摘要:
A phenolic foam is made by foaming and curing a formable phenolic resin composition that comprises a phenolic resin, a blowing agent, an acid catalyst and an inorganic filler. The blowing agent comprises a blend of chlorinated aliphatic hydrocarbon containing 2 to 5 carbon atoms and an aliphatic hydrocarbon containing from 3 to 6 carbon atoms mixed in a ratio of 60/40 to 95/5 parts by weight. The inorganic filler is at least one selected from a metal hydroxide, a metal oxide, a metal carbonate and metal powder. The phenolic foam has a pH of 5 or more and a water uptake less than 1 kg/m2. A phenolic foam with a higher pH value compared with conventional phenolic foam reduces corrosion risk when in contact with metallic materials. The phenolic foam maintains excellent long-term stable thermal insulation performance, low water uptake and fire resistance performance and by using the said blowing agent, does not harm the environment as an ozone or global warming depleting material.
摘要翻译:通过发泡和固化包含酚醛树脂,发泡剂,酸催化剂和无机填料的可成形酚醛树脂组合物来制备酚醛泡沫。 发泡剂包含含有2至5个碳原子的氯代脂族烃和含有3-6个碳原子的脂族烃的混合物,其混合比例为60/40至95/5重量份。 无机填料是选自金属氢氧化物,金属氧化物,金属碳酸盐和金属粉末中的至少一种。 酚醛泡沫体的pH为5以上,吸水量小于1kg / m 2。 与常规酚醛泡沫相比,具有较高pH值的酚醛泡沫体在与金属材料接触时可降低腐蚀风险。 酚醛泡沫塑料具有优异的长期稳定的隔热性能,低吸水性和耐火性能,并且通过使用所述发泡剂,不会对臭氧或全球变暖消耗材料造成危害。
摘要:
A phenolic foam is made by foaming and curing a foamable phenolic resin composition that comprises a phenolic resin, a blowing agent, an acid catalyst and an inorganic filler. The blowing agent comprises a blend of chlorinated aliphatic hydrocarbon containing 2 to 5 carbon atoms and an aliphatic hydrocarbon containing from 3 to 6 carbon atoms mixed in a ratio of 60/40 to 5/5 parts by weight. The inorganic filler is at least one selected from a metal hydroxide, a metal oxide, a metal carbonate and a metal powder. The phenolic foam has a pH of 5 or more and a water uptake less than 1 kg/m2. A phenolic foam with a higher pH value compared with conventional phenolic foam reduces corrosion risk when in contact with metallic materials. The phenolic foam maintains excellent long-term stable thermal insulation performance, low water uptake and fire resistance performance and by using the said blowing agent, does not harm the environment as an ozone or global warming depleting material.
摘要翻译:通过发泡和固化包含酚醛树脂,发泡剂,酸催化剂和无机填料的可发泡酚醛树脂组合物来制备酚醛泡沫。 发泡剂包含含有2至5个碳原子的氯化脂族烃和含有3至6个碳原子的脂族烃的混合物,其混合比例为60/40至5/5重量份。 无机填料是选自金属氢氧化物,金属氧化物,金属碳酸盐和金属粉末中的至少一种。 酚醛泡沫体的pH为5以上,吸水量小于1kg / m 2。 与常规酚醛泡沫相比,具有较高pH值的酚醛泡沫体在与金属材料接触时可降低腐蚀风险。 酚醛泡沫塑料具有优异的长期稳定的隔热性能,低吸水性和耐火性能,并且通过使用所述发泡剂,不会对臭氧或全球变暖消耗材料造成危害。
摘要:
This invention relates to a foamable resol type phenolic resin forming material comprising a liquid resol type phenolic resin, a foaming agent, a foam stabilizer, an additive and an acid curing agent, said additive containing a nitrogen-containing bridged cyclic compound and said foam stabilizer containing a chlorinated aliphatic hydrocarbon compound having 2 to 5 carbon atoms, and a phenolic resin foam product obtained by foaming and curing this forming material.
摘要:
A phenolic foam is made by foaming and curing a foamable phenolic resin composition that comprises a phenolic resin, a blowing agent, an acid catalyst and an inorganic filler. The blowing agent comprises a blend of chlorinated aliphatic hydrocarbon containing 2 to 5 carbon atoms and an aliphatic hydrocarbon containing from 3 to 6 carbon atoms mixed in a ratio of 60/40 to 5/5 parts by weight. The inorganic filler is at least one selected from a metal hydroxide, a metal oxide, a metal carbonate and a metal powder. The phenolic foam has a pH of 5 or more and a water uptake less than 1 kg/m2. A phenolic foam with a higher pH value compared with conventional phenolic foam reduces corrosion risk when in contact with metallic materials. The phenolic foam maintains excellent long-term stable thermal insulation performance, low water uptake and fire resistance performance and by using the said blowing agent, does not harm the environment as an ozone or global warming depleting material.
