A pneumatic tire having a tread comprised of (a) a diene-based elastomer containing olefinic unsaturation and (b) from 1 to 150 phr of a metal oxide aerogel.
摘要:
The present invention relates to rubber compositions containing borate compounds of the formula ##STR1## wherein R.sup.1 and R.sup.2 are independently selected from the group consisting of alkoxy radicals having from 1 to 8 carbon atoms; R.sup.3 is selected from the group consisting of alkylene groups having from 1 to 15 carbon atoms and arylene and alkyl substituted arylene groups having from 6 to 10 carbon atoms; X is selected from the group consisting of ##STR2## and Y is selected from the group consisting of S.sub.x and Se.sub.xwhere x is an integer of from 1 to 8.
摘要:
A rubber composition comprised of elastomer(s) including a tin or silicon modified elastomer, modified carbon black and silica coupler. Said modified carbon black has one or more of silanol, siloxane, titanium dioxide, zirconium hydroxide and aluminum hydroxide on its surface. A tire having a tread of such rubber composition is also provided.
摘要:
A rubber composition containing a filler having individual aggregates containing both large and small particles, where the small particles are grafted onto the surface of the large particles. The small particles range from 1 to 30 weight percent of the overall weight of the filler. The large particles range from 70 to 99 weight percent of the overall weight of the filler. The small particles range in size of from 1 to 16 nanometers in diameter and the large particles range in size of from 17 to 500 nanometers in diameter.
摘要:
This invention relates to aggregates comprised of particles which contain silicon dioxide and to elastomers reinforced therewith. The invention also relates to tires having treads composed of such reinforced elastomers.
摘要:
The invention relates to a tire with a tread composed of a rubber composition containing carbon black reinforcement as significant quantities two different carbon blacks and without quantitative amounts of silica reinforcement.
摘要:
The invention relates to a process for preparation of a rubber composition containing silica reinforcement through the utilization of a high purity organosilane disulfide/trisulfide. Pneumatic tires having treads prepared by such process are provided.
摘要:
The present invention relates to asymmetrical siloxy compounds of the formulae ##STR1## wherein R.sup.1, R.sup.2 and R.sup.3 are independently selected from the group consisting of alkoxy radicals having from 1 to 8 carbon atoms; R.sup.4 is selected from the group consisting of alkylene groups having from 1 to 15 carbon atoms and arylene and alkyl substituted arylene groups having from 6 to 10 carbon atoms; R.sup.5 is selected from the group consisting of alkylene groups having from 1 to 15 carbon atoms, arylene and alkyl substituted arylene groups having 6 to 10 carbon atoms; y is 2 to 8; X is selected from the group consisting of ##STR2## W is selected from the group consisting of ##STR3## and Z is 1 to 8
摘要:
The present invention relates to a rubber composition comprising (A) an elastomer containing olefinic unsaturation and (B) 35 to 110 phr of silica filler, wherein said silica filler is comprised of (i) 10 to 100 phr of a first silica having a pore size distribution maximum of the aggregates in the first silica ranging from greater than 55 to 400 nm as determined by mercury porosimetry and an average specific surface area ranging from 60 to 135 m2/g as determined by N2 adsorption; and (ii) 10 to 100 phr of a second silica having a pore size distribution maximum of the aggregates in the second silica ranging from 5 to 50 nm as determined by mercury porosimetry and an average specific surface area ranging from 140 to 250 m2/g as determined by N2 adsorption.
摘要:
This invention relates to preparation of an elastomer which contains a dispersion of silica reinforcement by forming a silica reinforcement in situ within an unvulcanized elastomer host, the resulting elastomer/filler composite and tire having component which contains such reinforced elastomer. The invention includes a rubber composition of at least two elastomers wherein one of said elastomers is a pre-formed composite of elastomer/in situ formed silica reinforcement. A tire having a component of such rubber composition, particularly a tire tread, is specifically contemplated.