摘要:
Bulk single crystal of aluminum nitride (AlN) having an areal planar defect density≦100 cm−2. Methods for growing single crystal aluminum nitride include melting an aluminum foil to uniformly wet a foundation with a layer of aluminum, the foundation forming a portion of an AlN seed holder, for an AlN seed to be used for the AlN growth. The holder may consist essentially of a substantially impervious backing plate.
摘要:
Reducing the microvoid (MV) density in AlN ameliorates numerous problems related to cracking during crystal growth, etch pit generation during the polishing, reduction of the optical transparency in an AlN wafer, and, possibly, growth pit formation during epitaxial growth of AlN and/or AlGaN. This facilitates practical crystal production strategies and the formation of large, bulk AlN crystals with low defect densities—e.g., a dislocation density below 104 cm−2 and an inclusion density below 104 cm−3 and/or a MV density below 104 cm−3.
摘要:
Bulk single crystal of aluminum nitride (AlN) having an areal planar defect density ≦100 cm−2. Methods for growing single crystal aluminum nitride include melting an aluminum foil to uniformly wet a foundation with a layer of aluminum, the foundation forming a portion of an AlN seed holder, for an AlN seed to be used for the AlN growth. The holder may consist essentially of a substantially impervious backing plate.
摘要:
In various embodiments, methods of forming single-crystal AlN include providing a substantially undoped polycrystalline AlN ceramic having an oxygen concentration less than approximately 100 ppm, forming a single-crystal bulk AlN crystal by a sublimation-recondensation process at a temperature greater than approximately 2000° C., and cooling the bulk AlN crystal to a first temperature between approximately 1500° C. and approximately 1800° C. at a first rate less than approximately 250° C./hour.
摘要:
Semiconductor structures and devices based thereon include an aluminum nitride single-crystal substrate and at least one layer epitaxially grown thereover. The epitaxial layer may comprise at least one of AlN, GaN, InN, or any binary or tertiary alloy combination thereof, and have an average dislocation density within the semiconductor heterostructure is less than about 106 cm−2.
摘要:
Bulk single crystal of aluminum nitride (AlN) having an areal planar defect density ≤100 cm=2, Methods for growing single crystal aluminum nitride include melting an aluminum foil to uniformly wet a foundation with a layer of aluminum, the foundation forming a portion of an AlN seed holder, for an AlN seed to be used for the AlN growth. The holder may consist essentially of a substantially impervious backing plate.
摘要:
Semiconductor structures and devices based thereon include an aluminum nitride single-crystal substrate and at least one layer epitaxially grown thereover. The epitaxial layer may comprise at least one of AlN, GaN, InN, or any binary or tertiary alloy combination thereof, and have an average dislocation density within the semiconductor heterostructure is less than about 106 cm−2.
摘要:
Bulk single crystal of aluminum nitride (AlN) having an a real planar defect density≦100 cm−2 Methods for growing single crystal aluminum nitride include melting an aluminum foil to uniformly wet a foundation with a layer of aluminum, the foundation forming a portion of an AlN seed holder, for an AlN seed to be used for the AlN growth. The holder may consist essentially of a substantially impervious backing plate.
摘要:
Bulk single crystal of aluminum nitride (AlN) having an areal planar defect density≤100 cm=2. Methods for growing single crystal aluminum nitride include melting an aluminum foil to uniformly wet a foundation with a layer of aluminum, the foundation forming a portion of an AlN seed holder, for an AlN seed to be used for the AlN growth. The holder may consist essentially of a substantially impervious backing plate.
摘要:
Bulk single crystal of aluminum nitride (AlN) having an areal planar defect density≦100 cm−2. Methods for growing single crystal aluminum nitride include melting an aluminum foil to uniformly wet a foundation with a layer of aluminum, the foundation forming a portion of an AlN seed holder, for an AlN seed to be used for the AlN growth. The holder may consist essentially of a substantially impervious backing plate.