    TITANIUM BLACK DISPERSION, PHOTOSENSITIVE RESIN COMPOSITION, WAFER LEVEL LENS, LIGHT BLOCKING FILM, METHOD FOR PRODUCING THE LIGHT BLOCKING FILM, AND SOLID-STATE IMAGE PICKUP ELEMENT
    7.
    发明申请
    TITANIUM BLACK DISPERSION, PHOTOSENSITIVE RESIN COMPOSITION, WAFER LEVEL LENS, LIGHT BLOCKING FILM, METHOD FOR PRODUCING THE LIGHT BLOCKING FILM, AND SOLID-STATE IMAGE PICKUP ELEMENT 有权
    钛黑色分散剂，感光性树脂组合物，水平镜片，遮光膜，用于制造遮光膜的方法和固态图像拾取元件

    公开(公告)号：US20120199727A1

    公开(公告)日：2012-08-09

    申请号：US13502714

    申请日：2010-10-19

    申请人： Makoto Kubota

    发明人： Makoto Kubota

    IPC分类号： H01L31/00 ,  B32B5/16 ,  G03F7/004 ,  G03F7/20 ,  C08K3/08 ,  C08L33/06

    CPC分类号： G03F7/105 ,  C08F290/064 ,  C08F292/00 ,  C08K3/22 ,  C08K2003/0881 ,  G03F7/033

    摘要： A titanium black dispersion includes titanium black particles, a dispersant, and an organic solvent. When the titanium black dispersion is for a wafer level lens, 90% or more of dispersed objects that consist of the titanium black particles have particle diameters of 30 nm or less, or dispersed objects including the titanium black particles contains Si atoms and the content ratio of Si atoms to Ti atoms (Si/Ti) in the dispersed objects is 0.05 or higher. When the titanium black dispersion is used for formation of a light-shielding film that is provided on one side of a silicon substrate having an image pickup device section on the other side, and that shields against infrared light, 90% or more of dispersed objects that consist of the titanium black particles have particle diameters of 30 nm or less.

    摘要翻译： 钛黑分散体包括钛黑颗粒，分散剂和有机溶剂。 当钛黑分散体用于晶片级透镜时，由钛黑颗粒组成的分散物体的90％以上具有30nm以下的粒径，或者包含钛黑粒子的分散物含有Si原子， 的Si原子与Ti原子（Si / Ti）的比例为0.05以上。 当钛黑色分散体用于形成遮光膜时，该遮光膜设置在另一侧具有图像拾取装置部分的硅衬底的一侧，并且屏蔽红外光，分散物体的90％以上 由钛黑粒子构成的粒径为30nm以下。

    HYBRID VEHICLE SYSTEMS
    9.
    发明申请
    HYBRID VEHICLE SYSTEMS 审中-公开
    混合动力系统

    公开(公告)号：US20090163656A1

    公开(公告)日：2009-06-25

    申请号：US12340207

    申请日：2008-12-19

    申请人： James Joseph DeLuca ,  Gary D. Tucker, II

    发明人： James Joseph DeLuca ,  Gary D. Tucker, II

    IPC分类号： B05D3/10 ,  C08G77/10

    CPC分类号： C08G77/58 ,  B01J13/00 ,  B01J13/0039 ,  B01J13/0047 ,  C01G23/053 ,  C08K3/08 ,  C08K2003/0881 ,  C09D1/00 ,  C09D7/61 ,  C09D7/63

    摘要： A hybrid film-forming composition is prepared by forming an aqueous mixture including an organofunctional silane, a metal chloride, and an acid, and boiling the mixture. A base is added to the aqueous mixture to substantially neutralize the mixture and to form a hydroxide of the metal. A colloidal suspension including the metal hydroxide and a siloxy compound is formed. A peroxide-based solution is added to the suspension to form a suspension including a peroxide of the metal. The suspension is allowed to equilibrate at room temperature. The suspension is boiled at a pressure greater than atmospheric pressure to form a hybrid film-forming composition including the condensation product of a siloxy compound and a metal peroxide. A coating formed from the hybrid film-forming composition may be hydrophobic or hydrophilic.

    摘要翻译： 通过形成包含有机官能硅烷，金属氯化物和酸的水性混合物并煮沸该混合物来制备混合成膜组合物。 将碱加入含水混合物中以基本上中和混合物并形成金属的氢氧化物。 形成包含金属氢氧化物和甲硅烷氧基化合物的胶态悬浮液。 向悬浮液中加入过氧化物溶液以形成包含金属的过氧化物的悬浮液。 使悬浮液在室温下平衡。 将悬浮液在大于大气压的压力下煮沸以形成包含甲硅烷氧基化合物和金属过氧化物的缩合产物的混合膜形成组合物。 由所述杂交成膜组合物形成的涂层可以是疏水的或亲水的。

    Thermally stable polyester, process for its preparation and its use
    10.
    发明授权
    Thermally stable polyester, process for its preparation and its use 失效
    热稳定聚酯，其制备方法及其用途

    公开(公告)号：US06841604B2

    公开(公告)日：2005-01-11

    申请号：US10295933

    申请日：2002-11-15

    申请人： Uwe Bayer ,  Jürgen Popp ,  Thomas Wehrmeister

    发明人： Uwe Bayer ,  Jürgen Popp ,  Thomas Wehrmeister

    IPC分类号： C08G63/85 ,  C08K3/04 ,  C08K3/08 ,  C08K3/20 ,  C08L67/00

    CPC分类号： C08K3/04 ,  C08G63/85 ,  C08K3/08 ,  C08K2003/0881 ,  Y10T428/2913 ,  Y10T442/30 ,  Y10T442/60 ,  C08L67/02

    摘要： A polyester with a carbon black content of up to 20% by weight, based on the polyester, is condensed, after transesterification of DMT with diol, or after esterification of terephthalic acid with diol, with the aid of a titanium-based catalyst. The carbon black is added in the form of a carbon black dispersion together with the polycondensation catalyst to the transesterification product or esterification product. The carbon black dispersion comprises gas black or furnace black and a dispersing agent, and these are dispersed in diol. The diameter of the carbon black particles is below that of carbon black particles in a polyester using an antimony compound as catalyst.

    摘要翻译： 在DMT与二醇的酯交换反应之后，或者通过钛基催化剂将对苯二甲酸与二醇酯化后，将碳黑含量高达20重量％的聚酯与基于聚酯的聚酯缩合。 将炭黑与缩聚催化剂一起以炭黑分散体的形式加入到酯交换产物或酯化产物中。 炭黑分散体包括气黑或炉黑和分散剂，并将它们分散在二醇中。 在使用锑化合物作为催化剂的聚酯中，炭黑粒子的直径低于炭黑粒子的直径。