摘要:
A method of forming a golf club head assembly includes aligning a faceplate with a recess of a club head; welding the faceplate to the club head; then, after welding the faceplate, heating the club head and the faceplate to at least a solvus temperature of the faceplate for a predetermined amount of time; and then, after heating the club head and the faceplate, allowing the club head and the faceplate to air cool.
摘要:
Ferritic stainless steel sheet which is excellent in ridging resistance which comprises, by mass %, Cr: 10 to 30%, Sn: 0.005 to 1%, C: 0.001 to 0.1%, N: 0.001 to 0.1%, Si: 0.01 to 3.0%, Mn: 0.01 to 3.0%, P: 0.005 to 0.1%, and S: 0.0001 to 0.01% and has a balance of Fe and unavoidable impurities and which has an X-ray diffraction strength in the {100} orientation from a surface layer to t/4 (“t” is sheet thickness) of 2 or more.
摘要:
Method of manufacturing a cemented carbide cutting tool, includes a) bonding a body part of hot work tool steel and a cutting part of cemented carbides together by heat treatment; b) cooling the bonded body part and cutting part for a preset period of time; c) machining the cutting part to have a predetermined pattern according to its application and forming a cutting tool; d) coating a surface of the machined cutting tool with a film of at least one of metallic oxides, nitrides and carbides; and e) cooling the coated cutting tool for a preset period of time in air, and a cutting tool manufactured by the method. Cracks do not generate even after the coating step, and thus cemented carbide cutting tool having excellent mechanical properties may be manufactured.
摘要:
The present invention provides a cold-rolled and annealed Dual-Phase steel sheet having strength from 980 to 1100 MPa and a breaking elongation greater than 9%. The composition includes the contents being expressed by weight: 0.055%≦C≦0.095%, 2%≦Mn≦2.6%, 0.005%≦Si≦0.35%, S≦0.005%, P≦0.050%, 0.1≦Al≦0.3%, 0.05%≦Mo≦0.25%, 0.2%≦Cr≦0.5%, Cr+2Mo≦0.6%, Ni≦0.1%, 0.010≦Nb≦0.040%, 0.010≦Ti≦0.050%, 0.0005≦B≦0.0025%, and 0.002%≦N≦0.007%. The remainder of the composition includes iron and inevitable impurities resulting from the smelting. A manufacturing method is also provided.
摘要:
The invention relates to a high-impact-toughness steel rail and a production method thereof, and belongs to the field of steel rail material production. The present invention is to provide a high-impact-toughness steel rail. The high-impact-toughness steel rail provided in the present invention is a pearlite steel rail with 0.05˜0.09 μm of inter-lamellar spacing and 30˜35 J of ballistic work at normal temperature; the chemical components of the steel rail in weight percentage are: C: 0.71-0.82 wt %, Si: 0.25-0.45 wt %, Mn: 0.75-1.05 wt %, V: 0.03-0.15 wt %, P: ≦0.030 wt %, S: ≦0.035 wt %, Al: ≦0.020 wt %, and Fe and inevitable impurities of the remaining content. The U-type impact toughness of rail head of the steel rail manufactured with the method disclosed in the present invention can be 30 J or more, and the tensile strength is about 1,300 MPa or higher.
摘要:
A high-formability, super-high-strength, hot-dip galvanized steel plate, the chemical composition of which comprises, based on weight percentage, C: 0.15-0.25 wt %, Si: 1.00-2.00 wt %, Mn: 1.50-3.00 wt %, P≦0.015 wt %, S≦0.012 wt %, Al: 0.03-0.06 wt %, N≦0.008 wt %, and the balance of iron and unavoidable impurities. The room temperature structure of the steel plate comprises 10-30% ferrite, 60-80% martensite and 5-15% residual austenite. The steel plate has a yield strength of 600-900 MPa, a tensile strength of 980-1200 MPa, and an elongation of 15-22%. Through an appropriate composition design, a super-high-strength, cold rolled, hot-dip galvanized steel plate is manufactured by continuous annealing, wherein no expensive alloy elements are added; instead, remarkable increase of strength along with good plasticity can be realized just by appropriate augment of Si, Mn contents in combination with suitable processes of annealing and furnace atmosphere control. In addition, the steel plate possesses good galvanization quality that meets the requirement of a super-high-strength, cold rolled, hot-dip galvanized steel plate for automobiles.
