Polyether-based urethane-group-containing polyamines containing polymers and/or copolymers of unsaturated monomers and, optionally, urea and/or biuret and/or allophanate groups are produced by (a) reacting an NCO-prepolymer in aqueous alkaline solution at 0.degree. to 40.degree. C. to form a carbamate; (b) converting this carbamate to an amine by adding an ion exchanger to the reaction mixture; and (c) separating the polyamine from the reaction mixture. The NCO-prepolymers used as starting materials are prepolymers of (i) polyalkylene ether polyols having a molecular weight of from 1,000 to 10,000 containing from 1 to 60 wt. % of graft (co)polymers of unsaturated monomers; and (ii) excess molar quantities of organic polyisocyanate; and optionally, (iii) a low molecular weight chain-extending agent. The product polyamines have a molecular weight of from 1,000 to 10,000 and contain from 0.65 to 59.3 wt. % graft (co)polymer and from 0.11 to 2.9 wt. % terminal NH.sub.2 groups attached to the ethers by urethane groups in the polyisocyanate. The product polyamines are particularly useful in the production of polyurethanes.
摘要:
Polymer-containing polyether polyamines containing terminal aromatically-bound amino groups are produced by in situ polymerization of a polyether polyamine with an olefinically unsaturated monomer. The polyether polyamine starting material must have terminal aromatic amino groups, a molecular weight of from 800 to 10,000 and an aromatic amino group content of from 0.3 to 16 wt. %. Suitable olefinically unsaturated monomers include .alpha.,.beta.-unsaturated nitriles, aromatic vinyl compounds, .alpha.,.beta.-unsaturated carboxylic acids and esters thereof, vinyl esters, vinyl halides, vinylidene halides, .alpha.,.beta.-unsaturated carboxylic acid amides and aminoalkyl esters of unsaturated carboxylic acids. Acrylonitrile/styrene mixtures are preferred monomers. The starting materials are employed in quantities such that the product modified polyether polyamine contains from 1 to 60 wt. % polymer or graft-polymer. The product polyamines are particularly useful in the production of polyurethanes.
摘要:
The present invention is directed to a process for the production of optionally cellular, polyurethane and/or polyurethane-urea moldings having an impervious skin by reacting in a closed mold a reaction mixture containing(a) at least one organic polyisocyanate,(b) at least one compound which has a molecular weight of about 400 to 12,000 and at least two isocyanate-reactive groups, and(c) optionally at least one compound which has a molecular weight of from 32 to 399 and at least two isocyanate-reactive groups,wherein before the reaction takes place a surface-improving additive (e) is added containing(e1) a liquid and sedimentation-stable polymer dispersion which is produced by the free radical addition polymerization or copolymerization of one or more olefinically unsaturated monomers in a high molecular weight compound having isocyanate-reactive groups of the type mentioned in (b),and optionally(e2) a metal salt of a monocarboxylic acid having at least 8 carbon atoms in the moleculewherein additive (e) is used in a quantity such that about 0.01 to 3 parts by weight of polymer solids of the polymer dispersion (e1) and up to about 2 parts by weight of metal salt (e2) are incorporated per 100 parts of component (b).
摘要:
Polymer modified polyamines having a polymer content of from 1 to 30 wt. % and an aromatic amino group content of from 1 to 12.5 wt. % are produced by hydrolyzing a polyisocyanate prepolymer in an aqueous alkaline medium. The polyisocyanate prepolymer is polymer modified by in situ polymerization of either the prepolymer or the isocyanate used in making the prepolymer with an unsaturated monomer in the presence of a radical forming polymerization catalyst in a manner such that a solution and/or dispersion is formed. The prepolymer is formed from a relatively high molecular weight polyhydroxyl compound, aromatic polyisocyanate, and optionally a chain extender or crosslinking agent. The aromatic polyisocyanate used is from 60-100 wt. % polyisocyanate of the diphenyl alkane series and from 0 to 60 wt. % tolylene diisocyanate. The preferred unsaturated monomer is acrylonitrile containing up to 20 wt. % comonomer. The polymer modified polyamines of the present invention are particularly useful in the production of polyurethanes.
