摘要:
A sheet of ultraviolet-cutoff glass includes a primer layer, an ultraviolet-cutoff layer, and a water-repellent layer which are successively deposited on a glass sheet. The water-repellent layer is formed of a vitreous water repellent. Since the water-repellent layer doubles as an overcoat layer, it makes it unnecessary to form a overcoat layer in a separate overcoating process.
摘要:
A water-resistant film is formed on a transparent panel such as an automobile window glass panel by applying a coating solution to a surface of a to be coated of the transparent panel, applying a solvent to a surface of a region not to be coated of the transparent panel in partly overlapping relation to the coating solution applied to the region to be coated, drying the applied coating solution and solvent, and thereafter baking the coating solution into a water-resistant film.
摘要:
A hydrolyzate resulting from co-hydrolysis of a perfluoroalkyl group-containing organic silicon compound and a hydrolyzable group-containing methylpolysiloxane compound in a hydrophilic solvent is blended with an organopolysiloxane and a strong acid to constitute a water repellent composition which is effective for imparting water repellency and facilitating falling of water droplets and thus imparting excellent water repellency and stain-proofness to a surface of an article treated therewith.
摘要:
Coating liquid prepared by dissolving an acid and a silicon alkoxide into alcohol, containing at least one of either a silicon alkoxide or a hydrolyzate thereof (including a partial hydrolyzate) in an amount of 0.010 to 3% by weight (in terms of silica), an acid in terms of 0.0010 to 1.0 normality, and water in terms of 0 to 10% by weight is coated on a substrate to produce an article coated with a silica-based film. By this method for producing a silica-based film coated article, an excellent silica-based film coated article can be obtained without requiring baking and pretreatment. Furthermore, a functional film coated article excellent in durability can be produced in a short period of time and safely by using the abovementioned silica-based film as a primer film and applying thereon an organosilane having a hydrolyzable group and a functional group having a specific function or a hydrolyzate thereof.
摘要:
A method for partially treating a water-repellent glass sheet is disclosed which comprises irradiating part of a water-repellent glass film, formed on the water-repellent glass sheet, with a stream of plasma jets generated by a plasma jet irradiating gun. By such plasma jet irradiation, the film part can be removed easily even when the glass sheet has a curved surface.
摘要:
A method for partially treating a water-repellent glass sheet is disclosed which comprises irradiating part of a water-repellent glass film, formed on the water-repellent glass sheet, with a stream of plasma jets generated by a plasma jet irradiating gun. By such plasma jet irradiation, the film part can be removed easily even when the glass sheet has a curved surface. A water-repellent glass sheet with the film part removed is also disclosed.
摘要:
A glass article provided with an organic functional film on a surface thereof of the present invention is characterized in that a coating film removable with a solvent is formed on at least a portion of the functional film. A method for handling a glass article with a handing tool of the present invention is characterized in the a glass article is handled with a handling tool via a coating film removable with a solvent between a surface of the tool in contact with the glass article and a surface of the glass article.
摘要:
For obtaining a substrate on the surface of which a water repellent film is firmly bonded through an undercoating film, and which shows a low critical inclination angle, superior durability, and high density, a water repellent and/or oil repellent film layer is formed by using a liquid for undercoating treatment. The liquid for undercoating treatment is obtained by dissolving and reacting a material having chlorosilyl radicle radicle in molecular form therein and is dissolved into an alcohol group solvent, so that a surface roughness (Ra) of less than 0.5 nm is obtained, thereby achieving high durability and a low critical inclination angle.
摘要:
This invention provides a water repellant glass plate for vehicles or buildings, which shows a long-term durability. The water repellant glass plate includes a primer layer on a glass substrate, consisting essentially of silicon oxide in which oxygen atoms are partially substituted by hydroxyl groups, at a thickness between 10 nm and 100 nm, and a second layer on the first layer consisting of an organic silicon compound including a fluoroalkyl group at a thickness between about 0.2 nm and about 40 nm.
摘要:
Heat-screening glass comprising a transparent glass substrate having consecutively thereon a heat-screening film, a first transparent protective film, and a second transparent protective film, the first transparent protective film comprising at least one member selected from the group consisting of silicon nitride, silicon dioxide, stannic oxide, oxynitride of silicon carbide, and oxynitride of tantalum carbide, and the second transparent protective film comprising at least one member selected from the group consisting of zirconium oxide, tantalum pentoxide, niobium oxide, zirconium oxynitride, tantalum oxynitride, and niobium oxynitride, and having a thickness of from 2 to 15 nm.