摘要:
Conjugate fibers are prepared in which at least one segment is a mixture of a high-D PLA resin and a high-L PLA resin. These segments have crystallites having a crystalline melting temperature of at least 200° C. At least one other segment is a high-D PLA resin or a high-L PLA resin. The conjugate fibers may be, for example, bicomponent, multi-component, islands-in-the-sea or sheath-and-core types. Specialty fibers of various types can be made through further downstream processing of these conjugate fibers.
摘要:
Conjugate fibers are prepared in which at least one segment is a mixture of a high-D PLA resin and a high-L PLA resin. These segments have crystallites having a crystalline melting temperature of at least 200° C. At least one other segment is a high-D PLA resin or a high-L PLA resin. The conjugate fibers may be, for example, bicomponent, multi-component, islands-in-the-sea or sheath-and-core types. Specialty fibers of various types can be made through further downstream processing of these conjugate fibers.
摘要:
PLA stereocomplex fibers are made by separately melting a high-D PLA starting resin and a high-L starting resin, mixing the melts and spinning the molten mixture. Subsequent heat treatment introduces high-melting “stereocomplex” crystallinity into the fibers. The process can form fibers having a high content of “stereocomplex” crystallites that have a high melting temperature. As a result, the fibers have excellent thermal resistance. The process is also easily adaptable to commercial melt spinning operations.
摘要:
PLA stereocomplex fibers are made by separately melting a high-D PLA starting resin and a high-L starting resin, mixing the melts and spinning the molten mixture. Subsequent heat treatment introduces high-melting “stereocomplex” crystallinity into the fibers. The process can form fibers having a high content of “stereocomplex” crystallites that have a high melting temperature. As a result, the fibers have excellent thermal resistance. The process is also easily adaptable to commercial melt spinning operations.
摘要:
A nonwoven fabric comprised of a lactide polymer. The lactide polymer comprises a plurality of poly(lactide) polymer chains, residual lactide in concentration of less than about 2 percent and water in concentration of less than about 2000 parts-per-million. A process for manufacturing a nonwoven fabric with the lactide polymer composition is also disclosed.
摘要:
A lactide polymer coating resulting in a strong, repulpable, high gloss, paper coating. The lactide polymer comprises a plurality of poly(lactide) polymer chains, residual lactide in concentration of less than about 5 percent and water in concentration of less than about 2000 parts-per-million. A process for coating paper with the lactide polymer composition is also disclosed.
摘要:
An amorphous film comprised of a lactide polymer. The lactide polymer comprises a plurality of poly(lactide) polymer chains, residual lactide in concentration of less than about 2 percent and water in concentration of less than about 2000 parts-per-million. A process for manufacturing an amorphous film with the lactide polymer composition is also disclosed.
摘要:
A semi-crystalline film comprised of a lactide polymer. The lactide polymer comprises a plurality of poly(lactide) polymer chains, residual lactide in concentration of less than about 5 percent and water in concentration of less than about 2000 parts-per-million. A process for manufacturing a semi-crystalline film with the lactide polymer composition is also disclosed.
摘要:
A compostable multilayer film includes a core layer having a first surface and a second surface, a first blocking reducing layer covering the first surface of the core layer, and a second blocking reducing core layer comprises a lactic acid residue-containing polymer having a glass transition temperature (Tg) below 20.degree. C. The first and second blocking reducing layers comprise a semicrystalline aliphatic polyester. The hydrolyzable polymer and have a T.sub.g above about 50.degree. C. The multilayer structure can be used for preparing bags and wrappers.
摘要:
A semi-crystalline film comprised of a lactide polymer. The lactide polymer comprises a plurality of poly(lactide) polymer chains, residual lactide in concentration of less than about 5 percent and water in concentration of less than about 2000 parts-per-million. A process for manufacturing a semi-crystalline film with the lactide polymer composition is also disclosed.