrided type that is good in glass film formation and excellent in magnetic properties, which method comprises: C: 0.025 to 0.09%, hot-rolling the steel slab containing Si: 2.5 to 4.0% and acid-soluble Al into a hot-rolled steel strip; controlling the rate at which N contained in the hot-rolled steel strip is precipitated as AlN to a precipitation rate of 20% or less; conducting hot-rolled strip annealing and cold rolling conducting decarburization-annealing combined with primary recrystallization by during the former part of the process in an atmosphere whose PH2O/PH2 is 0.30 to 0.70 and then during the latter part thereof in an atmosphere whose PH2O/PH2 is 0.20 or less, thereby making the circular equivalent average grain diameter of the primary recrystallization grains 7 μm to less than 18 μm; nitriding the strip as it travels in a mixed gas of hydrogen, nitrogen and ammonia; controlling the steel strip oxygen concentration before secondary recrystallization annealing calculated based on strip thickness of 0.30 mm (oxygen content: So) to 450 ppm to 700 ppm inclusive; applying a coat of annealing separator; and then conducting secondary recrystallization annealing in an atmosphere that, while the temperature at the hottest coil outer periphery point is between room temperature and 950° C., is controlled to a nitrogen atmosphere containing oxygen: 25 to 75% wherein the balance is hydrogen and PH2O/PH2 is 0.01 to 0.15.
摘要:
A means for treating the end faces of a core which is used for an electrical apparatuses and etc., to give insulation extremely superior in effect of improvement of the insulation, corrosion resistance, adhesiveness, heat resistance, and magnetic properties at a low temperature in a short time without cleaning for removing punching oil, annealing, or other pre-treatment; a core having an insulation coating comprised of a dry film of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as a silicone compound on the core end faces and having an average film thickness of at least 0.5 μm, a breakdown voltage of at least 30V, and a heat resistance in the air of at least 400° C.; and a method of production comprised of forming a core, then dipping it in or spraying it by one or more types of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as an insulation coating.
摘要:
A means for treating the end faces of a core which is used for an electrical apparatuses and etc., to give insulation extremely superior in effect of improvement of the insulation, corrosion resistance, adhesiveness, heat resistance, and magnetic properties at a low temperature in a short time without cleaning for removing punching oil, annealing, or other pre-treatment; a core having an insulation coating comprised of a dry film of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as a silicone compound on the core end faces and having an average film thickness of at least 0.5 μm, a breakdown voltage of at least 30V, and a heat resistance in the air of at least 400° C.; and a method of production comprised of forming a core, then dipping it in or spraying it by one or more types of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as an insulation coating.
摘要:
A means for treating the end faces of a core which is used for an electrical apparatuses and etc., to give insulation extremely superior in effect of improvement of the insulation, corrosion resistance, adhesiveness, heat resistance, and magnetic properties at a low temperature in a short time without cleaning for removing punching oil, annealing, or other pre-treatment; a core having an insulation coating comprised of a dry film of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as a silicone compound on the core end faces and having an average film thickness of at least 0.5 μm, a breakdown voltage of at least 30V, and a heat resistance in the air of at least 400° C.; and a method of production comprised of forming a core, then dipping it in or spraying it by one or more types of a pure silicone polymer, modified silicone polymer, and/or mixed silicone polymer as an insulation coating.
摘要:
The present invention provides an annealing separator comprising from 0.05 to 2.0 parts by weight of antimony sulfate based on 100 parts by weight of magnesium oxide, and at least one chloride selected from the group consisting of Sb, Sr, Ti, and Zr chlorides in a chlorine amount of from 5 to 20% by weight based on 100% of the chloride and antimony sulfate, and occasionally comprises Ti oxide in an amount of from 0.5 to 10 parts.The annealing separator is applied on the decarburization annealed strip, and improves both the magnetic properties and properties of glass film, in the production of a grain-oriented electrical steel sheet.
摘要:
A negative electrode active material for an electric device includes an alloy containing Si in a range of greater than or equal to 27% by mass and less than 100% by mass, Sn in a range of greater than 0% by mass and less than or equal to 73% by mass, V in a range of greater than 0% by mass and less than or equal to 73% by mass, and inevitable impurities as a residue. The negative electrode active material can be obtained with, for example, a multi DC magnetron sputtering apparatus by use of Si, Sn, and V as targets. An electric device using the negative electrode active material can achieve long cycle life and ensure a high capacity and cycle durability.