摘要:
The invention is directed to a thermoplastic recycling molding composition comprising recycled acrylonitrile-butadiene-styrene copolymer (r-ABS) as component A and virgin material as component B, wherein the component B is a mixture of at least two components selected from virgin thermoplastic polymers B1 and virgin lubricants B2, or wherein the component B is one or more polymer selected from polymers which are not homogenously miscible with rABS. Further, the present invention is directed to a process for the preparation of the thermoplastic recycling molding composition.
摘要:
The present invention relates to a thermoplastic polymer powder and to the use thereof as material for selective laser sintering (SLS). The polymer powder contains a partially crystalline polymer, an amorphous polymer and a compatibilizing agent, and optionally additional additives and/or auxiliary substances, wherein the partially crystalline polymer, the amorphous polymer and the compatibilizing agent are in the form of a polymer blend. The invention also relates to a method for producing the thermoplastic polymer powder and to a method of selective laser sintering (SLS).
摘要:
The invention relates to a method for economically using styrene-containing plastic waste as raw material for new high-quality plastic products as part of a raw material recycling process, optionally having the steps of pre-treating a styrene-containing starting material, decomposing the styrene-containing starting material in a suitable reactor, discharging and collecting the resulting gases and condensing the low-molecular products in a suitable separator, separating the collected low-molecular components of the previous step by means of a fractioning distillation process, and optionally additionally decomposing the styrene oligomers in a steam cracker.
摘要:
Polymer compositions comprising styrene butadiene block-copolymers (SBC) can be used for shrink-wrap films, a stiff star-shaped SBC block copolymer A having two short branches of a single copolymer block (B/S)Ai and two long branches of the structure St-[(B/S)A]n-(B/S)Ai or [(B/S)A]n-(B/S)Ai are used in said polymer composition, and the production of shrink-wrap films and of multilayer films is described.
摘要:
The present invention relates to a polymer composition comprising at least one block copolymer and a specific amount of at least one oil component. The block copolymer, which is the polymeric matrix of the inventive composition, is built up from at least one vinyl aromatic monomer MA and at least one conjugated diene monomer MB, in particular the block copolymer is a styrene butadiene block copolymer (SBC).
摘要:
The invention relates to the use of a thermoplastic moulding compound for 3D Printing, made of a mixture of the following components A-E: A: 35-60 wt. % impact resistant modified polymer A comprising: 30-95 wt. % SAN-copolymer and 5-70 wt. % ABS-graft copolymer; B: 33-58 wt. % aliphatic polyamide B; C: 1-10 wt. % SANMSA-terpolymer C as a compatibilizing agent; D: 0.01-5 wt. % processing agent D; and E: 0-30 wt. % other additives E.
摘要:
A thermoplastic molding composition can be employed for 3D printing if it comprises: A: 92.9 to 98.59 wt % of impact-modified polymer A, consisting of: 40 to 90 wt % of vinylaromatic copolymer a, 10 to 60 wt % of ABS graft copolymer b; B1: 1.2 to 3.5 wt % of amide or amide derivative of saturated higher fatty acid having 14 to 22 carbon atoms; B2: 0.2 to 0.6 wt % of salt of saturated higher fatty acid having 14 to 22 carbon atoms; and C: 0.01 to 3 wt % of auxiliaries C such as stabilizers, oxidation retarders, agents against heat and UV light decomposition.
摘要:
The invention relates to a thermoplastic molding material for 3-D printing, containing components A, B, and C: A: 40 to 100 wt % of at least one vinyl aromatic homo- or copolymer A having an average molar mass Mw of 150,000 to 360,000 g/mol, B: 0 to 60 wt % of one or more further polymers B selected from: polycarbonates, polyamides, poly(meth)acrylates, and polyesters and vinyl aromatic/diene copolymers (SBCs), C: 0 to 50 wt % of common additives and auxiliary agents, wherein the molding material has a viscosity (measured as per ISO 11443) not higher than 1×105 Pa*s at shear rates of 1 to 10 1/s and at temperatures of 250° C. and a melt volume rate (MVR, measured as per ISO 1133 at 220° C. and a load of 10 kg) of more than 6 ml/10 min.
摘要:
Thermoplastic elastomer compositions can be use for medical applications, Comprising: a) 97.1 to 90.9 wt.-% star-shaped block copolymer A with identical arms of the structure [S1-(S/B)k-(S/B)l-(S/B)m-S2]n-X, where S1 and S2 are vinylaromatic hard polymer and S/B are soft random vinylaromatic/diene copolymer blocks; X is a coupling center; and b) 2.9 to 9.1 wt.-% plasticizer B.
摘要:
High heat resistant ABS molding compositions for use in the automotive sector, electronics, and household or healthcare sector comprising: (A) 15 to 35 wt.-% ABS graft copolymer (A); (B) 15 to 35 wt.-% a-methylstyrene/acrylonitrile copolymer (B) (weight ratio 95:5 to 50:50); (C) 20 to 40 wt.-% styrene/acrylonitrile copolymer (C) (weight ratio 95:5 to 50:50; Mw 150,000 to 300,000); (D) 10 to 30 wt.-% random terpolymer (D) made from 13 to 27 wt.-% α, β ethylenically unsaturated cyclic anhydride, 60 to 74 wt.-% aromatic vinyl monomer, and 13 to 27 wt.-% maleimide monomer); (E) 0.1 to 5 wt.-%, of at least one elastomeric block copolymer (E) comprising a vinylaromatic monomer block S and an elastomeric random diene/vinylaromatic onomer block B/S; hard phase proportion is 1 to 40 vol.-% and the diene proportion is less than 50 wt.-%; and (F) 0 to 5 wt.-% of further additives and/or processing aids (F).