摘要:
A method of high aspect ratio contact etching a substantially vertical contact hole in an oxide layer using a hard photoresist mask is described. The oxide layer is deposited on an underlying substrate. A plasma etching gas is formed from a carbon source gas. Dopants are mixed into the gas. The doped plasma etching gas etches a substantially vertical contact hole through the oxide layer by doping carbon chain polymers formed along the sidewalls of the contact holes during the etching process into a conductive state. The conductive state of the carbon chain polymers reduces the charge buildup along sidewalls to prevent twisting of the contact holes by bleeding off the charge and ensuring proper alignment with active area landing regions. The etching stops at the underlying substrate.
摘要:
A composition for use in semiconductor processing wherein the composition comprises water, phosphoric acid, and an organic acid; wherein the organic acid is ascorbic acid or is an organic acid having two or more carboxylic acid groups (e.g., citric acid). The water can be present in about 40 wt. % to about 85 wt. % of the composition, the phosphoric acid can be present in about 0.01 wt. % to about 10 wt. % of the composition, and the organic acid can be present in about 10 wt. % to about 60 wt. % of the composition. The composition can be used for cleaning various surfaces, such as, for example, patterned metal layers and vias by exposing the surfaces to the composition.
摘要:
A method of fabricating a MRAM structure and the resulting structure. The MRAM structure of the invention has the pinned layer recessed within a trench with the upper magnetic layer positioned over it. The method of MRAM fabrication utilizes a spacer processing technique, whereby the upper magnetic layer of the MRAM stack structure is formed between the region defined by the spacers, thereby allowing for self-alignment of the upper magnetic layer over the underlying pinned magnetic layer.
摘要:
A method of high aspect ratio contact etching a substantially vertical contact hole in an oxide layer using a hard photoresist mask is described. The oxide layer is deposited on an underlying substrate. A plasma etching gas is formed from a carbon source gas. Dopants are mixed into the gas. The doped plasma etching gas etches a substantially vertical contact hole through the oxide layer by doping carbon chain polymers formed along the sidewalls of the contact holes during the etching process into a conductive state. The conductive state of the carbon chain polymers reduces the charge buildup along sidewalls to prevent twisting of the contact holes by bleeding off the charge and ensuring proper alignment with active area landing regions. The etching stops at the underlying substrate.
摘要:
A method of high aspect ratio contact etching a substantially vertical contact hole in an oxide layer using a hard photoresist mask is described. The oxide layer is deposited on an underlying substrate. A plasma etching gas is formed from a carbon source gas. Dopants are mixed into the gas. The doped plasma etching gas etches a substantially vertical contact hole through the oxide layer by doping carbon chain polymers formed along the sidewalls of the contact holes during the etching process into a conductive state. The conductive state of the carbon chain polymers reduces the charge buildup along sidewalls to prevent twisting of the contact holes by bleeding off the charge and ensuring proper alignment with active area landing regions. The etching stops at the underlying substrate.
摘要:
In damascene process integration, a reducing plasma is applied after the etch stop or barrier layer is opened over a copper layer. Currently known methods for opening barrier layers suffer from the disadvantage that they cause at least some of the underlying copper to oxidize to copper oxide. Because copper oxide is selectively removed by subsequent wet cleaning, voids can form where damaged copper (e.g., copper oxide) is removed, thus compromising the reliability of metal-to-metal contact in vias. The present invention advantageously overcomes this and other disadvantages of the prior art through the use of a hydrogen plasma following the barrier layer opening step, which repairs damaged copper (e.g., reduces copper oxide to copper), thus preventing and/or diminishing defects in metal-to-metal contacts in vias and concomitantly improving the reliability of the same.
摘要:
The invention encompasses a method of enhancing selectivity of etching silicon dioxide relative to one or more organic substances. A material comprising one or more elements selected from Group VIII of the periodic table is provided within a reaction chamber; and a substrate is provided within the reaction chamber. The substrate has both a silicon-oxide-containing composition and at least one organic substance thereover. The silicon-oxide-containing composition is plasma etched within the reaction chamber. The plasma etching of the silicon-oxide-containing composition has increased selectivity for the silicon oxide of the composition relative to the at least one organic substance than would plasma etching conducted without the material in the chamber. The invention also encompasses a plasma reaction chamber assembly. The assembly comprises at least one interior wall, and at least one liner along the at least one interior wall. The liner comprises one or more of Ru, Fe, Co, Ni, Rh, Pd, Os, W, Ir, Pt and Ti.
摘要:
The invention encompasses a method of enhancing selectivity of etching silicon dioxide relative to one or more organic substances. A material comprising one or more elements selected from Group VIII of the periodic table is provided within a reaction chamber; and a substrate is provided within the reaction chamber. The substrate has both a silicon-oxide-containing composition and at least one organic substance thereover. The silicon-oxide-containing composition is plasma etched within the reaction chamber. The plasma etching of the silicon-oxide-containing composition has increased selectivity for the silicon oxide of the composition relative to the at least one organic substance than would plasma etching conducted without the material in the chamber. The invention also encompasses a plasma reaction chamber assembly. The assembly comprises at least one interior wall, and at least one liner along the at least one interior wall. The liner comprises one or more of Ru, Fe, Co, Ni, Rh, Pd, Os, W, Ir, Pt and Ti.
摘要:
A method for forming a gate stack having a silicide layer that can subsequently undergo a SAC etch is disclosed. The present method provides a layer of insulating material on top of the silicide layer. The insulating material is sufficient to protect the gate stack, including the silicide layer when the low-resistance gate stack is used in subsequent self-aligned contact etch processes.
摘要:
Embodiments of the present disclosure are directed towards use of an etch process post wordline definition to improve data retention in a flash memory device. In one embodiment, a method includes forming a plurality of wordline structures on a substrate, wherein individual wordline structures of the plurality of wordline structures include a control gate having an electrically conductive material and a cap having an electrically insulative material formed on the control gate, depositing an electrically insulative material to form a liner on a surface of the individual wordline structures, and etching the liner to remove at least a portion of the liner. Other embodiments may be described and/or claimed.