摘要:
A coating composition for application to a subsea component or structure has cellulose acetate an amount of approximately 47% by weight of the total composition, diisooctyl phthalate in an amount of approximately 17% by weight of the total composition, a fatty acid ester in an amount of approximately 23% by weight of the total composition, a vegetable oil in an amount of approximately 8% by weight of the total composition, a stabilizer and a silica amorphous in which the stabilizer and the silica amorphous are in amount of approximately 5% by weight of the total composition. The stabilizer can be either titanium dioxide or aluminum dioxide. The vegetable oil is canola oil.
摘要:
Coating a metallic surface with at least one of a pretreatment composition prior to organic coating, with a passivation composition without intent for subsequent organic coating, with a pretreatment primer composition, with a primer composition, with a paint composition and with an electrocoating composition, wherein the coating composition includes particles on a base of at least one layered double hydroxide (LDH) phase characterized by the general formula [M2+(1±0.5)−x(M3+,M4+)x(OH)2±0.75]An−x/n.mH2O.
摘要:
Corrosion-inhibiting microgels that are suitable for use in non-chromated primer compositions. Each discrete microgel is composed of a cross-linked polymer network and organic corrosion-inhibiting compounds entrapped or immobilized within the polymer network.
摘要:
Cleaned metal surfaces are coated with an aqueous anti-corrosion treatment. The anti-corrosion treatment includes an organofunctional silsesquioxane and a fluoro metallic acid such as H2TiF6, H2ZrF6, as well as others and blends. The metal surface can be rinsed immediately after coating, making this anti-corrosion treatment suitable for preparing a metal surface for electrocoating.
摘要:
The present invention provides a water-based coating system that can be used to form a durable, abrasion resistant, tough, protective coating on a wide range of substrates. The coating system advantageously has excellent adhesion properties and can be directly coated onto stainless steel surfaces without requiring an intervening primer layer. Primer layers or other types of coatings can be used in combination with the coating system of the present invention if desired, however. The coating system is particularly effective for protecting metal-containing substrates such as intermodal, refrigerated cargo containers. The resultant coatings are flexible and impact resistant. Being water-based, the coating compositions have lower VOC emissions and less residual odor than solvent-based compositions.
摘要:
A corrosion inhibiting structure includes a mineral tubule having a first end, a second end, and a lumen extending from the first end to the second end. The lumen terminates in a first opening at the first end and a second opening at the second end. The corrosion inhibiting structure also includes an anticorrosion deposit disposed within the lumen, and first and second precipitate stoppers covering the first and second openings, respectively. A coating composition includes a population of corrosion inhibiting structures and a coating material. A method of inhibiting corrosion includes loading anticorrosion agent deposits into lumens, forming stoppers at first and second openings by mixing loaded mineral tubules with a solution containing a predetermined concentration of transition metal ions, mixing the loaded mineral tubules having stoppers with a coating material to form a composite material, and applying the composite material to a metal surface.
摘要:
The present invention relates to a composition for coating metallic surfaces, comprising a binder component; a corrosion inhibitor polymer based on an ethylenically monocarboxylic and dicarboxylic acid and, if appropriate, further ethylenical monomers, a solvent component, and, if appropriate, crosslinkable components, and also pigment/filler components. The invention further relates to processes for its preparation and also to methods of coating a metallic surface using the composition, to coated metallic surfaces thus obtained, and to the use of the composition as a primer, particularly in coil coating or in atmospheric corrosion control. After drying, the applied layer preferably has a thickness of at least 3.1 μm and is therefore thicker than a typical pretreatment layer.
摘要:
Disclosed is a layered double hydroxide capable of delamination in water comprising a plurality of basal layers of a double hydroxide of Formula: M(II)1-xM(III)x(OH)2 wherein M(II) is Mg, Zn or a combination thereof, M(III) is Al, and x is 0.2 to 0.33 and a plurality of intercalated layers between each adjacent basal layers of Mg acetate, Zn acetate or Ce acetate and water of intercalation. A process for producing the layered double hydroxide is also disclosed. The layered double hydroxide find use as an vehicle component or an anti-corrosive pigment of water-based protective coatings for metallic substrates, and as a humectant or a stabilizing agent for cosmetic preparations such as lotions, creams or foundations.
摘要:
Disclosed is a metallic pigment composition that can be used in coating compositions or ink compositions, specifically, in water-based coatings and water-based inks, and exhibits superior coating material storage stability. When formed into a coating material, the metallic pigment composition has superior performance for photoluminescence, concealment, flip-flop color and other properties, and does not change the color of dyes or organic pigments. The metallic pigment composition contains: at least one organic molybdenum compound; a hydrolysate of a compound containing silicon and/or a condensate thereof; and metal particles.
摘要:
This invention relates to galvanic aluminum alloy powder-pigments coated with a semi-conducting corrosion inhibiting oxide and the process for preparing said coated powder-pigments in combination with film-forming binders for coating metal substrates to inhibit corrosion. The coated aluminum alloy powder-pigments are electrically active and prevent corrosion of metals which are more cathodic (electropositive) than the aluminum alloy pigments.