摘要:
This invention relates to aliphatic polycarbonates including sequential copolymers based on cyclic aliphatic carbonates and esters and block copolymers of blocks of polymerised cyclic aliphatic carbonates and blocks of polymerised vinyl compounds stabilized against thermal degradation containing 0.01 to 3.0% by weight, based on polymer, of a compound of trivalent phosphorus.
摘要:
Thermoplastic block copolymers of the idealized formulae (I)A--B--A; B--A--B or (A--B).sub.x (I)in whichx=1 to 40,and whereinA is the radical of a homopolymer of styrene, vinylnaphthalene, butadiene and isoprene, andB the radical of a homopolymer of a cyclic polycarbonate or lactone,the average molecular weight of blocks A and B being greater than 800, and a process for the preparation of these blocks copolymers in several reaction stages.
摘要:
Process for the polymerization of cyclic aliphatic carbonates in the presence of aprotic organic solvents with exclusion of atmospheric oxygen and atmospheric moisture, wherein organometallic compounds of elements of main group 1 of the periodic table are used as initiators, the monomer/solvent ratio is in the range from 1 part by weight to 50 parts by weight of monomer per 100 parts by weight of solvent and the polymerization temperature is between -100.degree. C. and +20.degree. C.
摘要:
Trialkylsilyloxy-1,1-diphenyl ethylenes corresponding to general formula I, new polymers produced therewith terminated by aryl trialkylsilyl ether groups or by phenolic hydroxyl groups and a process for the production of these polymers by anionic polymerization ##STR1## in which R.sup.1, R.sup.2 .dbd.H, C.sub.1 -C.sub.4 alkyl, OCH.sub.3,R.sup.3 .dbd.H, C.sub.1 -C.sub.4 alkyl, O--C.sub.1 -C.sub.4 alkyl,R.sup.4 .dbd.H, C.sub.1 -C.sub.4 alkyl,R.sup.5 .dbd.C.sub.1 -C.sub.4 alkyl,R.sup.6 .dbd.H, C.sub.1 -C.sub.4 alkyl.
摘要:
Copolymers of blocks of polymers of cyclic aliphatic carbonates, cyclic aliphatic esters or cyclic aliphatic carbonates and cyclic aliphatic esters on the one hand and blocks of polymers of cyclic aromatic carbonates on the other hand and a process for their production by multistage polymerization, in which a block polymer is initially prepared from the aliphatic monomer and the aromatic polymer is produced in the presence of this block.
摘要:
Trialkylsilyloxy-1,1-diphenyl ethylenes corresponding to general formula I, new polymers produced therewith terminated by aryl trialkylsilyl ether groups or by phenolic hydroxyl groups and a process for the production of these polymers by anionic polymerization ##STR1## in which R.sup.1, R.sup.2 =H, C.sub.1 -C.sub.4 alkyl, OCH.sub.3,R.sup.3 =H, C.sub.1 -C.sub.4 alkyl, O--C.sub.1 -C.sub.4 alkyl,R.sup.4 =H, C.sub.1 -C.sub.4 alkyl,R.sup.5 =C.sub.1 -C.sub.4 alkyl,R.sup.6 =H, C.sub.1 -C.sub.4 alkyl.
摘要:
Thermoplastic moulding compositions composed ofI) 99.8-95% by weight of(A) 0-100% by weight of one or more graft polymers comprise the monomers styrene, .alpha.-methyl styrene, methyl methacrylate or a mixture of 95-50% by weight of styrene, .alpha.-methyl styrene, ring substituted styrene, methyl methacrylate or mixtures thereof with 5-50% by weight of methacrylonitrile, acrylonitrile, maleric acid anhydride, N-substituted malerimides or mixtures thereof, grafted onto a rubber substrate, andB) 100 to 0%, by weight of one or more thermoplastic vinyl polymers, andII) 0.2 to 5% by weight of a polyalkylene ether modified by a radical former which can be compounds conventionally used as an initiator for radical polymerization such as peroxides.
摘要:
Thermoplastic moulding compounds composed of99.8-95% by weight of A) 0-100% by weight of a graft polymer B) 100-0% by weight of a thermoplastic polymer of vinyl monomers and0.2 to 5% by weight of a polyalkylene ether which has been grafted with a polymer of C.sub.1 -C.sub.6 alkyl acrylates, cycloalkyl acrylates or methacrylates and optionally styrene or .alpha.-methyl styrene.
摘要:
Thermoplastic molding compositions containingA) ABS-type resin,B) aromatic polycarbonate resins,C) a compound bearing several carboxyl groups or mixtures thereof and optionallyD) further polymer resins,characterized in that an ABS resin with at least one basically acting additive is used as component A, component C is selected from compounds having a molecular weight of from 150 to 260 having at least two carboxyl groups (--COOH) in the molecule, and the weight ratio of basically acting additive in A: carboxyl groups in C is from 5:1 to 1:1.
摘要:
Polymers having a sequential structure of the following formula--A--X--B].sub.r (I)with r=1 to 20, in which --A-- is a polymer of a cyclic carbonate, --B-- is a polymer of a lactone and --X-- is a link, with a decreasing concentration of residues of the cyclic carbonate in the --B-- direction and a decreasing concentration of residues of the lactone in the --A-- direction, and the use of the these products as molding compositions.