摘要:
The present invention relates to an aqueous alkaline composition (A) for alkaline passivation of metallic components comprising at least in part surfaces of zinc or zinc alloys, containing iron(III) ions, phosphate ions, and one or more complexing agents, where a free alkalinity ranges from 1 to 6 points, and the pH is at least 11. The aqueous compositions (A) can additionally contain nonionic surfactants, so that such compositions are suitable for use in a method in which both cleaning and alkaline passivation of the metallic component occur in one step. The present invention further relates to a method for alkaline passivation of metallic components by contacting them with composition (A), and further a method for surface treatment in automobile body production, in which the alkaline passivation step using composition (A) is followed by an acid passivation step using a composition (B).
摘要:
A composition for coating a metal substrate with a white to off-white or gray colored autodeposited coating comprising water, polymeric resin, HF and pigment particles comprising a core of titanium dioxide, an intermediate zirconia and/or alumina layer, and an outer organic layer, optionally the particles are treated with an anionic surfactant.
摘要:
The anticorrosive properties of a coating autodeposited on a metal substrate are improved by contacting the autodeposited coating with an aqueous solution containing Group IIA or Group IIB metal cations (e.g., calcium or zinc cations) and phosphate anions prior to curing. The rinse solution is preferably acidic and can be prepared, for example, from calcium nitrate and an oxy acid of phosphorus or zinc dihydrogen phosphate. Optionally, the rinse solution also includes an accelerator such as hydroxylamine.
摘要:
The anticorrosive properties of a coating autodeposited on a metal substrate are improved by contacting the autodeposited coating with an aqueous solution of an alkaline earth metal compound such as calcium nitrate prior to curing.
摘要:
In at least one embodiment, the present invention relates to a increasing the hydrophilicity of an organic surface. One method in accordance with the present invention includes oxidizing at least a portion of the organic surface to form an oxidized surface portion, and treating the oxidized surfaces portion with an aqueous treatment solution comprising water-soluble and/or water-dispersible polyphenoresin. In at least another embodiment, the present invention relates to preventing the formation of coating defects in polymeric coated surfaces. In at least one embodiment, the present invention relates to increasing paint, ink, and adhesive adhesion.
摘要:
This invention provides an autodeposition bath composition and process capable of coating zinciferous metal surfaces with minimal pinhole formation, comprising (a) at least one polymer, (b) at least one emulsifier, (c) optionally at least one cross-linker, (d) at least one accelerator component such as acid, oxidizing agent and/or complexing agents, (e) an average minimum concentration of H2O2 of at least 100 parts per million, (f) optionally, at least one filler and/or colorant, (g) optionally, at least one coalescing agent, and (h) water.
摘要翻译:本发明提供一种自动沉积浴组合物和方法,其能够以最小的针孔形成涂覆含锌金属表面,其包含(a)至少一种聚合物,(b)至少一种乳化剂,(c)任选的至少一种交联剂,(d )至少一种促进剂组分,例如酸,氧化剂和/或络合剂,(e)H 2 O 2 O 2的平均最低浓度为至少100份/ (f)任选的至少一种填料和/或着色剂,(g)任选的至少一种聚结剂和(h)水。
摘要:
A coating composition comprising an aqueous mixture containing inorganic particles, a catechol compound, and one or more fluoroacids. The preferred fluoroacids are selected from fluorotitanic acid, fluorozirconic acid, fluorosilicic acid, fluoroboric acid, fluorostannic acid, fluorogermanic acid, fluorohafnic acid, fluoroaluminic acid or salts of each thereof. The invention is also directed to a coating on a metal substrate. The coating comprises silica particles attached to the metal substrate through a metal-oxide matrix. The metal-oxide matrix comprises a metal selected from titanium, zirconium, silicon, hafnium, boron, aluminum, germanium, or tin, and a catechol compound.
摘要:
Autodeposited coatings useful for protecting metal surfaces and in production of rubber-to-metal composites are obtained by curing adducts based on epoxy resins which are adhered to the metal surface. One or more epoxy resins, such as for example, the combination of a diglycidyl ether of bisphenol A and a flexibilizing epoxy resin, may be prereacted to form an adduct of higher average molecular weight than the starting epoxy resins. Said adduct may then be dispersed in water, with the resulting dispersion being used in an autodeposition bath composition.
摘要:
Heavy metals are efficiently removed from contaminated soil by a process which comprises leaching or washing the soil with a mild leachant solution comprised of an aqueous solution of an acid and a salt. Heavy metals are also efficiently removed from paint chips by washing with an aqueous acid. The heavy metals are recovered from the leachant be cementation.
摘要:
Heavy metals are efficiently removed from contaminated soil by a process which comprises leaching or washing the soil with a mild leachant solution comprised of an aqueous solution of an acid and a salt. Heavy metals are also efficiently removed from paint chips by washing with an aqueous acid. The heavy metals are recovered from the leachant be cementation.