摘要:
The hard coat layer-forming composition of this invention includes (A) composite oxide fine particles with a mean particle diameter of 1 to 200 nm, containing titanium, tin and optionally silicon, and with a rutile-type crystal structure, (B) an organosilicon compound represented by the formula R1aR2bSi(OR3)4−(a+b) and/or a hydrolyzate thereof, and (C) a cyanamide derivative compound. A hard coat layer formed from the composition not only is excellent in transparency, scratch resistance, adhesion property, weathering resistance, impact resistance, etc. but also can enjoy no coloration or little coloration, particularly in bluing or yellowing, upon exposure to or irradiation with ultraviolet rays, even if an antireflection film is provided.
摘要:
A hard coat or a transparent film having excellent adhesion to a polycarbonate substrate is provided. The transparent film-forming coating liquid of the present invention comprises the following components (A) to (D): (A) an organosilicon compound and/or a hydrolyzate of the organosilicon compound, (B) metal oxide fine particles each of which comprises a metal oxide core particle and a coating layer composed of antimony oxide, (C) one or more curing agents (curing agent (A)) selected from the group consisting of a polythiol compound, an organic polycarboxylic acid and an acetylacetone metal complex, and (D) a curing agent (curing agent B) comprising a compound containing basic nitrogen. The metal oxide particles (B) have been surface-modified with an organosilicon compound or an amine compound.
摘要:
The hard coat layer-forming composition of this invention includes (A) composite oxide fine particles with a mean particle diameter of 1 to 200 nm, containing titanium, tin and optionally silicon, and with a rutile-type crystal structure, (B) an organosilicon compound represented by the formula R1aR2bSi(OR3)4−(a+b) and/or a hydrolyzate thereof, and (C) a cyanamide derivative compound. A hard coat layer formed from the composition not only is excellent in transparency, scratch resistance, adhesion property, weathering resistance, impact resistance, etc. but also can enjoy no coloration or little coloration, particularly in bluing or yellowing, upon exposure to or irradiation with ultraviolet rays, even if an antireflection film is provided.
摘要:
A composite polymer is obtained by reacting (a) an elastomer having a carboxyl group with (b) metal oxide fine particles each having an epoxy ring-containing group on the particle surface. A thermally cured product of the composite polymer is a material favorable for forming a primer layer which has not only high transparency but also excellent adhesion to a hard coat layer and is excellent also in scratch resistance, heat resistance, weathering resistance, dyeing property, impact resistance and the like. An article such as an optical article whose primer layer comprises the thermally cured product of the composite polymer has high transparency and is excellent also in heat resistance.
摘要:
The present invention relates to a coating composition containing metal oxide particles with a high refractive index and low photocatalytic activity and a coating film obtained by applying the coating composition onto a substrate. The coating composition contains metal oxide particles with a high refractive index obtained by coating the specific fine particles of the titanium-based oxide on their surfaces with at least a silica-based oxide or a silica-based composite oxide, and the coating film is obtained by applying the coating composition onto a substrate. The metal oxide particles with not only a high refractive index but also low photocatalytic activity, and therefore a coating film with excellent weathering resistance and light resistance can be formed on a substrate.
摘要:
An optical element in which a hard coat layer is formed on an organic glass base material surface via a primer layer. For a primer composition forming a primer layer, whole or the main body of the primer layer formation polymer is made as being ester based TPE. Moreover, a hard coat composition forming a hard coat layer is consisted of a hydrolysate of alkoxysilane in which trialkoxysilane containing monoexpoxy organic group is the main body as a matrix formation ingredient, and the titanium based metal oxide complex particle as being an optical interference control agent, the foregoing titanium based metal oxide complex particle is consisted of T1O2 as the main body, SiO2 as a major sub-ingredient, and further, ZrO2 and K2O as a trace sub-ingredient. An optical element of the present invention is capable of suppressing optical interference even if it is a high refractive index base material and the stability of coated film portion is also excellent as well as has a variety of properties comparable to the conventional optical parts.
摘要:
A coating composition that can be applied to optical plastic moldings having a high refractive index, to protect them from deterioration by light without any adverse effect on their optical functions. The coating composition contains the following essential constituents.(A) 1 part of a hydrolyzate of a silane compound;(B) 0.2-5 parts of titanium oxide-based composite fine particles having a particle diameter of 1-100 nm in which titanium oxide integrally combines with iron oxide, with the ratio of iron oxide to titanium oxide being 0.005-0.15 by weight;(C) 0.02-0.5 part of an unsaturated or saturated polycarboxylic acid or an anhydride thereof; and(D) 0.01-0.2 part of a heat-curing catalyst.
摘要:
The present invention relates to a coating composition containing metal oxide particles with a high refractive index and low photocatalytic activity and a coating film obtained by applying the coating composition onto a substrate. The coating composition contains metal oxide particles with a high refractive index obtained by coating the specific fine particles of the titanium-based oxide on their surfaces with at least a silica-based oxide or a silica-based composite oxide, and the coating film is obtained by applying the coating composition onto a substrate. The metal oxide particles with not only a high refractive index but also low photocatalytic activity, and therefore a coating film with excellent weathering resistance and light resistance can be formed on a substrate.