A heat shrinkable multilayer film comprising an outer surface layer (a) formed of a thermoplastic resin, a first intermediate layer (b1) formed of a polyamide resin, a second intermediate layer (b2) formed of a saponified product of an ethylene-vinyl acetate copolymer, and an inner surface layer (c) formed of a polyolefin resin, whereinthe shrink of the heat shrinkable multilayer film in water at 90° C. is within a range of from 3 to 45% in each of machine and transverse directions, andthe polyamide resin is a mixture of 60 to 90% by weight of an aliphatic polyamide having a melting point of 210° C. or higher and 10 to 40% by weight of an aromatic polyamide comprising isophthalic acid and terephthalic acid as main components.
摘要:
The invention has for its object to provide a heat-shrinkable laminated film for deep drawing, which has an increased carbon dioxide transmission rate (CO2TR) and an enhanced ratio (CO2TR/O2TR) of carbon dioxide transmission rate-to-oxygen transmission rate (O2TR), and is less susceptible to pinholes. In the inventive heat-shrinkable laminated film for deep drawing, a polyamide resin composition layer (a) containing a polyamide resin mixture comprising 60 to 95% by mass of an aliphatic polyamide resin (A) and 5 to 40% by mass of a polyamide base resin (B) having a heat of crystalline fusion of 5 to 40 J/g is laminated onto a heat-sealing resin layer (a) containing a polyolefin resin via an adhesive resin layer (b).
摘要:
A food packaging method is provided in which food is packaged in a package with use of carbon dioxide to benefit from bacteriostatic effects and the food package contains the minimum reduced gas spaces and thereby has a volume substantially equal to the food volume. Tightly-fitting food packages are obtained by the method. A tightly-fitting food package is obtained by: placing at least one kind of foods selected from the group consisting of meats and processed meats in a plastic film package; blowing a carbon dioxide gas in the package to fill the package with the carbon dioxide gas in a volume of 10 to 45 cm3 per 100 g of the food as measured at 0° C. and 1 atm; and sealing and refrigerating the package.
摘要:
The invention has for its object to provide a heat-shrinkable laminated film for deep drawing, which has an increased carbon dioxide transmission rate (CO2TR) and an enhanced ratio (CO2TR/O2TR) of carbon dioxide transmission rate-to-oxygen transmission rate (O2TR), and is less susceptible to pinholes. In the inventive heat-shrinkable laminated film for deep drawing, a polyamide resin composition layer (a) containing a polyamide resin mixture comprising 60 to 95% by mass of an aliphatic polyamide resin (A) and 5 to 40% by mass of a polyamide base resin (B) having a heat of crystalline fusion of 5 to 40 J/g is laminated onto a heat-sealing resin layer (a) containing a polyolefin resin via an adhesive resin layer (b).
摘要:
A heat shrinkable multilayer film comprising an outer surface layer (a) formed of a thermoplastic resin, a first intermediate layer (b1) formed of a polyamide resin, a second intermediate layer (b2) formed of a saponified product of an ethylene-vinyl acetate copolymer, and an inner surface layer (c) formed of a polyolefin resin, wherein the shrink of the heat shrinkable multilayer film in water at 90° C. is within a range of from 3 to 45% in each of machine and transverse directions, and the polyamide resin is a mixture of 60 to 90% by weight of an aliphatic polyamide having a melting point of 210° C. or higher and 10 to 40% by weight of an aromatic polyamide comprising isophthalic acid and terephthalic acid as main components.
摘要:
A deep drawing packaging container comprising: a top film made of a first heat shrinkable multilayer film; and a bottom film made of a second heat shrinkable multilayer film, the deep drawing packaging container being formed by deep drawing, so that a drawing ratio (D1) of the top film and a drawing ratio (D2) of the bottom film satisfy conditions: D1=1.1 to 4.0; D2=1.5 to 5.0; and (D2/D1)=1.05 to 4.55, wherein a hot-water shrinkability (SM1) in a longitudinal direction and a hot-water shrinkability (ST1) in a transverse direction of the first heat shrinkable multilayer film and a hot-water shrinkability (SM2) in a longitudinal direction and a hot-water shrinkability (ST2) in a transverse direction of the second heat shrinkable multilayer film satisfy conditions: SM1=5 to 40%; ST1=5 to 40%; SM2=2 to 25%; ST2=2 to 25%; (SM1/SM2)=1.2 to 12; and (ST1/ST2)=1.2 to 12 (where the hot-water shrinkability is a shrinkability (%) after immersing the heat shrinkable multilayer film before drawing in hot water of 90° C. for 10 seconds).
摘要:
A deep drawing heat shrinkable multilayer film includes: an intermediate layer made of a vinylidene chloride copolymer resin (a); and a resin layer made of a first thermoplastic resin (b) layered on at least one surface of the intermediate layer. The multilayer film has hot water shrinkabilities in longitudinal and transverse directions at a temperature of 90° C. range from 3% to 35% respectively.
摘要:
A deep drawn container with a top film made of a first heat shrinkable multilayer film, and a bottom film made of a second heat shrinkable multilayer film. The deep drawn container having a drawing ratio (D1) of the top film and a drawing ratio (D2) of the bottom film satisfying conditions: D1=1.1 to 4.0; D2=1.5 to 5.0; and (D2/D1)=1.05 to 4.55. A hot-water shrinkability of the first heat shrinkable multilayer film in a longitudinal direction (SM1) and in a transverse direction (ST1), and a hot-water shrinkability of the second heat shrinkable multilayer film in a longitudinal direction (SM2) and in a transverse direction (ST2) satisfy conditions: SM1=5 to 40%; ST1=5 to 40%; SM2=2 to 25%; ST2=2 to 25%; (SM1/SM2)=1.2 to 12; and (ST1/ST2)=1.2 to 12.
摘要:
A deep drawing heat shrinkable multilayer film includes: an intermediate layer made of a vinylidene chloride copolymer resin (a); and a resin layer made of a first thermoplastic resin (b) layered on at least one surface of the intermediate layer. The multilayer film has hot water shrinkabilities in longitudinal and transverse directions at a temperature of 90° C. range from 3% to 35% respectively.
摘要:
To achieve stable, high capacity, high speed recording. Of two light beams emitted from a light irradiation means, one or two beams are made pass through an optical path changeable member whereof at least one of the thickness and refractive index changes continuously or in two or more steps immediately after emission from the light irradiation means, so that a difference is introduced into the optical path length of the two beams, and the focusing point of one beam is made to vary to coincide with a position in the recording layer used for playback or recording. Another light beam is used for servo. Converging of light during recording or read of a multilayer recording medium is performed with higher precision than in the prior art, so higher density, higher capacity recording/playback can be performed.