摘要:
A process for producing a propylene resin formed article with a hard coat is disclosed, comprising forming an ultraviolet-curing acrylic resin coating film on the surface of a propylene resin film or sheet, subjecting the film or sheet with the coating film to thermoforming, and irradiating the coating film to ultraviolet rays to cure said ultraviolet-curing resin, wherein said propylene resin film or sheet is composed of at least a propylene resin surface layer containing substantially no nucleating agent on which surface is coated said acrylic resin film and a thermoplastic resin base layer containing a nucleating agent which is laminated on the other side of said propylene resin surface layer prior to the thermoforming. The hard coat on the propylene resin formed article has high gloss.
摘要:
A laminated resin film having a thickness of from 7 to 25 .mu.m comprised of (A) a poly(4-methylpentene-1) resin layer having a thickness of from 1 to 10 .mu.m having laminated on one or both sides thereof (B) a crystalline propylene copolymer resin layer comprising from 1 to 10% by weight of ethylene, from 74 to 96% by weight of propylene, and from 3 to 25% by weight of an .alpha.-olefin containing from 4 to 8 carbon atoms and having a thickness of from 2 to 20 .mu.m, provided that the total thickness of layers (B) when provided on each side of layer (A) is in the range of from 4 to 20 .mu.m. The laminated film has excellent cutting properties and high heat resistance sufficient for use in microwave cooking.
摘要:
A process for producing an oriented blown film of a thermoplastic resin by blown film extrusion, carried out by blowing air into an extruded bubble of the resin extruded from a ring die to expand the bubble and cooling the expanded bubble with air from a cooling air ring, wherein blown film extrusion is carried out under such conditions that the ratio of (b) the final diameter of the expanded bubble to (a) the diameter of the bubble at the crystallizing temperature of the thermoplastic resin ((b)/(a)) ranges from 1.5 to 10. The process provides an oriented blown film excellent in strength, appearance, and heat shrinkage characteristics.
摘要:
A polyolefin-based wrapping film having one or more layers which satisfies the following conditions (1) to (4):(1) the film has a thickness ranging from 6 to 100 .mu.m;(2) the film has a birefringence .DELTA.n.sub.A of from 0.6.times.10.sup.-3 to 8.times.10.sup.-3 ;(3) the film has a ratio of percent heat shrinkage in MD to percent heat shrinkage in TD of from 0.65 to 1.50 in a silicon oil bath at 140.degree. C. for 3 minutes; and(4) the film has a strain recovery of at least 18 mm,which provides excellent performance properties in stretch wrapping, especially in the area of high deformation recover.
摘要:
The present invention relates to a film for use in stretch-packaging that comprises an intermediate layer which contains as its main component an .alpha.-olefin-series resin component containing a butene-1-series resin and at least two surface layers each containing an ethylene-vinyl acetate copolymer resin as its main component, the surface layers being laminated over both surfaces of the intermediate layer. The film has remarkably high values of tear strength and recovery from deformation.
摘要:
A laminate film for stretch-wrapping is disclosed, comprising an intermediate layer containing from 50 to 95% by weight of an ethylene-.alpha.-olefin copolymer, a propylene-ethylene-.alpha.-olefin random copolymer, a propylene-.alpha.-olefin random copolymer, a butene-1 homopolymer, or a butene-1-ethylene copolymer and from 5 to 50% by weight of a hydrogenated block copolymer elastomer having laminated on both sides thereof a surface layer comprising from 75 to 95% by weight of ethylene and from 5 to 25% by weight of vinyl acetate. The film is excellent in stretchability, softness, tear strength, and in particular deformation recovery properties.
摘要:
A method for producing an antibacterial molded article of polyolefin resin is described, comprising molding a polyolefin resin composition having compounded therewith 0.01% by weight or more, based on the polyolefin resin composition, of an antibacterial agent which is a zeolite containing silver to form a molded article of a desired shape, and thereafter subjecting the antibacterial surface of the molded article to a corona discharge treatment.
摘要:
A display module 1 of the present invention includes a first board 3, a second board 4, a base film 5, and a circuit member 2. The first board 3 and the second board 4 are bonded together to face with each other. The base film 5 is provided between the first board 3 and the second board 4 and extends outwardly from an end of the first board 3. The base film 5 has an insulating property and the extended portion is bent to an outer surface side of one of the first board 3 and the second board 4. The circuit member 2 is formed on the base film 5.
摘要:
A measuring method of a hole diameter of a holey optical fiber includes calculating an arithmetical mean value I(x) from two backscattering light intensities at a position x of two backscattering light waveforms of the holey optical fiber, in which the two backscattering light waveforms are obtained by OTDR measurement; and obtaining the hole diameter at the position x, based on a correlation between an arithmetical mean value I(x) and an hole diameter of the holey optical fiber that is obtained in advance.
摘要:
A toner with good low-temperature fixability even in light-pressure type fixing units, which causes no contamination of fixing films and provides images having stable image densities and excellent image quality after long-term use. The toner includes a toner particle containing a binder resin, a coloring agent, a release agents (a) and (b) The release agent (a) is a monofunctional or bifunctional ester wax; the release agent (b) is a hydrocarbon wax; a solubility of the release agent (a) into the binder resin is higher than that of the release agent (b). When tetrahydrofuran-soluble components of the toner are subjected to GPC, a proportion of components having a molecular weight of 500 or less is 2.5 area % or less. When the tetrahydrofuran-soluble components at 25° C. are subjected to SEC-MALLS, a weight-average molecular weight Mw thereof is 5,000-100,000, and the Mw and the radius of gyration Rw thereof satisfy 5.0×10−4≦Rw/Mw≦1.0×10−2.