摘要:
Disclosed is a filler for a heat-sensitive recording paper comprising finely divided amorphous silica having a BET specific surface area of 10 to 100 m.sup.2 /g and a bulk density of 0.14 to 0.30 g/cc, said finely divided amorphous silica having such a secondary particle size distribution that secondary particles having a size smaller than 4 microns, as measured by the centrifugal precipitation method, occupy at least 90% by weight of the total particles.This filler is excellent in the effects of preventing the background coloration, improving the lubricating property, preventing the adhesion of scum and improving the image density.
摘要:
Disclosed is a filler for a heat-sensitive recording paper comprising finely divided amorphous silica having a BET specific surface area of 10 to 100 m.sup.2 /g and a bulk density of 0.14 to 0.30 g/cc, said finely divided amorphous silica having such a secondary particle size distribution that secondary particles having a size smaller than 4 microns, as measured by the centrifugal precipitation method, occupy at least 90% by weight of the total particles.This filler is excellent in the effects of preventing the background coloration, improving the lubricating property, preventing the adhesion of scum and improving the image density.
摘要:
A stabilizer for resin, which is composed of a lithium aluminum complex hydroxide salt represented by the following formulaAl.sub.2 Li(OH).sub.6).sub.n X.mH.sub.2 O . . . (1)wherein X is an inorganic or organic anion, n is a valence number of anion X, and m is a number of not more than 3.A chlorine-containing polymer composition comprising a chlorine-containing polymer and 0.01 to 10 parts by weight, per 100 parts by weight of the chlorine-containing polymer, of the above stabilizer. There is also provided an olefin-type resin composition comprising an olefin-type resin containing halogen-containing catalyst residues and 0.01 to 10 parts by weight, per 100 parts by weight of the olefin-type resin, of the above stabilizer. The stabilizer has excellent heat stabilizing action.
摘要:
An lithium aluminum complex hydroxide salt (LAHS) and a process for preparation thereof is provided. The LAHS is represented by the formula;(Al.sub.2 Li(OH).sub.6).sub.n X, mH.sub.2 Owherein X is an inorganic or organic anion, n is a value number of X, and m is a number of not more than 3, and having an orientation degree (OD) of not less than 10, OD being defined by the formula;OD=I.sub.(002) /I.sub.(110)wherein I.sub.(002) is a relative intensity of a peak in X-ray diffraction pattern with an index of a plane (002) appearing at a spacing (d) of 7.67 .ANG. to 7.84 .ANG. and I.sub.(110) is a relative intensity of a peak in X-ray pattern with an index of a plane (110) appearing at a spacing (d) of 4.41 .ANG. to 4.45 .ANG.. This LAHS is useful for a stabilizer for chlorine-containing polymers or olefin-type resins containing halogen-containing catalyst residues.
摘要:
A stabilizer for resin, which is composed of a lithium aluminum complex hydroxide salt represented by the following formula[Al.sub.2 Li(OH).sub.6 ].sub.n X.mH.sub.2 O (1)wherein X is an inorganic or organic anion, n is a valence number of anion X, and m is a number of not more than 3.A chlorine-containing polymer composition comprising a chlorine-containing polymer and 0.01 to 10 parts by weight, per 100 parts by weight of the chlorine-containing polymer, of the above stabilizer. There is also provided an olefin-type resin composition comprising an olefin-type resin containing halogen-containing catalyst residues and 0.01 to 10 parts by weight, per 100 parts by weight of the olefin-type resin, of the above stabilizer. The stabilizer has excellent heat stabilizing action.
摘要翻译:由下式[Al 2 Li(OH)6] n X.mH 2 O(1)表示的锂铝复合氢氧化物盐组成的树脂稳定剂,其中X是无机或有机阴离子,n是阴离子X的价数 ,m为3以下的数。含有上述稳定剂的含氯聚合物的含氯聚合物组合物,相对于100重量份含氯聚合物,为0.01〜10重量份。 还提供了一种烯烃型树脂组合物,其包含含有含卤素的催化剂残余物的烯烃型树脂和每100重量份的上述稳定剂的烯烃型树脂为0.01至10重量份。 稳定剂具有优异的热稳定作用。
摘要:
Disclosed is an abrasion-resistant granular zeolite formed from a mixture of a synthetic zeolite and a clay binder, said granular zeolite comprising a core composed of a synthetic zeolite clay binder mixture containing the synthetic zeolite at a content higher than the average synthetic zeolite content in the granular zeolite and a shell composed of a synthetic zeolite-clay binder mixture containing the clay binder at a content higher than the average clay binder content in the granular zeolite.This granular zeolite is excellent in both the zeolitic characteristics such as adsorbability and ion exchange capacity and the mechanical strength characteristics such as abrasion resistance and compression strength.
摘要:
A thin and highly transparent coating having excellent air tightness, adhesion to a substrate, lubricating properties, galling resistance, and corrosion resistance is formed on the surface of a metal substrate and particularly on the surface of a threaded joint which is used for connection of oil country tubular goods. A photocurable composition comprising (A) a photocurable (meth)acrylate resin, (B) a (meth)acrylate monomer selected from a monofunctional (meth)acrylate monomer and a difunctional (meth)acrylate monomer, (C) a trifunctional or higher multifunctional (meth)acrylate monomer, (D) a photopolymerization initiator, (E) a benzotriazole anticorrosive agent, (F) an anticorrosive pigment selected from a phosphate anticorrosive pigment and calcium ion-exchanged silica, and (G) a phosphate ester is used to form a photocured coating.
摘要:
In order to provide a tubular threaded joint constituted by a pin and a box each having threads and an unthreaded metal contact portion with excellent galling resistance and gas tightness even in extremely cold environments at −60° C. to −20° C. and rust preventing properties without using a compound grease, a thermoplastic solid lubricating coating containing low friction copolymer particles made from an acrylic-silicone copolymer and preferably further containing a solid lubricant (e.g., graphite) in a thermoplastic polymer matrix (e.g., selected from polyolefin resins and ethylene-vinyl acetate copolymer resins) is formed on the surface of the threads and unthreaded metal contact portion of a pin and/or a box.
摘要:
A chemical conversion treatment liquid which can stably form a phosphate-type chemical conversion film on a steel material for a joint portion of an oil well steel pipe containing 0.5-13% Cr is developed.Using a chemical conversion treatment liquid to which a prescribed amount of potassium is added, a chemical conversion film containing a prescribed amount of potassium compounds and having a prescribed thickness can be formed on the threaded surface of a joint portion of an oil well steel pipe.
摘要:
A threaded joint for steel tubes has a contact surface (30) including a threaded portion and a non-threaded metal-to-metal contact portion. The contact surface of at least one of a pin and a box of the joint is coated with a first plating layer (34) made of a Cu—Zn alloy or a Cu—Zn-M1 alloy (wherein M1 is at least one element selected from Sn, Bi, and In). An undercoat (32) of one or both of a Ni plating layer (32a) and a Cu plating layer (32b) and an overcoat of a Sn-M2 alloy plating layer (36) (wherein M2 is one or more elements selected from Bi, In, Ni, Zn, and Cu) may be formed below and above the first layer, respectively. A solid lubricating coating (38a) and a viscous liquid or semisolid lubricating coating (38b) may also be formed atop the plating layer as a lubricating coating (38).