摘要:
The present invention relates to mixtures, containing A) reaction products from isocyanates and NCO-reactive silanes and B) carbosilane dendrimers, a process for preparing powder coatings from the mixtures and their use.
摘要:
Liquid isocyanate-terminated polyurethane prepolymers are cured by mixing them with 10% to 200% by weight, based on the weight of the prepolymer, of an organic hydroxy silicate compound or their condensation product. The cured material may be non-porous elastomeric products or fine cellular products.
摘要:
Polyisocyanates are reacted chemically with an oxidated silicon compound to produce a polyisocyanate silicate prepolymer. The polyisocyanate silicate prepolymer will react with organic compounds to produce a polyisocyanate organic silicate solid/cellular solid product.
摘要:
The compositions of this invention comprise uncrosslinked reaction mixtures comprising (1) at least one organic monomer, oligomer or polymer comprising a multiplicity of organic, electrophilic substituents, and (2) at least one metal-containing polymer comprising a metal-nitrogen polymer.Preferred compositions of this invention comprise reaction mixtures comprising (1) at least one organic monomer, oligomer or polymer comprising a multiplicity of organic, electrophilic substituents, and (2) at least one of: silicon-nitrogen polymers, aluminum-nitrogen polymers and boron-nitrogen and polymer combinations thereof comprising a multiplicity of sequentially bonded repeat units the compositions comprising the reaction products of the reaction mixtures, and the compositions obtained by crosslinking the reaction products of the reaction mixtures. The crosslinking may be effected through at least one of thermal-based, radiation-based free radical-based or ionic-based crosslinking mechanisms. Furthermore, the reaction mixtures, the composition comprising the reaction products and the crosslinked composition may further comprise at least one filler or reinforcement. The composition may be molded or shaped by various techniques into numerous useful articles. Furthermore, the compositions may be applied as coatings by various techniques onto numerous articles to enhance the articles usefulness.
摘要:
A composition for preparing polyurethanes comprising an organic polyisocyanate; a poly(silyldiamine) of the unit formula ##STR1## wherein the grouping ##STR2## is a divalent organic radical terminated by two nitrogen atoms with R being a divalent organic moiety, or a divalent alicyclic radical in which R and R.sup.1 with the two nitrogens form a cyclic diamine structure, R.sup.1 is hydrogen or a monovalent hydrocarbon, R.sup.2 is a monovalent hydrocarbon, and n is an integer greater than 1; and a polyol. When poly(silyldiamines) of the above formula are reacted with a polyisocyanate prepolymer and a polymeric polyol, elastomeric polyurethanes having good elastomeric properties are obtained.
摘要:
Alkali metal aldehyde lignin-cellulose silicate polymers are reacted chemically with an epihalohydrin compound to produce a polyepoxy silicate resin; the polyepoxy silicate resin may be cured by a catalyst, e.g., an amine or Lewis acid, to produce a cured epoxy resin, solid or cellular solid product which may be used as an adhesive, as construction sheets, etc.
摘要:
Small particles of cellulose-containing plants, fine granular oxidated, silicon compounds and an alkali metal hydroxide are mixed, then heated to 150.degree. C. to 220.degree. C. while agitating until the plant particles soften or melt, thereby producing an alkali metal cellulose silicate condensation product.
摘要:
Composite resins produced from chemical reactions among a polyglycol epoxide liquid epoxy resin, an aminosilane, tri- and/or tetra-alkoxysilanes and an isocyanate. The hybrid compositions are prepared by an in situ sol-gel process where components of the composition are mixed together sequentially. The composite resins are formed by a coupling reaction between the epoxide groups of the epoxy resin and the amino groups of the aminosilane. The silanes are hydrolyzed to form silanol groups which then undergo polycondensation to form an inorganic polymeric network of an intermediate. Finally, urethane moieties are introduced to the composite resins when unreacted hydroxyl groups from the intermediate react with the isocyanate. These composite resins are evaluated as protective coatings of mild steel substrates, including mechanical strength, anticorrosiveness in a saline medium, and adhesiveness to the mild steel substrates.
摘要:
Water dispersible polyamides having carboxylic acid groups are disclosed. These are made by reacting polycarboxyl is acids or anhydrides thereof with amine containing monomer or an amide terminated polyamide under reaction conditions such that a few of the carboxylic acid groups are residual and can promote dispersion in water. These polyamides after dispersion can be chain extended to higher molecular weight polymers or can be terminally functionalized with reactive groups such as isocyanate, epoxy, vinyl, acetoacetonate, or silanol groups. Composites and hybrids of these polyamides with vinyl polymers are also disclosed and claimed.
摘要:
The present invention relates to alkoxysilane-functionalized and allophanate-functionalized urethanes, methods for the preparation thereof, coating compositions comprising these and to the use thereof.