摘要:
A tin-plating or aluminum-plating surface treated steel material with excellent corrosion resistance containing an intermetallic compound composed of one or more Group IIa (alkaline earth metal) elements and one or more Group IVb elements in a tin-based plating layer or aluminum-based plating layer on the surface of a steel material. For a tin-based plating layer, the long diameter of the intermetallic compound massive bodies is 1 82 m or greater and the short diameter/long diameter ratio is at least 0.4. For an aluminum-based plating layer, the long diameter of the intermetallic compound massive bodies is 10 &mgr;m or greater and the short diameter/long diameter ratio is at least 0.4.
摘要:
A Sn-based metal-coated steel strip excellent in appearance comprises a Ni-based metal (such as Ni, a Ni—Sn alloy, a Ni—Zn alloy, a Ni—Fe alloy and a Ni—Co alloy) preplating layer and a Sn-based metal (such as a Sn—Zn alloy) coating formed thereon, and is characterized in that a Ni emission intensity line and an Fe emission intensity line obtained by glow discharge spectroscopy of the surface of the coated steel strip satisfy a relationship of the formula: T1≧T2 wherein T1 is a sputtering time at the peak of a Ni emission intensity line, and T2 is a sputtering time at the inflection point of an Fe emission intensity line, or a relationship of the formulas: T1≧T2, and 1≦T1/T2≦1.5
摘要翻译:外观优异的Sn系金属涂层钢带包括Ni基金属(Ni,Ni-Sn合金,Ni-Zn合金,Ni-Fe合金,Ni-Co合金)预镀层和 在其上形成的Sn基金属(例如Sn-Zn合金)涂层,其特征在于,通过镀覆钢带的表面的辉光放电光谱获得的Ni发射强度线和Fe发射强度线满足关系 其中T 1是在Ni发射强度线的峰值处的溅射时间,T 2是在Fe发射强度线的拐点处的溅射时间,或者 公式:T 1> = T 2,1 <= T 1 / T 2 <= 1.5
摘要:
A coated steel material excellent in corrosion resistance and a method of producing the same, wherein a coated steel material has on the surface of the steel sheet a Zn-alloy coating layer containing 1-10 wt % of Mg, 2-19 wt % of Al and 0.01-2 wt % of Si, where Mg and Al satisfy Mg (%)+Al (%)≦20%, the balance being Zn and unavoidable impurities, and has a coating layer structure of a Mg intermetallic compound or the like. As a base metal treatment, it is preferably provided with a Ni coating layer. The coated Zn-alloy coated steel sheet may have provided on the coating layer, as an intermediate layer, a chromate film layer, and, as an upper layer, an organic coating layer. The Zn-alloy coating layer may further contain one or more of 0.01-1 wt % of In, 0.01-1 wt % of Bi and 1-10 wt % of Sn. The coated steel material may be painted.
摘要:
In a plated steel sheet having an aluminum-plating layer comprising at least Al formed on one side or both sides of the steel sheet, there is provided a plated steel sheet which, owing to the presence of a surface coating layer containing a compound having wurtzite crystal structure on the aluminum-plating layer, has excellent lubricity, prevents the plating thickness from becoming uneven during heating, and can improve formability and productivity in hot stamping, and a method of hot-stamping the plated steel sheet.
摘要:
In a plated steel sheet having an aluminum-plating layer comprising at least Al formed on one side or both sides of the steel sheet, there is provided a plated steel sheet which, owing to the presence of a surface coating layer containing a compound having wurtzite crystal structure on the aluminum-plating layer, has excellent lubricity, prevents the plating thickness from becoming uneven during heating, and can improve formability and productivity in hot stamping, and a method of hot-stamping the plated steel sheet.
摘要:
In a plated steel sheet having an aluminum-plating layer comprising at least Al formed on one side or both sides of the steel sheet, there is provided a plated steel sheet which, owing to the presence of a surface coating layer containing a compound having wurtzite crystal structure on the aluminum-plating layer, has excellent lubricity, prevents the plating thickness from becoming uneven during heating, and can improve formability and productivity in hot stamping, and a method of hot-stamping the plated steel sheet.
摘要:
In a plated steel sheet having an aluminum-plating layer comprising at least Al formed on one side or both sides of the steel sheet, there is provided a plated steel sheet which, owing to the presence of a surface coating layer containing a compound having wurtzite crystal structure on the aluminum-plating layer, has excellent lubricity, prevents the plating thickness from becoming uneven during heating, and can improve formability and productivity in hot stamping, and a method of hot-stamping the plated steel sheet.
摘要:
The present invention relates to aluminum plated steel sheet which does not require coating after plating and is high in production flexibility enabling application of conventional production processes as they are or exhibits excellent corrosion resistance to flex fuels and further is excellent in appearance and to fuel tanks characterized by being produced using the steel sheet. The Si, Mg, Ca, and Ti ingredients in the aluminum plating layer are defined and the cooling method after hot dip aluminum coating is controlled to make Mg2Si particles with a long axis of 10 μm or less and an aspect ratio of 1 to 3 finely disperse in the plating layer. Due to the Mg2Si particles, it is possible to give an excellent corrosion resistance to flex fuels and suppress the deterioration in appearance due to MgO.
摘要:
The present invention relates to aluminum plated steel sheet which does not require coating after plating and is high in production flexibility enabling application of conventional production processes as they are or exhibits excellent corrosion resistance to flex fuels and further is excellent in appearance and to fuel tanks characterized by being produced using the steel sheet.The means for solving this is characterized by defining the Si, Mg, Ca, and Ti ingredients in the aluminum plating layer and controlling the cooling method after hot dip aluminum coating so as to make Mg2Si particles with a long axis of 10 μm or less and an aspect ratio of 1 to 3 finely disperse in the plating layer. Due to the Mg2Si particles, it is possible to give an excellent corrosion resistance to flex fuels and suppress the deterioration in appearance due to MgO.
摘要:
The present invention stably provides a high-strength hot-dip galvanized steel sheet having a high tensile strength and no non-plated portions and being excellent in workability and surface properties even when the employed equipment has only a reduction annealing furnace and a steel sheet containing relatively large amounts of Si, Mn and Al that are regarded as likely to cause non-plated portions is used as the substrate. The present invention: secures good plating performance even when the steel sheet contains Si, Mn and Al by adding Ni to a steel sheet, thus forming oxides at some portions in the steel sheet surface layer, and resultantly suppressing the surface incrassation of Si, Mn and Al at the portions where oxides are not formed; enhances the effect of Ni and accelerates the formation of oxides by further adding Mo, Cu and Sn; and moreover, in the case of a TRIP steel sheet, secures austenite by determining the ranges of Si and Al strictly, avoiding the deterioration of plating performance caused by the addition of Ni, and further adding Mo in a balanced manner. In addition, the present invention, in a TRIP steel sheet, improves press formability by regulating a retained austenite ratio and accelerates the formation of oxides by regulating a hydrogen concentration and a dew point in annealing before plating.