摘要:
A process of forming a lactide copolymer includes forming a dimethylidene lactide molecule from an L-lactide molecule. The process also includes forming a functionalized lactide monomer from the dimethylidene lactide molecule. The process includes forming a mixture that includes the functionalized lactide monomer and a bisphenol A (BPA) monomer or a BPA-derived monomer. The process further includes polymerizing the mixture to form a lactide copolymer.
摘要:
A resin composition contains (A) a polylactic acid, (B) a polyhydroxyalkanoate, (C) an ammonium polyphosphate, and (D) a phenol-modified epoxy compound. With respect to the total amount of the resin composition, the polylactic acid (A) and the polyhydroxyalkanoate (B) are contained from about 60% by mass to about 95% by mass; the ammonium polyphosphate (C) is contained from about 4% by mass to about 35% by mass; the phenol-modified epoxy compound (D) is contained from about 1% by mass to about 5% by mass; the polylactic acid (A) is contained from about 40% by mass to about 90% by mass; the polyhydroxyalkanoate (B) is contained from about 5% by mass to about 55% by mass; and the amount ratio of the polylactic acid (A) to the polyhydroxyalkanoate (B) is from about 0.7 to about 18.
摘要:
A thermosetting resin composition capable of providing a molding, such as a resin sheet, that excels in not only dielectric characteristics but also dimensional stability at high temperature and even after exposure to high temperature thermal history, exhibits little dimensional change by the thermal history, namely, exhibiting low linear expansion coefficient. There are further provided a resin sheet and resin sheet for insulated substrate produced from the thermosetting resin composition. In particular, there is provided a thermosetting resin composition comprising an epoxy resin of 100 to 2000 epoxy equivalent, an epoxy resin hardening agent consisting of a phenolated compound, and a layered silicate, and are further provided a resin sheet comprised of the thermosetting resin composition and a resin sheet for insulated substrate comprised of the resin sheet.
摘要:
Curable compositions are provided which contain a curable component and particular m-hydroxybenzene derivatives, wherein such derivatives function as aging inhibitors. Such curable compositions are useful as coating agents and adhesives having improved aging resistance.
摘要:
New polymers and new anti-reflective compositions containing such polymers are provided. The compositions comprise a polymer (e.g., epoxy cresol novolac resins) bonded with a chromophore (4-hydroxybenzoic acid, trimellitic anhydride). The inventive compositions can be applied to substrates (e.g., silicon wafers) to form anti-reflective coating layers having high etch rates which minimize or prevent reflection during subsequent photoresist exposure and developing.
摘要:
New polymers and new anti-reflective compositions containing such polymers are provided. The compositions comprise a polymer (e.g., epoxy cresol novolac resins) bonded with a chromophore (4-hydroxybenzoic acid, trimellitic anhydride). The inventive compositions can be applied to substrates (e.g., silicon wafers) to form anti-reflective coating layers having high etch rates which minimize or prevent reflection during subsequent photoresist exposure and developing.
摘要:
Coating compositions comprising an epoxy resin and a curative which is methylenedisalicylic acid and/or a methylendisalicylic acid ring-substituted homologue are found to cure at and produce a wrinkle finish at relatively low temperatures when a borontrifluoride:amine complex is used as the cure catalyst.
摘要:
A high solids coating composition comprising a branched hydroxy-functional polyester oligomer and a curing agent; and the oligomer itself containing at least 20% by weight of the binder of at least one of the following tertiary acid ester end groups: ##STR1## where R.sub.1, R.sub.2 and R.sub.3 are independently selected from CH.sub.3 and CH.sub.2 OH; the composition being suitable as an automobile clearcoat or pigmented topcoat.
摘要:
Modified epoxy resins are obtained by reaction of an epoxy resin with up to one mol equivalent per epoxy group of an alkyl or alkenyl substituted, hydroxy substituted aromatic acid, especially by reaction of a bisphenol A based epoxy resin with an alkylated salicylic acid. Also are described a process for the production of such modified resins, curable compositions comprising the modified epoxy resin and products provided with the cured composition, especially in coating applications and civil engineering applications.
摘要:
An epoxy coating powder composition and a method for controlling the denseness of cured wrinkle finish patterns are provided by the use of a curing agent mixture comprising a blocked Lewis acid, methylenedisalicylic acid and a ring-substituted homolog thereof having the formula ##STR1## wherein x and y are from 1 to 3, and R.sup.1 and R.sup.2 are, independently, hydrogen, alkyl groups having from 1 to 20 carbon atoms, aryl groups having from 6 to 10 carbon atoms, or aryl-substituted methylene groups; with the proviso that when x=y=3, R.sup.1 and R.sup.2 .noteq.hydrogen;wherein the ratio of methylene disalicylic acid and the ring-substituted homolog is from about 50:50 to about 2:98 by weight.
摘要翻译:环氧涂料粉末组合物和通过使用包含封闭的路易斯酸,亚甲基二水杨酸和其具有下式的环取代的同系物的固化剂混合物来提供固化的皱纹整理剂图案的密度的方法,其中x和y是 1至3,并且R 1和R 2独立地为氢,具有1至20个碳原子的烷基,具有6至10个碳原子的芳基或芳基取代的亚甲基; 条件是当x = y = 3时,R1和R2均为氢; 其中亚甲基二水杨酸和环取代的同系物的比例为约50:50至约2:98(重量比)。