摘要:
A phthalate-free procatalyst composition is disclosed for olefin polymerization that exhibits excellent polymerization activity and response to hydrogen, and can produce a polyolefin exhibiting high stereoregularity, high melt flow rate, and desirable molecular weight distribution. The method for producing the procatalyst composition includes reaction of a magnesium support precursor with a tetravalent titanium halide and a combination of different internal electron donors. The first internal electron donor may comprise one or more substituted phenylene aromatic diester and the second internal electron donor may comprise a polyether, preferably a 1,3-diether. In one embodiment, the support precursor comprises a spherical spray crystalized MgCl2-EtOH adduct.
摘要:
A Prepolymerized catalyst component for the polymerization of olefins comprising a solid catalyst component which comprises Mg, Ti, and chlorine atoms and an electron donor (ID) said prepolymerized catalyst component being characterized by the fact that: the electron donor (ID) is constituted by at least 80% mol of 1,3 diethers with respect to the total molar amount of electron donor compounds; the prepolymerized catalyst has a porosity due to pores with diameters up to 1 μm of less than 0.2 cm3/g; it contains an amount of ethylene prepolymer of less than 45% with respect to the total weight of prepolymerized catalyst.
摘要:
The instant invention provides a polyolefin composition, a catalyst composition, and a method of producing the same. The method for polymerizing one or more polyolefins according to the present invention comprises the steps of: (1) selecting a first olefin monomer and optionally one or more alpha-olefin comonomers; (2) selecting one or more catalyst systems comprising one or more procatalysts comprising a first metal selected from the group consisting of Ti, V, Hf, Zr, and combinations or mixture two or more thereof, one or more cocatalysts comprising Al, and one or more self-limiting agents (SLA) selected from the group consisting of polyether, polyester, and combinations or mixtures thereof; wherein the ratio of said SLA to said first metal (SLA:first metal) is from 0.1:1 to 30:1; (3) polymerizing said first olefin monomer and optionally one or more alpha-olefin comonomers in the presence of said one or more catalyst systems via a slurry polymerization process or gas-phase polymerization process in one or more reactors; (4) thereby producing one or more olefin-based polymers; (5) wherein said catalyst system has a loss of least 85 percent of catalyst activity when the temperature is increased from 85 to 110° C.
摘要:
A polyethylene composition made from or containing a polyethylene, having the following features: 1) a density from about 0.930 to about 0.945 g/cm3, determined according to ISO 1183 at 23° C.; 2) a ratio of MIF/MIP from about 30 to about 55; 3) a MIF from about 3 to about 25 g/10 min.; 4) a Mz equal to or greater than about 1,500,000 g/mol; and 5) a long-chain branching index, LCBI, equal to or lower than about 0.55, wherein the LCBI is the ratio of the measured mean-square radius of gyration Rg, measured by GPC-MALLS, to the mean-square radius of gyration for a linear PE having about the same molecular weight of 1,000,000 g/mol.
摘要:
A polyethylene composition made from or containing a polyethylene, having the following features: 1) a density from about 0.930 to about 0.945 g/cm3, determined according to ISO 1183 at 23° C.; 2) a ratio of MIF/MIP from about 10 to less than about 30; 3) a MIF from about 3 to about 25 g/10 min.; 4) a Mz equal to or greater than about 1,500,000 g/mol; and 5) a long-chain branching index, LCBI, equal to or lower than about 0.55, wherein the LCBI is the ratio of the measured mean-square radius of gyration Rg, measured by GPC-MALLS, to the mean-square radius of gyration for a linear PE having the about same molecular weight of 1,000,000 g/mol.
摘要:
Preparing propylene polymer compositions comprising 50 to 90% by weight of a propylene (co)polymer, and 10 to 50% by weight of an ethylene copolymer. The polymerization process includes, in the presence of a catalyst system: (i) a first step of polymerizing propylene to produce the propylene (co)polymer; and (ii) a successive gas-phase polymerization step performed in the presence of the propylene (co)polymer, ethylene, and one or more α-olefins to produce the ethylene copolymer. The catalyst system contains the product obtained by contacting: (a) a solid catalyst component comprising at least two internal electron donor compounds, a succinate and a 1,3-diether; (b) an aluminum hydrocarbyl compound, and (c) optionally, an external electron donor compound.
摘要:
The present disclosure provides a catalyst system made from or containing: (A) a solid catalyst component made from or containing (i) a titanium compound supported on a magnesium dichloride; (B) an aluminum alkyl compound; and (C) a halogenated organic ester of formula A-COOR, wherein R is a C1-C10 hydrocarbon group and A is a C1-C15 saturated or unsaturated hydrocarbon group in which at least one of the hydrogen atoms is replaced by a chlorine atom. The present disclosure also provides a process for preparing an olefinic polymer, including a polymerization step of polymerizing an olefin in the presence of the catalyst system. The present disclosure also provides an olefinic polymer made therefrom.
摘要:
An object of the present invention is to provide a propylene-based resin composition capable of providing a molded article having an excellent balance between rigidity and impact resistance. The object can be achieved by a propylene-based resin composition including an olefin-based resin characterized by including a grafted ethylene-based copolymer having an ethylene polymer as a side chain.
摘要:
A copolymer of propylene with hexene-1 containing from 5 to 9% by weight of recurring units derived from hexene-1, having a melting temperature from 125° C. to 140° C. and Melt Flow Rate (ASTM D1238, 230° C./2.16 Kg) from 0.1 to 3 g/10 min., is used to produce blown films having valuable mechanical and optical properties.
摘要:
The present invention provides a catalyst component for olefin polymerization, obtained by a reaction of magnesium, titanium, halogen and an internal electron donor, the internal electron donor comprising an imine compound as shown in Formula Z. The present invention also provides a preparation method of the catalyst component, and a catalyst for olefin polymerization containing the same. When the catalyst of the present invention is used for olefin polymerization reaction, the catalyst has a high activity, and a slow rate of activity decay, and the obtained polymer has a high isotacticity index, and a wide molecular weight distribution.