Thermoplastic resin composition
    2.
    发明授权

    公开(公告)号:US11136449B2

    公开(公告)日:2021-10-05

    申请号:US16473058

    申请日:2017-12-20

    IPC分类号: C08L25/12 C08K3/22 C08L25/16

    摘要: A thermoplastic resin composition of the present invention comprises: (A) 100 parts by weight of a thermoplastic resin comprising (A1) a rubber-modified aromatic vinyl-based graft copolymer, (A2) an aromatic vinyl-based copolymer resin having a flow index of about 5 g/10 min to about 8 g/10 min as measured by the ASTM D 1238 standard, and (A3) an α-methylstyrene copolymer; and (B) about 0.1 to about 10 parts by weight of zinc oxide, wherein the zinc oxide has a size ratio (B/A) of peak A in the region of 370 nm to 390 nm to peak B in the region of 450 nm to 600 nm of about 0.01 to about 1 in photoluminescence measurement, and has a BET surface area of about 10 m2/g or less as measured by a BET analyzer.

    Blow-moldable polyamide compositions

    公开(公告)号:US10655013B2

    公开(公告)日:2020-05-19

    申请号:US16259408

    申请日:2019-01-28

    申请人: BASF SE

    摘要: Thermoplastic molding compositions comprising A) from 10 to 99.7% by weight of a polyamide, B) from 1 to 30% by weight of an impact modifier, C) from 0.1 to 10% by weight of a copolymer of C1) from 50 to 95% by weight of styrene or substituted styrenes of the general formula I or a mixture of these in which R is an alkyl radical having from 1 to 8 carbon atoms or a hydrogen atom and R1 is an alkyl radical having from 1 to 8 carbon atoms and n has the value 0, 1, 2, or 3, and C2) from 5 to 50% by weight of structural units derived from one or more dicarboxylic anhydrides, D) from 0.001 to 20% by weight of iron powder, E) from 0.05 to 3% by weight of a copper-containing stabilizer, F) from 100 ppm to 5% by weight of a phosphorus-containing, inorganic acid or salts thereof or ester derivatives thereof or a mixture thereof, G) from 0 to 2% by weight of a polyethyleneimine homo- or copolymer, H) from 0 to 60% by weight of further additives, where the total of the percentages by weight of A) to H) is 100%.

    Method of preparing thermoplastic resin

    公开(公告)号:US10392457B2

    公开(公告)日:2019-08-27

    申请号:US15528492

    申请日:2016-09-08

    申请人: LG CHEM, LTD.

    摘要: The present invention relates to a method of preparing a thermoplastic resin. More particularly, the present invention relates to a method of preparing a thermoplastic resin, the method including a coagulation step of adding a water-soluble silicate compound and a metal salt coagulant to an α-methylstyrene-vinyl cyan compound copolymer latex, followed by coagulation. In accordance with the present invention, a method of preparing a thermoplastic resin having superior heat resistance by adding an additive during coagulation and aging of α-methylstyrene-vinyl cyan compound copolymer latex while controlling an addition time point of the additive is provided.

    Blow-Moldable Polyamide Compositions
    9.
    发明申请

    公开(公告)号:US20190153223A1

    公开(公告)日:2019-05-23

    申请号:US16259408

    申请日:2019-01-28

    申请人: BASF SE

    摘要: Thermoplastic molding compositions comprising A) from 10 to 99.7% by weight of a polyamide, B) from 1 to 30% by weight of an impact modifier, C) from 0.1 to 10% by weight of a copolymer of C1) from 50 to 95% by weight of styrene or substituted styrenes of the general formula I or a mixture of these in which R is an alkyl radical having from 1 to 8 carbon atoms or a hydrogen atom and R1 is an alkyl radical having from 1 to 8 carbon atoms and n has the value 0, 1, 2, or 3, and C2) from 5 to 50% by weight of structural units derived from one or more dicarboxylic anhydrides, D) from 0.001 to 20% by weight of iron powder, E) from 0.05 to 3% by weight of a copper-containing stabilizer, F) from 100 ppm to 5% by weight of a phosphorus-containing, inorganic acid or salts thereof or ester derivatives thereof or a mixture thereof, G) from 0 to 2% by weight of a polyethyleneimine homo- or copolymer, H) from 0 to 60% by weight of further additives, where the total of the percentages by weight of A) to H) is 100%.

    Spandex fiber having improved adhesive characteristics with hot melt adhesive and method for manufacturing same

    公开(公告)号:US10174197B2

    公开(公告)日:2019-01-08

    申请号:US14893031

    申请日:2014-01-07

    摘要: The present invention relates to a spandex fiber and a method for manufacturing the same that is capable of providing excellent adhesive characteristics, by means of a hot melt adhesive, between the spandex fiber and a polypropylene nonwoven fabric or a polyethylene film, during a diaper-manufacturing process. The method for manufacturing a spandex fiber comprises the steps of: preparing a polyurethane urea solution as a spinning solution; and dry-spinning the spinning solution to obtain the spandex fiber, where the polyurethane urea solution contains, with respect to the weight of the solid content, about 0.1 to 30 wt. % of an ethylene vinyl acetate monomer or polymer, or a derivative thereof, a C9 hydrocarbon-based resin monomer or polymer, or a derivative thereof, a C5 hydrocarbon-based resin monomer or polymer, or a derivative thereof, or a C5/C9 hydrocarbon-based resin monomer or copolymer, or a derivative thereof.