摘要:
A high-strength galvanized steel sheet has a TS of at least 590 MPa and excellent ductility and stretch flangeability and a method for manufacturing the high-strength galvanized steel sheet. The galvanized steel sheet contains, on the basis of mass percent, C: 0.05% to 0.3%, Si: 0.01% to 2.5%, Mn: 0.5% to 3.5%, P: 0.003% to 0.100% or less, S: 0.02% or less, and Al: 0.010% to 1.5%. The total of Si and Al is 0.5% to 2.5%. The remainder are iron and incidental impurities, contain 20% or more of ferrite phase, 10% or less of martensite phase, and 10% to 60% of tempered martensite, on the basis of area percent, and 3% to 10% of retained austenite phase on the basis of volume fraction. The retained austenite has an average grain size of 2.0 μm or less.
摘要:
The present invention provides a high-strength galvanized steel sheet having excellent ductility, stretch flangeability, and fatigue resistance, and a method for manufacturing the same. A high-strength galvannealed steel sheet having excellent formability and fatigue resistance is characterized in that the steel sheet is composed of steel having a composition containing, by % by mass, C: 0.05% to 0.3%, Si: 0.5% to 2.5%, Mn: 1.0% to 3.5%, P: 0.003% to 0.100%, S: 0.02% or less, Al: 0.010% to 0.1%, and the balance including iron and unavoidable impurities, and the steel sheet has a microstructure containing 50% or more of ferrite, 5% to 35% of martensite, and 2% to 15% of pearlite in terms of an area ratio, the martensite having an average gain size of 3 μm or less and an average distance of 5 μm or less between adjacent martensite grains.
摘要:
A high-strength galvanized steel sheet has a TS of at least 590 MPa and excellent ductility and stretch flangeability and a method for manufacturing the high-strength galvanized steel sheet. The galvanized steel sheet contains, on the basis of mass percent, C: 0.05% to 0.3%, Si: 0.01% to 2.5%, Mn: 0.5% to 3.5%, P: 0.003% to 0.100% or less, S: 0.02% or less, and Al: 0.010% to 1.5%. The total of Si and Al is 0.5% to 2.5%. The remainder are iron and incidental impurities, contain 20% or more of ferrite phase, 10% or less of martensite phase, and 10% to 60% of tempered martensite, on the basis of area percent, and 3% to 10% of retained austenite phase on the basis of volume fraction. The retained austenite has an average grain size of 2.0 μm or less.
摘要:
A high-strength galvanized steel sheet is provided which has a tensile strength of a level of about 590 MPa and superior formability, including a coating with good appearance. The galvanized steel sheet includes a base steel and a galvanized coating layer formed over the surface of the base steel. The galvanized steel sheet has a chemical composition containing 0.005% to 0.12% of C, 0.7% to 2.7% of Si, 0.5% to 2.8% of Mn, 0.1% or less of P, 0.07% or less of S, 1.0% or less of Al, 0.008% or less of N, and the balance being Fe and inevitable impurities on a mass basis, and a microstructure constituted of at least 90% of ferrite and 2% to 10% of martensite on an area basis. The ferrite has a Vickers hardness of 120 or more on average, and an inclusion is precipitated from the grain boundary with a length of 50% or less relative to the entire length of the grain boundary in the surface layer of the base steel with a depth of 3 μm from the interface between the coating layer and the base steel.
摘要:
The present invention provides a high-strength galvanized steel sheet having excellent ductility, stretch flangeability, and fatigue resistance, and a method for manufacturing the same. A high-strength galvannealed steel sheet having excellent formability and fatigue resistance is characterized in that the steel sheet is composed of steel having a composition containing, by % by mass, C: 0.05% to 0.3%, Si: 0.5% to 2.5%, Mn: 1.0% to 3.5%, P: 0.003% to 0.100%, S: 0.02% or less, Al: 0.010% to 0.1%, and the balance including iron and unavoidable impurities, and the steel sheet has a microstructure containing 50% or more of ferrite, 5% to 35% of martensite, and 2% to 15% of pearlite in terms of an area ratio, the martensite having an average gain size of 3 μm or less and an average distance of 5 μm or less between adjacent martensite grains.