摘要翻译:通过发泡和固化包含酚醛树脂,发泡剂,酸催化剂和无机填料的可发泡酚醛树脂组合物来制备酚醛泡沫。 发泡剂包含含有2至5个碳原子的氯化脂族烃和含有3至6个碳原子的脂族烃的混合物,其混合比例为60/40至5/5重量份。 无机填料是选自金属氢氧化物,金属氧化物,金属碳酸盐和金属粉末中的至少一种。 酚醛泡沫体的pH为5以上,吸水量小于1kg / m 2。 与常规酚醛泡沫相比,具有较高pH值的酚醛泡沫体在与金属材料接触时可降低腐蚀风险。 酚醛泡沫塑料具有优异的长期稳定的隔热性能,低吸水性和耐火性能,并且通过使用所述发泡剂,不会对臭氧或全球变暖消耗材料造成危害。
摘要:
A phenolic foam is made by foaming and curing a foamable phenolic resin composition that comprises a phenolic resin, a blowing agent, an acid catalyst and an inorganic filler. The blowing agent comprises an aliphatic hydrocarbon containing from 1 to 8 carbon atoms and the inorganic filler is at least one selected from a metal hydroxide, a metal oxide, a metal carbonate and a metal powder. The phenolic foam has a pH of 5 or more. The phenolic foam has a higher pH value compared with conventional phenolic foam and reduces corrosion risk when in contact with metallic materials. The phenolic foam maintains excellent long-term stable thermal insulation performance, low water uptake and fire resistance performance and by using a hydrocarbon blowing agent, does not harm the environment as an ozone depleting or global warming material.
摘要:
A phenolic foam is made by foaming and curing a foamable phenolic resin composition that comprises a phenolic resin, a blowing agent, an acid catalyst and an inorganic filler. The blowing agent comprises an aliphatic hydrocarbon containing from 1 to 8 carbon atoms and the inorganic filler is at least one selected from a metal hydroxide, a metal oxide, a metal carbonate and a metal powder. The phenolic foam has a pH of 5 or more. The phenolic foam has a higher pH value compared with conventional phenolic foam and reduces corrosion risk when in contact with metallic materials. The phenolic foam maintains excellent long-term stable thermal insulation performance, low water uptake and fire resistance performance and by using a hydrocarbon blowing agent, does not harm the environment as an ozone depleting or global warming material.
摘要:
The object of the present invention is to provide an expandable or foamable resol-type phenolic resin forming material that gives a phenolic resin foamed material or article which is excellent in strength and improved in brittleness and which has a high pH as compared with conventional materials or articles and has an excellent anti-corrosion property against a contact member, and a phenolic resin foamed material or article having the above properties, obtained by foaming the same, which are a foamable resol type phenolic resin forming material comprising a liquid resol type phenolic resin, a blowing agent, a foam stabilizer, an additive and an acid curing agent, said blowing agent comprising an organic non-reactive blowing agent and said additive comprising a nitrogen-containing bridged cyclic compound, and a phenolic resin foamed material or article obtained by foaming this forming material.
摘要:
A display device according to the present disclosure includes: an organic EL display unit having pixels; a variable voltage source which supplies a voltage to the organic EL display unit; and a voltage drop amount calculating circuit which regulates the voltage output by the variable voltage source, according to video data, in which the organic EL display unit further includes an anode-side power source line network and a cathode-side power source line network connected to the pixels and the variable voltage source, for supplying the voltage from the variable voltage source, and the voltage drop amount calculating circuit estimates, from the video data, a distribution of voltage drop amount in the anode-side power source line network and the cathode-side power source line network for each of the pixels, and regulates the voltage based on the estimated distribution of voltage drop amount for each of the pixels.
摘要:
An X-ray analysis apparatus has information about a relationship between selection of a measurement type and a replacement work of optical parts and shows, on a screen of a display, graphical information about optical parts which should be changed, to make it easy for an operator to perform a preliminary work before measurement. When the operator selects one desired measurement type among a plurality of measurement types in a selection window, there is displayed on the display, depending on the selected measurement type, graphical information about necessary optical parts which should be newly installed and/or installed optical parts which should be removed. The operator looks at the operating instructions and then performs the replacement work. The graphical information may be: graphical indication of the installation locations of the optical parts; different pictorial expressions about the installation and the removal works; and graphical indication of the identification marks of the optical parts.
摘要:
A method of manufacturing a cold-rolled can steel sheet having less planar anisotropy and achieving good workability. Rough-rolling is first performed on a continuously-cast slab. The slab has a composition essentially consisting of: C: 0.004 wt % or lower; Mn: 0.05-0.5 wt %; P: 0.02 wt % or lower; Al: 0.005-0.07 wt %; N: 0.004 wt % or lower; and Nb: 0.001-0.018 wt %, the rest being Fe and unavoidable impurities. A resultant sheet bar is then subjected to hot rolling which is completed at a finishing rolling temperature at an Ar.sub.3 transformation point or higher. The resultant sheet bar is coiled at a temperature range from 450.degree.-700.degree. C. Subsequently, the resultant sheet bar undergoes primary cold rolling before continuous annealing, which is performed at a recrystallization temperature or higher, and secondary cold rolling. The primary and secondary cold rolling are respectively performed at reduction ratios satisfying the following conditions of: 88%.gtoreq.CR.sub.1 %+0.36.times.CR.sub.2 .ltoreq.105% wherein CR.sub.1 : reduction ratio of the primary cold rolling CR.sub.2 : reduction ratio of the secondary cold rolling