摘要:
The eyewear material is an eyewear material containing thermoplastic polyurethane. The eyewear material has a tan δ peak at both less than 0° C. and 0° C. or more and 70° C. or less observed in dynamic viscoelasticity measurement in tensile mode under the measurement conditions of a temperature increase speed of 5° C./min and a measurement frequency of 10 Hz.
摘要:
A polymerizable composition for an optical material containing two or more different monomers for an optical material, and a polymerization catalyst, in which at least one of the two or more different monomers for an optical material is an isocyanate compound containing no aromatic rings, a content of the polymerization catalyst with respect to a total of 100 parts by mass of the two or more different monomers for an optical material is from more than 0.05 parts by mass to 2.0 parts by mass, and a viscosity measured by a B-type viscometer at 25° C. and 60 rpm is from 10 mPa·s to 1,000 mPa·s.
摘要:
A polymerizable composition for an optical material according to the present invention includes one or two or more compounds selected from the group consisting of component (A): an ester compound having a specific structure and component (B): an ether compound having a specific structure, and a polymerizable compound.
摘要:
Disclosed is a polymerizable composition for an optical material containing polyisocyanate (a) including aliphatic polyisocyanate (a1) and a modified aliphatic polyisocyanate (a2); and polythiol (b) having a di- or higher functional thiol group, in which the modified aliphatic polyisocyanate (a2) is contained in the polyisocyanate (a) in the amount of less than or equal to 60 weight %.
摘要:
A polymerizable composition for an optical material containing two or more different monomers for an optical material, and a polymerization catalyst, in which at least one of the two or more different monomers for an optical material is an isocyanate compound containing an aromatic ring, a content of the polymerization catalyst with respect to a total of 100 parts by mass of the two or more different monomers for an optical material is from 0.010 parts by mass to 0.50 parts by mass, and the viscosity measured by a B-type viscometer at 25° C. and 60 rpm is from 10 mPa·s to 1,000 mPa·s.
摘要:
The polymerizable composition for an optical material of the present invention includes a compound (A) represented by General Formula (a) and including two or more allyloxycarbonyl groups, at least one kind of radical polymerization initiator (B) selected from the group consisting of a peroxyketal-based radical polymerization initiator, a peroxymonocarbonate-based radical polymerization initiator, and a peroxyester-based radical polymerization initiator, and a modifier (C) selected from a polyether modified siloxane compound represented by General Formula (c1) or a polyol compound represented by General Formula (c2).
摘要:
There is provided a polymerizable composition for an optical material including a polyether-modified compound having a polyether group represented by General Formula (4) below, and a polymerization reactive compound. (In General Formula (4), R25 represents a linear or branched alkylene group having 1 to 20 carbon atoms, R26 represents a hydrogen atom, a linear or branched alkyl group having 1 to 20 carbon atoms, a linear or branched alkenyl group having 2 to 20 carbon atoms, or a linear or branched alkynyl group having 2 to 20 carbon atoms, a plurality of present R25's may be the same or different, and k is an integer equal to or more than 1.)
摘要:
1,4-bis(isocyanatomethyl)cyclohexane contains 70 mol % or more and 95 mol % or less of a trans isomer relative to a total amount of a cis isomer and the trans isomer, and 0.1 ppm or more and 300 ppm or less of the compound represented by formula (1) below:
摘要:
A process for producing a plastic lens includes a step of stirring and mixing a solution including a polymerization reactive compound in a preparation tank; a step of transferring the polymerizable composition obtained in the step from the preparation tank to a lens casting mold; a step of curing the polymerizable composition; and a step of obtaining a plastic lens molded product by separating the obtained resin from the lens casting mold. The step of transferring the polymerizable composition includes a step of re-mixing the polymerizable composition discharged from the preparation tank and injecting the polymerizable composition into the lens casting mold.