摘要:
A polymeric fiber for use in gas separation is formed from a spin dope which includes solvent and non-solvent materials. The fiber is passed through a quench bath, and then a leach bath, in which the solvent and non-solvent are removed. The quench bath and the leach bath include sets of rollers which transport the fiber through the system. Each set of rollers in the leach bath operates at a speed which is greater than or equal to the speed of the rollers which are immediately upstream. Thus, the fiber is stretched, in different amounts, at the same time that the solvent and non-solvent are being removed, and while the fiber is still wet. The resulting fiber has been found to exhibit superior flux and selectivity properties.
摘要:
An acrylic fiber is composed of an acrylic polymer. The acrylic polymer includes acrylonitrile, wherein the acrylic fiber has a deformation degree of 0.13 or less and a surface roughness of 6000 μm2 or less. A method for producing an acrylic fiber by wet spinning or dry-wet spinning includes: dissolving an acrylic polymer in an organic solvent to form a spinning solution, the acrylic polymer including acrylonitrile; discharging the spinning solution into a coagulation bath to form an acrylic fiber; water washing the acrylic fiber; and drying the acrylic fiber, wherein, before drying the acrylic fiber, the acrylic fiber is pressed with a nip roll and subjected to pre-drying using a dryer into which steam is fed.
摘要:
A polyester fiber that can be used for an airbag fabric is disclosed. The polyester fiber has an elongation of 1.65% to 2.5% when tensile strength of 1.0 g/d is applied after heat treatment at 185° C. for 2 minutes, and additionally elongates in the range of elongation from 0.5% to 5% at the range of tensile strength from 8.0 g/d to the maximum strength. The polyester fiber simultaneously has low initial Young's modulus and excellent mechanical properties, and thus, it may provide excellent packing, dimensional stability, and excellent air cut-off effect, and simultaneously, minimize impact applied to a passenger thus safely protecting a passenger.
摘要:
The invention relates to a yarn comprising a copolyamide in an amount of at least 90 wt % with respect to the total weight of the yarn, which copolyamide comprises a) at least 95 wt % by weight with respect to the total weight of copolyamide, monomeric units derived from hexamethylene diamine and adipic acid and b1) cyclic monomeric units derived from a diamine X, and cyclic monomeric units derived from a diacid Y, and/or b2) cyclic monomeric units derived from an amino acid Z, in which the summed amount of monomeric units derived from X, Y and Z is between 0.1 to 4.5 wt % by weight with respect to the total weight of the copolyamide and wherein the yarn has a tensile strength of at least 80 cN/tex as measured according to ASTM D885-04. The invention also relates to a process for preparing the yarn.
摘要:
A manufacturing method for a transparent fiber is provided. The method includes forming a spinning solution containing a polyimide polymer in an organic solvent. The polydispersity index (PDI) of the polyimide polymer is 1.3˜2.6. The spinning solution is used to perform a dry-jet wet spinning step to form a plurality of fibers. Furthermore, the plurality of fibers are subjected to a thermal drawing step to form a plurality of transparent fibers, wherein the temperature of the thermal drawing step is controlled from 215° C. to 350° C. The manufacturing method for a transparent fiber provided in the present invention makes use of a polyimide polymer material and utilizes a dry-jet wet spinning step and a thermal drawing step, which allows the formation of a transparent and high strength polyimide fiber.
摘要:
Techniques produce a multifilament thread from a polyamide melt. In this case, freshly extruded filaments are cooled and combined to form a thread. In order, in addition to low boil-off shrinkage, to achieve high strength, the thread is taken off at a take-off rate in the range from 3600 m/min to 4600 m/min, preferably from 4000 m/min to 4400 m/min, by a first godet group having unheated guide casings. Subsequently, the thread is fully drawn between the first godet group and a second godet group having heated guide casings. After drawing, the thread is heated to a thread temperature in the range from 140° C. to 200° C. under tension at the guide casings of the second godet group and relaxed. After relaxing, the thread runs in a contact-free manner through at least one free cooling section between the second godet group and a third godet group having unheated guide casings.
摘要:
Disclosed is a high strength polyester fiber for a seat belt, and in particular, a polyester fiber for a seat belt, which has intrinsic viscosity of 0.8 to 1.5 dl/g, tensile strength of 8.8 g/d or more, and total fineness of 400 to 1800 denier. A method of preparing the fiber is disclosed. The polyester fiber includes filaments having high strength, low modulus, and high elongation to significantly lower shrinkage, while securing excellent mechanical properties, it is possible to manufacture a seat belt having excellent impact absorption and significantly improved abrasion resistance and heat resistant strength retention, even with a woven density of 260 yarns/inch or less.
摘要:
A method for manufacturing a dull polyamide 56 fiber includes steps as follows. Bright polyamide 56 chips are provided. A viscosity adjusting step is provided, wherein a relative viscosity in sulfuric acid of the bright polyamide 56 chips is adjusted to a range of 2.90 to 3.00. A moisture adjusting step is provided, wherein a moisture content of the bright polyamide 56 chips is adjusted to a range of 350 to 550 ppm. A spinning step is provided, which includes providing dull polyamide 6 chips and a blending step. The dull polyamide 6 chips include TiO2. In the blending step, the dull polyamide 6 chips and the bright polyamide 56 chips dealt with the viscosity adjusting step and the moisture adjusting step are melted and blended, and then spun at a temperature ranging from 275° C. to 285° C., thus the dull polyamide 56 fiber is obtained.
摘要:
Method for manufacturing structural synthetic fibers for concretes and mortars and the synthetic fiber obtained, particularly a polyolefin-based synthetic fiber for use in concretes and mortars with a hydraulic binder as a cementing base for increasing the elastic modulus of the same which comprises the mixture of polyolefin and additives, the formation of threads, a first stretching process, an alternate series of heating-cooling, collecting the threads in coils and stabilization of the polymerization/cross-linking for two days to one week; the threads are subsequently again subjected to one or several re-stretching phases, including the heating-cooling and subsequent stabilization processes if successive re-stretching processes are going to be carried out; lastly a surface etching phase and the cutting of the threads.
摘要:
Methods and apparatuses for preparing protein fibers (biofilaments) from recombinant biofilament proteins are disclosed. The methods are particularly useful for spinning fibers of spider silk or silkworm silk proteins from recombinant sources and may be used to spin such fibers for use in the manufacture of industrial and commercial products.