摘要:
A steel slab having a composition containing C: more than 0.07% and 0.2% or less, Si: 2.0% or less, Mn: 1.0% to 3.0%, Al: 0.1% or less, Ti: 0.05% to 0.3%, and V: 0.05% to 0.3% on a mass percent basis is heated to 1100° C. or more and is subjected to rough rolling and finish rolling. In the finish rolling, the total rolling reduction of two final passes is 30% or more, and the finish rolling temperature ranges from (Ar3 transformation temperature) to (Ar3 transformation temperature+120° C.). Cooling is started within 2 seconds after the finish rolling. Coiling is performed at an average cooling rate of 40° C./s or more at a coiling temperature in the range of 300° C. to 500° C. The resulting high-strength hot-rolled steel sheet has a microstructure in which a bainite phase constitutes more than 90% by volume, the average lath interval of bainite is 0.45 μm or less, and the ratio of Fe-based carbide precipitated in bainite lath to all Fe-based carbide is 10% or more, has a high tensile strength of 900 MPa or more, and has significantly improved punchability in mass production.
摘要:
There is provided a thick steel plate having good multipass weld joint CTOD characteristics for low to medium heat input and a method for manufacturing the thick steel plate. A steel plate containing, on a mass percent basis, C: 0.03% to 0.12%, Si: 0.5% or less, Mn: 1.0% to 2.0%, P: 0.015% or less, S: 0.0005% to 0.0050%, Al: 0.005% to 0.060%, Ni: 0.5% to 2.0%, Ti: 0.005% to 0.030%, N: 0.0015% to 0.0065%, O: 0.0010% to 0.0050%, Ca: 0.0005% to 0.0060%, and optionally one or two or more of Cu and the like, wherein Ti/N, Ceq, Pcm, and ACR are in particular ranges, a base material of the plate has an effective grain size of 20 μm or less at half the thickness of the plate, and the plate contains a particular number of complex inclusions at ¼ and ½ of the thickness of the plate, the complex inclusions being composed of a sulfide containing Ca and Mn and an oxide containing Al and having an equivalent circular diameter of 0.1 μm or more. Steel having the composition described above is heated at a particular temperature, is then hot-rolled, and is cooled.
摘要:
Ferritic stainless steel sheet which is excellent in ridging resistance which comprises, by mass %, Cr: 10 to 30%, Sn: 0.005 to 1%, C: 0.001 to 0.1%, N: 0.001 to 0.1%, Si: 0.01 to 3.0%, Mn: 0.01 to 3.0%, P: 0.005 to 0.1%, and S: 0.0001 to 0.01% and has a balance of Fe and unavoidable impurities and which has an X-ray diffraction strength in the {100} orientation from a surface layer to t/4 (“t” is sheet thickness) of 2 or more.
摘要:
A high-strength multiphase steel with minimum tensile strengths of 580 MPa, preferably having a dual-phase structure for a cold-rolled or hot-rolled steel strip with improved forming properties, particularly for lightweight vehicle construction contains the elements (contents in mass-%): C 0.075 to ≦0.105; Si 0.600 to ≦0.800; Mn 1.000 to ≦2.250; Cr 0.280 to ≦0.480; Al 0.010 to ≦0.060; P≦0.020; N≦0.0100; S≦0.0150, remainder iron, including typical steel-accompanying elements not mentioned above, which are impurities introduced by smelting, with the condition that the Mn content is preferably ≦1.500% for strip thicknesses up to 1 mm, the Mn content is preferably ≦1.750% for strip thicknesses of 1 to 2 mm, and the Mn content is preferably ≧1.500% for strip thicknesses ≧2 mm