摘要:
A cured adhesive composition comprising: (a) a copolymer comprising the reaction product of: 65 to 94.5 wt % of a C?8#191 acrylate ester, 0.5 to 5 wt % of a polar cross-linkable monomer, and 5-30 wt % of a non polar monomer, wherein the copolymer has a weight average molecular weight of 400,000 to 2,200,000 grains/mole; (b) 30 to 70 parts of a hydrogenated hydrocarbon tackifier per 100 parts of the copolymer; and (c) 0.01 to 3 parts (solid/solid) of a cross-linking agent per 100 parts of the copolymer wherein the cured adhesive has a peel value greater than 6 N/cm when tested according to FINAT test method No. 2 on a low density polyethylene; and further wherein the cured adhesive has a shear value greater than 2000 minutes when tested according to FINAT test method No. 8 on low density polyethylene. The cured adhesive of this disclosure is found to exhibit excellent adhesion to low surface energy substrates.
摘要翻译:一种固化的粘合剂组合物,其包含:(a)共聚物,其包含反应产物:65至94.5重量%的C 8#191丙烯酸酯,0.5至5重量%的极性可交联单体和5-30重量% %的非极性单体,其中共聚物的重均分子量为400,000至2,200,000个谷物/摩尔; (b)每100份共聚物30〜70份氢化烃增粘剂; 和(c)每100份共聚物中0.01〜3份(固体/固体)交联剂,其中当根据FINAT试验方法2测试时,固化的粘合剂的剥离值大于6N / cm 低密度聚乙烯; 此外,当根据FINAT试验方法8在低密度聚乙烯上测试时,固化的粘合剂的剪切值大于2000分钟。 发现本公开的固化的粘合剂对低表面能基底表现出优异的粘合性。
摘要:
A method for aqueous bead-type suspension polymerization of (meth)acrylic monomers to prepare non-agglomerating, storage stable (meth)acrylic polymer beads which are extrudable at low temperatures. The invention also relates to the polymer beads and to their use as adhesive, in particular as a pressure sensitive adhesive. The invention also discloses adhesive compositions comprising the polymer beads.
摘要:
Pressure sensitive adhesives containing a cyclic phosphonate ester are described. Methods of preparing such adhesives and articles comprising such adhesives are also described.
摘要:
Fluorinated polymeric microparticles, processes for preparing them and uses thereof as additives for fluid loss control of drilling fluids and methods of fluid loss control of drilling fluid loss with fluorinated microparticles and uses of fluoropolymers as fluid loss control agents. Said fluorinated polymeric microparticles comprise one or more repeating units derived from one or more fluorinated monomers and one or more repeating units derived from one or more acrylate monomers.
摘要:
Sterilization indicator tapes utilizing moisture-resistant, water-dispersible, pressure sensitive adhesives are provided. The indicator tapes comprise a non-water-dispersible backing having a sterilization indicator thereon, which is coated on at least one side with the moisture-resistant, water-dispersible, pressure sensitive adhesive. The indicator tapes are useful to maintain a sterilization wrapper containing articles to be sterilized in a closed position during sterilization, and normal pre- and post-sterilization handling, while also providing a means to indicate if the wrapped articles have passed through a sterilization cycle. After use, the adhesives coating the indicator tapes disperse in aqueous alkali solutions, such as are found in commercial laundries, while the backing remains intact. Methods of making and using the indicator tapes are also provided.
摘要:
Sterilization indicator tapes utilizing moisture-resistant, water-dispersible, pressure sensitive adhesives are provided. The indicator tapes comprise a non-water-dispersible backing having a sterilization indicator thereon, which is coated on at least one side with the moisture-resistant, water-dispersible, pressure sensitive adhesive. The indicator tapes are useful to maintain a sterilization wrapper containing articles to be sterilized in a closed position during sterilization, and normal pre- and post-sterilization handling, while also providing a means to indicate if the wrapped articles have passed through a sterilization cycle. After use, the adhesives coating the indicator tapes disperse in aqueous alkali solutions, such as are found in commercial laundries, while the backing remains intact. Methods of making and using the indicator tapes are also provided.
摘要:
A pressure sensitive adhesive composition is described which is water-dispersible under acidic conditions. The composition comprises a terpolymer of a hydrophobic monomeric acrylic or methacrylic ester of a non-tertiary alcohol (monomer A); a polar monomer copolymerizable with said A monomer and having carboxylic, sulfonic acid or hydroxyl functionality or combinations thereof (monomer B); and a water soluble or water-dispersible macromolecular monomer of the formula X--Y--Z which is copolymerizable with A and B wherein X is a copolymerizable moiety containing a double bond, Y is a divalent linking group and Z is a water-dispersible polymeric moiety (monomer C). The combined acid groups employed in the B monomer are neutralized from 5 to 100% based on the total amount of acid groups in B. The composition further comprises tackifier and/or plasticizers at a level such that the ratio of terpolymer to additives falls within a range of from 0.2:1 to 5:1. The pressure sensitive adhesive composition is dispersible under a variety of pH conditions. Also described are tapes comprising the repulpable composition of the invention and their use in papermaking industry.
摘要:
Hot-melt processable adhesive, such as pressure-sensitive-adhesive (PSA) or heat-activatable adhesive, compositions of the present invention possess a broad formulation latitude and adequate cohesive strength after application for use in high performance applications. Hot-melt processable adhesives of the invention comprise at least one block copolymer comprising at least two A blocks and at least one B block. The A and B blocks are derived from monoethylenically unsaturated monomers, which monomers result in saturated polymer backbones without the need for subsequent hydrogenation upon their polymerization. Preferably, the block copolymer is a (meth)acrylate block copolymer.
摘要:
A method of using a pressure sensitive adhesive to form a moisture resistant, water-dispersible tape is provided. The adhesive and tape are resistant to autoclavation conditions and/or moisture and body fluids during usage, and are water-dispersible when immersed in aqueous solutions. The tape may be used with cloth body coverings, such as garments such as hospital gowns, drapes, dressings, diapers and other body coverings which require cloth to cloth or cloth to skin adhesion in the presence of moisture and bodily fluids yet be dispersible from such body coverings during laundering or other aqueous alkali immersion.
摘要:
A method of using a pressure sensitive adhesive to form a moisture resistant, water-dispersible tape is provided. The adhesive and tape are resistant to autoclavation conditions and/or moisture and body fluids during usage, and are water-dispersible when immersed in aqueous solutions. The tape may be used with cloth body coverings, such as garments such as hospital gowns, drapes, dressings, diapers and other body coverings which require cloth to cloth or cloth to skin adhesion in the presence of moisture and bodily fluids yet be dispersible from such body coverings during laundering or other aqueous alkali immersion.