摘要:
The present invention describes a Fischer-Tropsch process for synthesis of hydrocarbons comprising contacting a charge comprising synthesis gas under Fischer-Tropsch synthesis operating conditions with at least one catalyst containing an active phase comprising at least one metal of group VIIIB selected from cobalt, nickel, ruthenium and iron deposited on an oxides support comprising alumina, silica and phosphorus, said oxides support not containing any spinel phase. The catalyst has an improved hydrothermal and mechanical resistance in a Fischer-Tropsch process while improving its catalytic performances.
摘要:
The present invention describes a catalyst containing an active phase comprising at least one metal of group VIIIB selected from cobalt, nickel, ruthenium and iron deposited on an oxides support comprising alumina, silica, a spinel and phosphorus. It also concerns the process for preparation of said catalyst and its use in a Fischer-Tropsch process. The catalyst has an improved hydrothermal and mechanical resistance in a Fischer-Tropsch process while improving its catalytic performances.
摘要:
The invention concerns a catalyst containing an active cobalt phase deposited on a support comprising alumina, silica or silica-alumina, said support containing a mixed oxide phase containing cobalt and/or nickel, said catalyst being prepared by introducing at least one dicarboxylic acid comprising at least three carbon atoms. The invention also concerns its use in the field of Fischer-Tropsch synthesis processes.
摘要:
Preparation of a catalyst that comprises an active phase of at least one metal of group VIM that is deposited on an oxide substrate, a) An oxide substrate that comprises alumina, silica, or a silica-alumina is provided; b) The oxide substrate of step a) is impregnated by an aqueous or organic solution that comprises at least one metal salt of group VIM that is selected from among cobalt, nickel, ruthenium, and iron, and then the product that is obtained is dried at a temperature of between 60 and 200° C.; A treatment under water vapor of the solid that is obtained in step b) is carried out at a temperature of between 110 and 195° C. for a length of time of between 30 minutes and 4 hours, in the presence of an air/vapor mixture that comprises between 2 and 50% by volume of water in vapor form.
摘要:
A catalyst containing an active phase comprising at least one metal of group VIIIB selected from cobalt, nickel, ruthenium and iron deposited on a support containing silica, alumina and at least one simple spinel MAl2O4 or mixed spinel MxM′(1−x)Al2O4) which is or is not partial, wherein M and M′ are separate metals selected from the group formed by magnesium, copper, cobalt, nickel, tin, zinc, lithium, calcium, caesium, sodium, potassium, iron and manganese, and wherein x is between 0 and 1, the values 0 and 1 being themselves excluded, characterised in that said active phase further comprises boron, the boron content being between 0.001% and 0.5% by weight with respect to the total weight of the catalyst, the value 0.5 being itself excluded.
摘要:
The invention concerns a catalyst containing an active cobalt phase deposited on a support comprising alumina, silica or silica-alumina, said support containing a mixed oxide phase containing cobalt and/or nickel, said catalyst being prepared by introducing at least one organic compound comprising at least one ester function. The invention also concerns its use in the field of Fischer-Tropsch synthesis processes.
摘要:
Process for preparing a catalyst or a trapping mass comprising the following steps: bringing a porous oxide support into contact with a metal salt comprising at least one metal belonging to groups VIB, VIIB, VIIIB, IB or IIB, of which the melting point of said metal salt is between 20° C. and 150° C., for a period of between 5 minutes and 5 hours in order to form a solid mixture, the weight ratio of said metal salt to said porous oxide support being between 0.1 and 1; heating the solid mixture with stirring at a temperature between the melting point of said metal salt and 200° C. and for 5 minutes to 12 hours; calcining the solid obtained in the preceding step at a temperature above 200° C. and below or equal to 1100° C. under an inert atmosphere or under an oxygen-containing atmosphere.
摘要:
The invention relates to a catalyst containing an active cobalt phase, deposited on a support comprising alumina, silica or silica-alumina, said support also containing a mixed oxide phase containing cobalt and/or nickel, said catalyst having been prepared by introducing at least one hydrocarbon organic compound of formula CxHy. The invention also relates to the use thereof in the field of Fischer-Tropsch synthesis processes.