摘要:
A ceramic material having particular utility as a thermal insulating or thermal barrier coating on metallic substrates is provided. The ceramic material broadly comprises at least one oxide and the balance comprising a first oxide selected from the group consisting of zirconia, ceria, and hafnia. The at least one oxide has a formula A2O3 where A is selected from the group consisting of La, Pr, Nd, Sm, Eu, Tb, In, Sc, Y, Dy, Ho, Er, Tm, Yb, Lu, and mixtures thereof. The present invention also broadly relates to an article having a metal substrate and a thermal barrier coating as discussed above.
摘要翻译:提供了一种特别用作金属基底上的绝热或隔热涂层的陶瓷材料。 陶瓷材料广泛地包括至少一种氧化物,余量包含选自氧化锆,二氧化铈和铪的第一氧化物。 所述至少一种氧化物具有式A 2 O 3 3,其中A选自La,Pr,Nd,Sm,Eu,Tb,In,Sc ,Y,Dy,Ho,Er,Tm,Yb,Lu及其混合物。 本发明还广泛地涉及具有如上所述的金属基材和热障涂层的制品。
摘要:
A method for applying ceramic coatings using electron beam--physical vapor deposition techniques is described. The method includes the step of introducing the anionic constituent of the ceramic into a coating chamber and confining the anionic constituent about the component to be coated during the coating cycle.
摘要:
A coated article and method for producing the coated article are described. The article is provided with a coating system which provides protection against hot corrosion at moderate temperatures (1200.degree.-1700.degree. F.). An overlay coating based on a metal selected from the group consisting of iron, nickel or cobalt or mixtures thereof and containing chromium and optionally aluminum, yttrium and/or hafnium is applied to the article to be protected. A silicon rich surface zone is produced at the surface of the overlay coating. Methods including pack cementation and physical vapor deposition are described for producing the coating.
摘要:
The process of making an ingot for use as a feed stock for a coating process in which the ingot is vaporized to produce the coating material; the ingot being made by forming a billet of the alloy minus the reactive element with a rod of the reactive element of the alloy extending centrally through the billet and then shaping the billet to ingot size, the cross-sectional area of the rod having the same relation of the remainder of the area of the billet as the percentage of the reactive element in the alloy.
摘要:
Concepts relating to the heat treatment of single crystal superalloy articles are disclosed. A first concept is the use of a heat treatment sequence which includes incipient melting of the article being heat treated followed by one or more steps which essentially heal the incipient melting damage. A second concept relates to the treatment of previously heat treated single crystal articles which have incipient melting. Methods are disclosed for healing this damage and for recovering the mechanical properties of such articles. A third concept disclosed is a particular cycle which permits effective heat treatment of a specific single crystal alloy composition.
摘要:
A coated article and method for producing the coated article are described. The article is coated with a system which provides protection against oxidation and corrosion and which significantly reduces the substrate temperature. An MCrAlY layer is applied to the article to be protected and a columnar grain ceramic is applied by vapor deposition to the MCrAlY coated article. An alumina layer which exists between the MCrAlY layer and the columnar ceramic layer provides for the adherence of the columnar layer to the MCrAlY layer. An important feature of the invention is that the interface between the MCrAlY layer and the alumina layer has a low surface roughness and this greatly improves the columnar ceramic layer adherence.
摘要:
A coated article and method for producing the coated article are described. The article is provided with a coating system which provides protection against hot corrosion at moderate temperatures (1200-1700.degree. F.). An overlay coating based on a metal selected from the group consisting of iron, nickel or cobalt or mixtures thereof and containing chromium and optionally aluminum, yttrium and/or hafnium is applied to the article to be protected. A silicon rich surface zone is produced at the surface of the overlay coating. Methods including pack cementation and physical vapor deposition are described for producing the coating.
摘要:
A coated article and method for producing the coated article are described. The article is coated with a system which provides protection against oxidation and corrosion and which significantly reduces the substrate temperature. An MCrAlY layer is applied to the article to be protected and a columnar grain ceramic is applied by vapor deposition to the MCrAlY coated article. An alumina lyaer which exists between the MCrAlY layer and the columnar ceramic layer provides for the adherence of the columnar layer to the MCrAlY layer. An important feature of the invention is that the interface between the MCrAlY layer and the alumina layer has a low surface roughness and this greatly improves the columnar ceramic layer adherence.
摘要:
A spallation resistant metallic article comprising a metallic substrate, at least one ceramic thermal barrier coating comprising a zirconia base and at least one other element selected from the group consisting of La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Sc, In, Y, Mo and C, rare earth oxides, scandium, and indium, and a ceramic bond coat located on at least a portion of the substrate and between the metallic substrate and the at least one ceramic thermal barrier coating wherein the ceramic bond coat is composed of yttria stabilized zirconia (YSZ).
摘要:
A turbine component has a substrate formed from a ceramic material selected from the group consisting of a monolithic ceramic material and a composite ceramic material and a thermal barrier coating bonded to the substrate. In one embodiment, the ceramic material forming the substrate is selected from the group of silicon nitride and self-reinforced silicon nitride. In another embodiment, the ceramic material forming the substrate is selected from the group consisting of a silicon carbide-silicon carbide material and a carbon-carbon material. At least one bond coat layer may be interposed between the substrate and the thermal barrier coating.