摘要:
The present invention provides fabrics with cut loop pile comprising a synthetic filament core yarn and covering yarn of a split microfiber yarn and a viscose rayon yarn and a manufacturing method thereof. The core yarn at the section where said loops are cut is outwardly protruded from the covering yarn, wherein the synthetic multifilament core yarn is separated into multiple filaments to function as hooks. The fabrics with cut loop pile show superior characteristics in polishing properties, sliding properties, water absorption properties, rapid drying properties and feeling of touch owing to the split yarn of microfibers and the viscose rayon yarn which comprises the covering yarn, and polishing can be performed while easily catching foreign substances such as extremely minute dust particles or human hairs and the like by the hook-shaped multifilaments of the core yarn. Thus the fabrics with cut loop pile according to the present invention can be used usefully in products such as various kind of mats, towels, bathroom products, and the like including dishcloths and mops.
摘要:
The present invention provides a glove having both high softness and high air tightness. A glove of the present invention has a fiber-made base having a shape of a hand of a person and a coating formed on a surface of at least a portion of the base, where a burning treatment is applied to the base, air tightness of a portion of the glove which has been applied with the burning treatment is maintained even when pressure of 9 kPa or higher is imparted to inside of the base, and the fiber-made base is formed of filament yarns.
摘要:
The present invention provides fabrics with cut loop group and a manufacturing method thereof, wherein the core yarn at the section where said loops are being cut is outwardly protruded from the covering yarns, while the rayon yarn, which is a core yarn, is separated into multiple filaments. The fabrics with cut loop group show superior characteristics in polishing properties, sliding properties, water absorption properties, rapid drying properties and feeling of touch since polishing can be performed while easily catching foreign substances such as extremely minute dust particles or human hairs and the like by the rayon yarn, which is a core yarn, functioning as a hook. Thus the fabrics with cut loop group according to the present invention can be used usefully in the products such as various kind of mats, towels, bathroom products, and the like including dishclothes and mops.
摘要:
A method of making a sheared wool, deep pile fabric that closely resembles natural sheepskin fleece that includes forming a length of wool pile fabric having natural wool fibers on one side and a scrim on an opposing side and finishing the wool pile fabric as natural shearling. The finishing process includes polishing the wool fiber side of the pile fabric by guiding the length of pile fabric over one or more heated first polishing rolls, applying a sheepskin conditioning solution to the wool fiber side of the pile fabric, further polishing the wool fiber side of the pile fabric by guiding the fabric a plurality of times over one or more second heated polishing rolls, and cutting the wool fibers to a designated length.
摘要:
An artificial leather is provided having a raised nap to give an elegant appearance, and further has a good pilling-resistance without affecting the spinning performance. The pilling-resistant artificial leather is a sheet-form object including a microfiber having a monofilament diameter of 0.3 to 10 μm and a polymeric elastomer, and having a raised nap made of the microfiber. The microfiber includes inorganic particles in a proportion of 0.01 to 5% by mass relative to 100% by mass of the microfiber, and a silicone oil in a proportion of 0.001 to 1% by mass relative to 100% by mass of the microfiber. The microfiber contains a polyester microfiber in a proportion of 90% by mass or more thereof.
摘要:
A double-face velour fabric article consists of a fabric body having a technical face formed by a filament stitch yarn and a technical back formed by a filament loop yarn. The filament stitch yarn includes a heat sensitive material, e.g. a hot melt material or a heat shrinkable material, and/or an elastomeric material, such as spandex. The fabric body has a velour surface formed at both the technical back and the technical face. Raised fibers of at least one of the technical face and the technical back may be entangled, including in and/or through interstices of the fabric body, toward the other of the technical face and the technical back, e.g., by a hydroentanglement process applied after finishing. The fabric body has permeability of about 80 ft3/ft2/min, or less, under a pressure difference of ½ inch of water across the fabric body.
摘要:
The object of the invention is an aroma-therapeutic bedding set comprising a filling consisting of fibre fleece layers, made of natural or synthetic fibres or a mixture thereof, or fibres placed in an outside ticking, and containing preferably evenly distributed dried and cut herbs embedded in the fibres, or between the layers and embedded in the fibres of the layers.
摘要:
A union fabric comprising 6 to 60% by weight of a polyester fiber (A), 35 to 85% by weight of a halogen-containing fiber (B), and 5 to 55% by weight of a cellulose fiber (C) in which fabric the warp comprises weaving yarn containing the polyester fiber and the weft comprises flameproof chenille yarn and other weaving yarn, with the chenille yarn containing 10 to 70% by weight of halogen and 1 to 35% by weight of a flame retardant consisting of a metal compound, and in which fabric the content of the warp-constituting weaving yarn containing the polyester fiber is 20 to 40% by weight and those of the weft-constituting flameproof chenille yarn and the weft-constituting other weaving yarn are 35 to 70% by weight and 10 to 45% by weight respectively. This union fabric is excellent in design, texture, comfortableness in use.
摘要:
A sheet of an artificial leather substrate contains an upper-layer nonwoven fabric A (1) and a base nonwoven fabric B (2). The upper-layer nonwoven fabric A (1) is a wet-laid nonwoven fabric having a density of 0.30 to 0.50 g/cm3 and being produced with synthetic fibers in which the component fibers have a fineness of 0.005 to 1.1 dtex, a fiber length of 3 to 10 mm and a weight per unit area of 20 to 150 g/m2, and the base nonwoven fabric B (2) is a layer of a nonwoven fabric having a density of 0.15 g/cm3 or more and less than 0.28 g/cm3 and being produced with synthetic fibers in which the component fibers have a fineness greater than that of the component fibers of the upper-layer nonwoven fabric A and 4.5 dtex or less, a fiber length of 2 to 15 mm and a weight per unit area of 50 to 400 g/m2. The upper-layer nonwoven fabric A (1) and the base nonwoven fabric B (2) are layered, made into a single body by entanglement of the component fibers of both layers and impregnated with an elastic polymer. Thus, artificial leather having a texture similar to natural leather and a substrate for use therein are provided at low cost.
摘要翻译:人造皮革基材的片材含有上层无纺布A(1)和基础无纺布B(2)。 上层无纺布A(1)是密度为0.30〜0.50g / cm 3的湿式无纺布,其成分纤维的细度为0.005〜1.1dtex,纤维长度 3〜10mm,单位面积重量为20〜150g / m 2,基体无纺布B(2)为密度为0.15g / cm 3以上且小于0.28g的无纺布层 / cm3,并且由合成纤维制成,其中组分纤维的细度大于上层无纺织物A的组分纤维的纤度,4.5dtex或更小,纤维长度为2至15mm,每单位重量 面积为50〜400g / m2。 上层无纺布A(1)和基底无纺布B(2)通过两层的组分纤维缠结并用弹性聚合物浸渍而被层压成单体。 因此,以低成本提供具有类似于天然皮革的质地的人造革和其中使用的基材。
摘要:
An apparatus for raising the pile of a sheet of cloth web comprising a transport means for transporting the sheet of cloth web along a path; and, at least one primary air knife disposed at a distance from a first side of said path and arranged such that it extends across the path and is inclined such that the air stream from the air knife is incident to the path at an angle to the normal to the path.