摘要:
A resin-coated metal sheet includes resin layers formed on both surfaces thereof and composed of a polyester as a main component, wherein the resin layer covering the inner surface of a container after the formation thereof has an interfacial free energy with water of 30 mN/m or more. The container formed from the resin-coated metal sheet exhibits an excellent content release property for contents with a high protein content.
摘要:
A resin-coated metal sheet includes resin layers formed on both surfaces thereof and composed of a polyester as a main component, wherein the resin layer covering the inner surface of a container after the formation thereof has an interfacial free energy with water of 30 mN/m or more. The container formed from the resin-coated metal sheet exhibits an excellent content release property for contents with a high protein content.
摘要:
A DI forming water-based coolant of a laminated metal sheet includes at least one kind of base (a) selected from alkanolamines and alkali metal hydroxides, a fatty acid (b), and water (c), wherein the total content of the base (a) and the fatty acid (b) is 0.02 to 4% by mass and the ratio of a straight-chain fatty acid having a carbon number of 6 to 12 in the fatty acid (b) is 80 to 100% by mass.
摘要:
A DI forming water-based coolant of a laminated metal sheet includes at least one kind of base (a) selected from alkanolamines and alkali metal hydroxides, a fatty acid (b), and water (c), wherein the total content of the base (a) and the fatty acid (b) is 0.02 to 4% by mass and the ratio of a straight-chain fatty acid having a carbon number of 6 to 12 in the fatty acid (b) is 80 to 100% by mass.
摘要:
A colored laminated metal plate for containers includes a metal plate having one or both surfaces coated with a film for lamination in which a colored adhesive layer is coated to a polyester resin film. The colored adhesive layer contains a polyester resin as a main component and further contains an etherified amino resin, an epoxy resin, a strong acid compound, and a coloring agent. The colored laminated steel sheet is excellent in deep drawability, adhesion after forming, rust resistance of a damaged portion, and so on. When the steel sheet is applied to manufacturing of a container such as a can, retort whitening of the laminate film hardly occurs, and the design properties of appearance can be maintained.
摘要:
The resin-coated metal sheet has: a metal sheet; a lower polyester resin layer having 0.03 or smaller plane orientation factor and 5 to 20 μm of thickness, being formed on at least one side of the metal sheet; and an upper polyester resin layer containing 0.1 to 5% by mass of olefin wax, having larger than 0.06 and not larger than 0.15 of plane orientation factor and 0.5 to 10 μm of thickness, being formed on the lower polyester resin layer. The metal sheet assures excellent taking-out performance of the contents also those of low fat and high protein foods, and provides formability and adhesion requested for the container working.
摘要:
The resin-coated metal sheet is composed of: a metal sheet; a lower resin layer containing a hydrophilic copolyester, formed on at least one side of the metal sheet; and an upper resin layer containing a polyester containing a diol component composed of a diol derivative of 1 to 10% by mole of alicyclic compound and 99 to 90% by mole of ethylene glycol, and a dicarboxylic acid component consisting of terephthalic acid, formed on the lower resin layer. The sum of cyclic trimer of alkylene terephthalate existing in the upper resin layer and the lower resin layer is 0.9% or less by mass. Since the manufacture of food cans using the resin-coated metal sheet does not induce white haze phenomenon and retort blushing phenomenon on outer surface of the can even after retorting, the decorative appearance on outer surface of the can is not deteriorated.
摘要:
A laminated steel sheet for a two-piece can body with a high strain level satisfying the following formulae, the polyester resin layer composing the laminated steel sheet having a center line surface roughness (Ra) of 0.2 μm to 1.8 μm: r1≦r, 0.1≦r1/R≦0.25, and 1.5≦h/(R−r)≦4 wherein h is the height of the two-piece can body, r is the maximum radius, r1 is the minimum radius, and R is the radius of the circular laminated steel sheet before forming having the same weight as the can body.
摘要:
A method to evaluate the corrosion resistance of a can to a content includes filling the can with the content to form a specimen, setting the specimen in an apparatus capable of blocking an outside atmosphere from entering the specimen, optionally saturating the content with nitrogen gas to expel dissolved oxygen present in the content, thereafter while maintaining the temperature of the content at a constant temperature in the range of 25 to 60° C., applying a constant potential that is more anodic than an immersion potential by 50 mV to 200 mV to the can of the specimen, and evaluating the corrosion resistance of the can to the content based on the accumulated amount of electricity generated during a time appropriately selected from 6 to 48 hours immediately after the application of the constant potential.
摘要:
A method to evaluate the corrosion resistance of a can to a content includes filling the can with the content to form a specimen, setting the specimen in an apparatus capable of blocking an outside atmosphere from entering the specimen, optionally saturating the content with nitrogen gas to expel dissolved oxygen present in the content, thereafter while maintaining the temperature of the content at a constant temperature in the range of 25 to 60° C., applying a constant potential that is more anodic than an immersion potential by 50 mV to 200 mV to the can of the specimen, and evaluating the corrosion resistance of the can to the content based on the accumulated amount of electricity generated during a time appropriately selected from 6 to 48 hours immediately after the application of the constant potential.