摘要:
The present invention relates to a process for the preparation of mixed vanadium, antimony and iron oxides and to their use as catalysts for the ammoxidation of alkanes. The process for the preparation of a mixed oxide defined above is characterized in that:respective vanadium, antimony and iron compounds are dissolved in at least one saturated alcohol or in water,the alcoholic .epsilon.olution or the aqueous solution thus obtained is brought into contact with an aqueous solution containing an ammonium salt, in order to precipitate the mixed oxide,the mixed oxide obtained is separated and calcined.
摘要:
Disclosed are catalysts in powdered form comprising a major amount of the oxides of a first metal selected from copper or zinc, a second metal selected from chromium, molybdenum, tungsten and vanadium, and optionally, a minor amount of the oxide of a promoter metal selected from the group consisting of manganese, barium, zinc, nickel, cobalt, cadmium, iron and any combination thereof provided that the promoter metal is not zinc if the first metal is zinc, wherein the average particle diameter of the powder is from about 6 to about 20 microns; and the particle surface area is from about 20 to about 70 m.sup.2 /g. Also disclosed is a process for preparing such catalysts and a process for hydrogenating aldehydes, ketones, carboxylic acids and carboxylic acid esters with catalysts of the type described.
摘要:
The present invention relates to a catalyst for use in a process for the preparation of hydrocarbons comprising cobalt and manganese and/or vanadium, supported on a carrier, wherein the cobalt:(manganese+vanadium) atomic ratio is at least 12:1. Preferably, the cobalt:(manganese+vanadium) atomic ratio is at most 1500:1. The invention further relates to a process for the preparation of hydrocarbons which comprises contacting a mixture of hydrogen and carbon monoxide at elevated temperature and pressure with a catalyst as described hereinbefore. Typically, at least part of the cobalt is present in the metallic state.
摘要:
Disclosed is a process for making an .alpha., .beta.-unsaturated monoitrile by the catalytic reaction of a paraffin containing 3-5 carbon atoms with molecular oxygen and ammonia by catalytic contact of the foregoing reactants in a reaction zone with a metal oxide catalyst containing the elements indicated by the empirical formula,V.sub.v A.sub.a D.sub.d Sn.sub.m Sb.sub.n Cu.sub.c O.sub.x (formula 1)in the relative atomic proportions indicated by the subscripts, whereA is selected from Te and BiD is one or more optional elements selected from Mo, W, Ti, Ge, Ce, La, Cr, Mn, Mg, Ca, Co, Ni, Fe, Nb, Ta, Ag, Zn, Cd, B, P, Na, K and Cs, anda is 0.001 to 30d is zero to 30c is 0.001 to 30m is 0.1 to 60n is 0.1 to 60n/v is>12 and
摘要:
The present invention pertains to novel solid solutions involving FeO, V.sub.2 O.sub.3 and TiO.sub.2 and the method for their preparation. The solid compositions involving FeO, V.sub.2 O.sub.3 and TiO.sub.2 fall within the shaded area of a polygon in a ternary composition diagram of FeO, V.sub.2 O.sub.3 and TiO.sub.2 as shown in the drawing herein e.g., FIG. 1. The composition may be used as an oxidation catalyst or in the manufacture of high temperature refractories.
摘要翻译:本发明涉及涉及FeO,V2O3和TiO2的新型固溶体及其制备方法。 涉及FeO,V2O3和TiO2的固体组合物在FeO,V 2 O 3和TiO 2的三元组成图中落在多边形的阴影区域内,如图所示,如图1所示。 该组合物可用作氧化催化剂或制造高温耐火材料。
摘要:
A process for the reduction of nitrogen oxides contained in exhaust gases comprising reacting the gases with a reducing agent in the presence of a catalyst, the catalyst being based on carbon and having a carbon content greater than 65% by weight and containing 0.1 to 10% by weight of a sparingly soluble oxide of one or more metal selected from the group consisting of Co, Fe, Ni, Cr, V, Mo, W, Cu, Mn and Ti and having a nitrogen content of from 0.5 to 5% by weight, wherein the molar ratio of the reducing agent to the nitrogen oxide is 0.3 to 0.7.
摘要:
Carbon monoxide is reacted with water vapor and converted into hydrogen and carbon dioxide, in the presence of a thio-resistant catalyst which comprises an active phase deposited onto a support, said active phase comprising molybdenum, vanadium or tungsten, and a cobalt and/or nickel promoter therefor, and said support comprising cerium oxide or zirconium oxide. The reaction mixture advantageously includes carbon monoxide, hydrogen, water and compounds of sulfur, wherefrom hydrogen is selectively produced in increased amounts.
摘要:
Carbon monoxide is reacted with water vapor and converted into hydrogen and carbon dioxide, in the presence of a thio-resistant catalyst which comprises an active phase deposited onto a support, said active phase comprising molybdenum, vanadium or tungsten, and a cobalt and/or nickel promoter therefor, and said support comprising cerium oxide or zirconium oxide. The reaction mixture advantageously includes carbon monoxide, hydrogen, water and compounds of sulfur, wherefrom hydrogen is selectively produced in increased amounts.
摘要:
Ammoxidation of C.sub.3 to C.sub.5 acyclic alkanes with NH.sub.3 and O.sub.2 using (1) a mole ratio of alkane:NH.sub.3 in the range from 2 to 16 and a mole ratio of alkano:O.sub.2 in the range 1 to 10 and (2) a mixture of particulate catalyst composition, the first being especially effective to promote formation of an unsaturated nitrile and an olefin from the paraffin, and the second catalyst composition being especially effective to promote the conversion of the olefin to the unsaturated nitrile. Catalytic compositions useful in the process are disclosed.
摘要:
A catalyst suitable for use in catalytic shift, or methanol synthesis, comprises copper, zinc oxide, magnesia, and at least one trivalent metal oxide, e.g. alumina. The amount of magnesia is such that the magnesium atoms constitute 0.2 to 7% of the total number of copper, zinc, and magnesium atoms.