摘要:
Ethylene polymer composites, concentrates and a process utilized for their preparation are provided. The composites of the invention have increased melt strength compared to the base resin and other improved physical characteristics. The composites contain an organically modified clay and may also contain a compatibilizng agent, depending on the base resin used.
摘要:
Ethylene polymer composites, concentrates and a process utilized for their preparation are provided. The composites of the invention have increased melt strength compared to the base resin and other improved physical characteristics. The composites contain an organically modified clay and may also contain a compatibilizng agent, depending on the base resin used.
摘要:
Ethylene polymer composites and concentrates utilized for their preparation are provided. The composites of the invention have increased melt strength compared to the base resin and other improved physical characteristics. The composites contain an organically modified clay and may also contain a compatibilizng agent, depending on the base resin used.
摘要:
Resins comprising a relatively high-density, low-molecular-weight polyethylene component and a relatively low-density, high-molecular-weight ethylene copolymer component and methods of making the resins are disclosed. The rheological polydispersity of the high-density component exceeds that of either the resin or the low-density component. The resins are valuable for making films, sheets, coatings, pipes, fibers, and molded articles having a favorable balance of good stiffness and excellent environmental stress crack resistance.
摘要:
A process for extrusion coating metal foils and metallized films which utilizes a mixture of silanated and non-silanated ethylene polymers is provided.
摘要:
Disclosed is a method for making LLDPE grades having different xylene solubles or hexane extractables with the same Ziegler-Natta catalyst by varying the amount of alkylaluminum used for polymerization. The method comprises copolymerizing ethylene with a C3-10 α-olefin in the presence of a Ziegler-Natta catalyst, an alkylaluminum, and an electron donor; determining the dependency of the xylene solubles or hexane extractables on the alkylaluminum/electron donor ratio; and adjusting the alkylaluminum/electron donor ratio to achieve a desired xylene solubles or hexane extractables.
摘要:
A process for polymerizing ethylene is disclosed. The polymerization is performed in the presence of a Ziegler-Natta catalyst system in two slurry reaction zones. Most of the polyethylene (70-95 wt. %) is produced in one of the zones, while a smaller fraction is produced in the other zone. The ratio of the weight average molecular weight of the smaller fraction to that of the larger fraction is greater than 8:1. The resulting polyethylene blend, which should have both high melt strength and high extrudate swell, will be useful for blow-molding applications.
摘要:
A polyethylene having improved rheological properties is disclosed. The polyethylene has a melt index (MI2) from about 0.01 dg/min to about 50 dg/min and a melt strength (&eegr;) that satisfies MI2×&eegr;≧3.5. A process for making the polyethylene is also disclosed. The process uses an azaborolinyl-containing single-site catalyst in the presence of hydrogen, where the hydrogen consumption is controlled to be less than 30%.
摘要:
A process for improving the melt characteristics of polyethylene resins is provided. The process involves contacting a polyethylene resin powder with a low level of free radical initiator at a temperature below the melting point of the resin.
摘要:
A very low density polyethylene (VLDPE) film is disclosed. The film has a high average heat seal strength and physical strength. The VLDPE has a density within the range of about 0.880 to 0.914 g/cm3. The film has a seal initiation temperature lower than or equal to 95° C. and an average heat seal strength greater than or equal to 1.75 lb/in. The film has a machine-direction (MD) modulus greater than or equal to 12,000 psi. The film can be used as a monolayer film or as a layer of a multilayer film. It is suitable for heat sealable bags and many other applications.
摘要翻译:公开了一种非常低密度的聚乙烯(VLDPE)膜。 该膜具有高的平均热封强度和体力。 VLDPE的密度在约0.880-0.914g / cm 3的范围内。 该膜具有低于或等于95℃的密封起始温度和大于或等于1.75磅/英寸的平均热密封强度。 该膜具有大于或等于12,000psi的机器方向(MD)模量。 该膜可以用作单层膜或多层膜的层。 适用于热封袋和许多其他应用。