摘要:
The invention concerns a method for producing an aluminium alloy foam, consisting essentially of the aluminium alloy, in molten form, infiltrating the interstices of a preform consisting of silicon elastomer elements, by means of a conventional moulding process, typically a low-pressure process, followed by the elimination of the preform broken down into silica powder during the moulding cycle and/or an additional baking cycle.
摘要:
A metal article containing at least 10% interconnected porosity is produced by using a preform.To make the preform, an organic binder, a wetting agent and a granular material are mixed to obtain a mouldable paste that combines 10 vol. pct. or more of the granular material, this material dissolving easily in a liquid solvent. The paste is shaped into an aerated preform, thus creating an open pore space to be infiltrated by the metal or alloy.The wetting agent is evaporated and the preform is baked to a temperature sufficient to degrade the binder and create a network of interconnected open porosity in the preform. Then, the open pore space is filled with the liquid metal or alloy.All or part of the baked preform can be easily leached by a liquid solvent through the network of fine pores.
摘要:
A three-dimensional network aluminum porous body which enables to produce an electrode continuously, an electrode using the aluminum porous body, and a method for producing the electrode is disclosed. A long sheet-shaped three-dimensional network aluminum porous body is provided to be used as a base material in a method for producing an electrode including at least winding off, a thickness adjustment step, a lead welding step, an active material filling step, a drying step, a compressing step, a cutting step and winding-up, wherein the three-dimensional network aluminum porous body has a tensile strength of 0.2 MPa or more and 5 MPa or less.
摘要:
The present invention relates to a combustion reactor for nanopowders, a synthesis apparatus for nanopowders using the combustion reactor, and a method of controlling the synthesis apparatus. The combustion reactor for nanopowders comprises an oxidized gas supply nozzle connected to an oxidized gas tube; a gas supply unit supplying a fuel gas and a precursor gas; and a reaction nozzle forming concentricity on an inner wall of the oxidized gas supply nozzle to be connected to the gas supply unit and having an inlet opening for supplying an oxidized gas disposed at a region adjacent to a jet orifice for spraying flames. In the present invention, it is possible to precisely control the stability of flames, the uniform temperature distribution of flames and the temperature of flames that affect the properties of nanopowders, and the deposition of oxide in the combustion reactor is prevented to thus enable a continuous and uniform reaction for a long time, thereby enabling an economic and efficient synthesis of nanopowders.
摘要:
A three-dimensional network aluminum porous body which enables to produce an electrode continuously, an electrode using the aluminum porous body, and a method for producing the electrode is disclosed. A long sheet-shaped three-dimensional network aluminum porous body is provided to be used as a base material in a method for producing an electrode including at least winding off, a thickness adjustment step, a lead welding step, an active material filling step, a drying step, a compressing step, a cutting step and winding-up, wherein the three-dimensional network aluminum porous body has a tensile strength of 0.2 MPa or more and 5 MPa or less.
摘要:
A preform intended for the manufacture of a metal foam having a porosity of between 62% and 85%, the preform including a set of precursors in the form of balls formed of a mixture of 12% to 25% of organic binder, 72% to 87% of sodium chloride and 1 to 3% of kalinite. The precursors have a diameter of around 1 mm to 10 mm, and preferably 4 mm, the precursors being obtained by granulating the mixture using a fluidized bed process.
摘要:
A three-dimensional network aluminum porous body which enables to produce an electrode continuously, an electrode using the aluminum porous body, and a method for producing the electrode. A long sheet-shaped three-dimensional network aluminum porous body is provided to be used as a base material in a method for producing an electrode including at least winding off, a thickness adjustment step, a lead welding step, an active material filling step, a drying step, a compressing step, a cutting step and winding-up, wherein the three-dimensional network aluminum porous body has a tensile strength of 0.2 MPa or more and 5 MPa or less.
摘要:
The invention provides foams of desired cell sizes formed from metal or ceramic materials that coat the surfaces of carbon foams which are subsequently removed. For example, metal is located over a sol-gel foam monolith. The metal is melted to produce a metal/sol-gel composition. The sol-gel foam monolith is removed, leaving a metal foam.
摘要:
A metal composite material which can show high wear resistance and durability when used as a sliding member and a process for producing such a metal includes material are proposed. The metal composite material (10) comprises a porous preform (1) containing porous aluminum borate particles (3) in which pores (3a) of the aluminum borate particles (3) are filled with a metal as a result of impregnation of a melt of the metal into the porous preform under pressure. In the metal composite material (10), the metal base material and the aluminum borate particles (3) are tightly bound to each other. Therefore, the metal composite material (10) has high strength and hardness and can show excellent wear resistance when used as a sliding member.
摘要:
The present invention relates to a combustion reactor for nanopowders, a synthesis apparatus for nanopowers using the combustion reactor, and a method of controlling the synthesis apparatus. The combustion reactor for nanopowders comprises an oxidized gas supply nozzle connected to an oxidized gas tube; a gas supply unit supplying a fuel gas and a precursor gas; and a reaction nozzle forming concentricity on an inner wall of the oxidized gas supply nozzle to be connected to the gas supply unit and having an inlet opening for supplying an oxidized gas disposed at a region adjacent to a jet orifice for spraying flames. In the present invention, it is possible to precisely control the stability of flames, the uniform temperature distribution of flames and the temperature of flames that affect the properties of nanopowders, and the deposition of oxide in the combustion reactor is prevented to thus enable a continuous and uniform reaction for a long time, thereby enabling an economic and efficient synthesis of nanopowders.