摘要:
A high-strength galvanized steel sheet is provided which has a tensile strength of a level of about 590 MPa and superior formability, including a coating with good appearance. The galvanized steel sheet includes a base steel and a galvanized coating layer formed over the surface of the base steel. The galvanized steel sheet has a chemical composition containing 0.005% to 0.12% of C, 0.7% to 2.7% of Si, 0.5% to 2.8% of Mn, 0.1% or less of P, 0.07% or less of S, 1.0% or less of Al, 0.008% or less of N, and the balance being Fe and inevitable impurities on a mass basis, and a microstructure constituted of at least 90% of ferrite and 2% to 10% of martensite on an area basis. The ferrite has a Vickers hardness of 120 or more on average, and an inclusion is precipitated from the grain boundary with a length of 50% or less relative to the entire length of the grain boundary in the surface layer of the base steel with a depth of 3 μm from the interface between the coating layer and the base steel.
摘要:
A high strength galvanized steel sheet has a TS of 590 MPa or more and excellent processability. The component composition contains, by mass %, C: 0.05% to 0.3%, Si: 0.7% to 2.7%, Mn: 0.5% to 2.8%, P: 0.1% or lower, S: 0.01% or lower, Al: 0.1% or lower, and N: 0.008% or lower, and the balance: Fe or inevitable impurities. The microstructure contains, in terms of area ratio, ferrite phases: 30% to 90%, bainite phases: 3% to 30%, and martensite phases: 5% to 40%, in which, among the martensite phases, martensite phases having an aspect ratio of 3 or more are present in a proportion of 30% or more.
摘要:
A high-strength cold-rolled steel sheet and high-strength galvanized steel sheet has a TS of 1180 MPa or more and excellent formability including stretch flangeability and bendability. The high-strength cold-rolled steel sheet contains 0.05% to 0.3% C, 0.5% to 2.5% Si, 1.5% to 3.5% Mn, 0.001% to 0.05% P, 0.0001% to 0.01% S, 0.001% to 0.1% Al, 0.0005% to 0.01% N, and 1.5% or less Cr (including 0%) on a mass basis, the remainder being Fe and unavoidable impurities.
摘要:
A high strength galvanized steel sheet with excellent workability, having a component composition containing C: 0.04% or more, and 0.15% or less, Si: 0.7% or more, and 2.3% or less, Mn: 0.8% or more, and 2.2% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.1% or less, N: 0.008% or less, and the remainder composed of iron and incidental impurities on a percent by mass basis, and a microstructure including 70% or more of ferrite phase, 2% or more, and 10% or less of bainite phase, and 0% or more, and 12% or less of pearlite phase on an area fraction basis and 1% or more, and 8% or less of retained austenite phase on a volume fraction basis, wherein an average crystal grain diameter of ferrite is 18 μm or less and an average crystal grain diameter of retained austenite is 2 μm or less.
摘要:
The high-strength galvanized steel sheet having excellent formability has a component composition containing, on the basis of mass percent, 0.05 to 0.2% C, 0.5 to 2.5% Si, 1.5 to 3.0% Mn, 0.001 to 0.05% P, 0.0001 to 0.01% S, 0.001 to 0.1% Al, and 0.0005 to 0.01% N, the balance being Fe and incidental impurities; and the steel sheet has a microstructure including a ferritic phase and a martensitic phase including a tempered-martensitic phase, the ferritic phase having an area fraction of 30% or more relative to an entirety of the microstructure, the martensitic phase having an area fraction of 30 to 50% relative to the entirety of the microstructure, and the tempered-martensitic phase having an area fraction of 70% or more relative to an entirety of the martensitic phase.