摘要:
The instant invention is directed to compounds having an average molecular weight of from 300 to 12,000, containing: at least one hydroxyl group and at least one urethano-aryl-sulfonic acid group and a method for their preparation. The process is characterized as a process for the preparation of compounds having a number average molecular weight of from 300 to 12,000 having at least one hydroxyl group and at least one urethano-aryl-sulfonic acid group, comprising: reacting at from 0.degree. to 190.degree. C.(A) compounds having a molecular weight of from 62 to 10,000 having at least two hydroxyl groups; with(B) aromatic isocyanato sulfonic acids, wherein the equivalent ratio of the total quantity of isocyanate groups (including any isocyanate groups present in dimerized form) to sulfonic acid groups is from 0.5:1 to 50:1 and the equivalent ratio of the sum of hydroxyl groups in (A) to NCO groups is from 1.5:1 to 30:1. The invention is also directed to the product by the process.
摘要:
The instant invention is directed to compounds having an average molecular weight of from 300 to 12,000, containing: at least one hydroxyl group and at least one urethano-aryl-sulfonic acid group and a method for their preparation. The process is characterized as a process for the preparation of compounds having a number average molecular weight of from 300 to 12,000 having at least one hydroxyl group and at least one urethano-aryl-sulfonic acid group, comprising: reacting at from 0.degree. to 190.degree. C.(A) compounds having a molecular weight of from 62 to 10,000 having at least two hydroxyl groups; with(B) aromatic isocyanato sulfonic acids, wherein the equivalent ratio of the total quantity of isocyanate groups (including any isocyanate groups present in dimerized form) to sulfonic acid groups is from 0.5:1 to 50:1 and the equivalent ratio of the sum of hydroxyl groups in (A) to NCO groups is from 1.5:1 to 30:1. The invention is also directed to the product by the process.
摘要:
The present invention is directed to new aromatic diamines containing sulfonic acid aryl esters corresponding to the formula ##STR1## wherein R.sub.1 represents hydrogen, an optionally branched C.sub.1 -C.sub.6 alkyl radical (preferably a methyl group), a C.sub.1 -C.sub.6 alkoxy radical or a halogen atom (preferably chlorine) andR.sub.2 and R.sub.3 which may be the same or different, represent hydrogen, an optionally branched C.sub.1 -C.sub.20 (preferably C.sub.1 -C.sub.6) alkyl radical, a C.sub.1 -C.sub.6 alkoxy radical or a halogen atom (preferably chlorine).The present invention is also directed to a process for the production of the above aromatic diamines containing sulfonic acid esters by the reaction of optionally substituted sulfochlorides with optionally substituted phenols followed by hydrogenation.Finally, the present invention is directed to the use of aromatic diamines containing sulfonic acid aryl esters as a synthesis component for the production of polyurethane plastics by the isocyanate polyaddition process.
摘要:
A mortar comprising an inorganic binder such as anhydrite, gypsum or cement is rendered more flowable and processible by incorporating therein a sulfonic acid group-containing formaldehyde condensation product with a cycloalkanone, e.g. preferably about 0.05 to 5% by weight of the binder of the condensation product of sodium sulfite, formaldehyde and cyclohexanone. There may also be present an auxiliary such as FeSO.sub.4,7 H.sub.2 O,Al.sub.2 (SO.sub.4).sub.3.18 H.sub.2 O or KAl(SO.sub.4).sub.2, as well as an additive such as a plasticizer, hardening accelerator, retarder, air-entraining agent, thickener, activator, anti-foam agent or synthetic resin dispersion, and/or an aggregate such as sand, silica, perlite, pumice or foamed plastic beads.
摘要:
The mechanical properties of gelatin layers for photographic materials are improved by the addition of water-insoluble, elastic copolymers which consist of acrylic acid or methacrylic acid esters (I) which may be mixed with other vinyl and divinyl monomers (II) and which contain comonomers (III) which contain disulfone imidoester or sulfonimidophosphoric acid ester or amide groups.
摘要:
The compounds of the present invention are obtained by the reaction of carbamoyl lactams (from lactams and polyisocyanates) with polyhydric alcohols or monoamino alcohols in the presence of catalytic quantities of a strong basic catalyst, e.g. an alkali metal alcoholate, at elevated temperatures.The polyols contain urea groups and either ester or amide groups and correspond to formula (I) or (II) ##STR1## The polyols are crystalline, relatively high melting compounds which are used as reactants for the synthesis of polyurethane elastomers, in particular in the form of finely divided components in one-component polyurethane reaction mixtures.