摘要:
Melt-processable polyurethanes containing certain waxes are produced. These polyurethanes are useful for the production of films, coatings and injection moldings.
摘要:
A process for the continuous production of a thermoplastic molding composition containing a mixture of a TPU and a thermoplastic (co)polymer is disclosed. The process comprises (i) introducing into an extruder via a first feed point component I) with at least 3% by weight, with respect to component I), of at least one member selected from the group consisting of components A), B) and C), and(ii) metering in the balance of said A), B) and C) into said extruder via one or more subsequent feed points, (iii) extruding components I) and II) under conditions sufficient to cause A), B) and C) reaction to form TPU, and (iv) upon the completion of said reaction, removing the resulting mixture of TPU and (co)polymer from the extruder, wherein component I) comprises 1 to 60% by weight, with respect to the total mixture, of a thermoplastic (co)polymer, and wherein component II) comprises 99 to 40% by weight, with respect to the total mixture, of the polyurethane-forming components including A) an organic diisocyanate, B) a linear polyol having terminal hydroxyl groups and a number average molecular weight of 500 to 5000, and C) a chain extender having a molecular weight of 60 to 500, and wherein the molar ratio of NCO groups in A) to the groups which react with NCO in B) and C) is in the range of 0.9 to 1.2.
摘要:
A process for the continuous production of a thermoplastic molding composition containing a mixture of a TPU and a thermoplastic (co)polymer is disclosed. The process comprises(i) introducing into an extruder via a first feed point component I) with at least 3% by weight, with respect to component I), of at least one member selected from the group consisting of components A), B) and C), and(ii) metering in the balance of said A), B) and C) into said extruder via one or more subsequent feed points,(iii) extruding components I) and II) under conditions sufficient to cause A), B) and C) reaction to form TPU, and(iv) upon the completion of said reaction, removing the resulting mixture of TPU and (co)polymer from the extruder,wherein component I) comprises 1 to 60% by weight, with respect to the total mixture, of a thermoplastic (co)polymer, and wherein component II) comprises 99 to 40% by weight, with respect to the total mixture, of the polyurethane-forming components including A) an organic diisocyanate, B) a linear polyol having terminal hydroxyl groups and a number average molecular weight of 500 to 5000, and C) a chain extender having a molecular weight of 60 to 500, and wherein the molar ratio of NCO groups in A) to the groups which react with NCO in B) and C) is in the range of 0.9 to 1.2.
摘要:
A thermoplastic molding composition comprising a thermoplastic polyurethane and a wax mixture is disclosed. The polyurethane is a product of an organic diisocyanate, a linear, hydroxyl-terminated polyol and a diol or diamine chain extender. The wax mixture contains a first mixture of an ester of a C.sub.10-45 aliphatic carboxylic acid and a diol, and an alkali metal or alkaline earth metal salt of a C.sub.10-45 aliphatic carboxylic acids, and at least one member selected from the group consisting of fatty acid ester, fatty acid amide, fatty acid ester amide and polyethylene wax.
摘要:
A thermoplastsic molding composition comprising thermoplastic polyurethane resin and about 0.05 to 2 percent of a wax is disclosed. The composition which offers processing advantages, including release and cosmetic properties, is characterized in that the wax contains acylation products of hydroxy groups and of amino groups of amino alcohols.
摘要:
A process for the continuous production of a thermoplastic molding composition containing a mixture of TPU and a (co)polymer is disclosed. The process comprises (a) introducing into an extruder under time and temperature conditions sufficient to bring about the formation of thermoplastic polyurethane a (co)polymer, and polyurethane-forming components comprising A) an organic diisocyanate, B) a linear polyol having terminal hydroxyl groups and a molecular weight of 500 to 5000, and C) a chain extender having a molecular weight of 60 to 500, and upon completing the formation of said polyurethane (b) discharging the resulting TPU/(co)polymer mixture from the extruder. Importantly, the (co)polymer contains a flow enhancer and the molar ratio of the NCO groups in A) to the groups which react with NCO in B) and C) is 0.9 to 1.2.
摘要:
The present invention relates to a process for the preparation of self-extinguishing thermoplastic polyurethanes which optionally contain conventional additives and/or auxiliary substance.
摘要:
The present invention relates to a process for the preparation of self-extinguishing thermoplastic polyurethanes which optionally contain conventional additives and/or auxiliary substance.
摘要:
Thermoplastic polyurethanes which are readily released from a mold, have a hardness of up to 80 Shore A, and a low degree of cold hardening are produced from polyester polyols made with at least one dihydric alcohol having no ether groups and an average of at least 0.40 side carbon chains per ester group in the polyester polyol.
摘要:
The present invention relates to a multi-stage process for the continuous preparation of thermoplastically processable polyurethanes with improved processing properties based on various polyols