摘要:
The present invention provides a method of manufacturing a composite material made of a rubber and a clay mineral dispersed uniformly therein. The method proceeds exchanging inorganic ions of the clay mineral with organic onium ions to organize the clay mineral; mixing the organized clay mineral and a process oil and/or a plasticizer; and mixing the rubber material with the mixture of the organized clay mineral and the process oil and/or the plasticizer. Process oil and/or plasticizer are intercalated into the organized clay mineral. As a result, the interlayer distance of the clay mineral is enlarged. The most favorable mode of the present invention is for a barrier material against water, gas and the like and for a rubber material required for an improved mechanical property.
摘要:
Devulcanized rubber in which sulfuric crosslinking bonds are cut and which contains carbon black particles having very small diameters. Vulcanized rubber of discarded products is devulcanized by heating it at a temperature of 180.degree. C. --350.degree. C. and applying a shearing pressure of 10-150 kg/cm.sup.2 thereto. Reclaimed rubber products are manufactured by vulcanizing and molding, into desired shapes, a material made of only devulcanized rubber in which sulfuric crosslinking bonds are cut and which contains carbon black particles having very small diameters or a material made of the devulcanized rubber mixed with virgin unvulcanized rubber.
摘要翻译:其中硫酸交联键被切割并含有具有非常小直径的炭黑颗粒的脱硫橡胶。 将废弃产品的硫化橡胶在180℃-350℃的温度下加热并对其施加10-150kg / cm 2的剪切压力进行脱硫。 再生橡胶制品通过硫化和成型制成所需形状的仅由硫化交联键切割并含有非常小直径的炭黑颗粒的脱硫橡胶制成的材料或由脱硫硫化橡胶混合的原料未硫化的材料 橡胶。
摘要:
A phenolic resin composite material includes a phenolic resin, a filler dispersed in the phenolic resin and being a reinforcement member and an organized layered clay mineral being different from the filler and dispersed uniformly in the phenolic resin. The phenolic resin composite material is improved in terms of the heat resistance as well as the mechanical strengths.
摘要:
A composite clay material with the interlayer distance sufficiently expanded by dispersing clay mineral in a low polar polymer on a molecular level and the method for producing the same, blend material and composite clay rubber material using the same and the production method thereof.The composite clay material is formed of a clay mineral rendered compatible with an organic material through ionic bonding to an organic onium ion having 6 or more carbon number and a main guest molecule having a polar group in its main chain and side chain and molecular length equal to or larger than that of said organic onium ion. The main guest molecule is incorporated at least partially into an interlayer section of the clay mineral which has a hydrogen bonding with the polar group of the main guest molecule. The main guest molecule preferably has a molecular weight ranging from about 100 to 100000. Alternatively a first guest molecule having a polar group and molecular length equal to or smaller than that of the organic onium ion and a second guest molecule having no polar group therein and molecular length larger than that of the organic onium ion are incorporated into the interlayer section of the clay mineral instead of the main guest molecule. The above obtained clay composite material may be mixed with the rubber material.
摘要:
A composite clay material with the interlayer distance sufficiently expanded by dispersing clay mineral in a low polar polymer on a molecular level and the method for producing the same, blend material and composite clay rubber material using the same and the production method thereof. The composite clay material is formed of a clay mineral rendered compatible with an organic material through ionic bonding to an organic onium ion having 6 or more carbon number and a main guest molecule having a polar group in its main chain and side chain and molecular length equal to or larger than that of said organic onium ion. The main guest molecule is incorporated at least partially into an interlayer section of the clay mineral which has a hydrogen bonding with the polar group of the main guest molecule. The main guest molecule preferably has a molecular weight ranging from about 100 to 100000. Alternatively a first guest molecule having a polar group and molecular length equal to or smaller than that of the organic onium ion and a second guest molecule having no polar group therein and molecular length larger than that of the organic onium ion are incorporated into the interlayer section of the clay mineral instead of the main guest molecule. The above obtained clay composite material may be mixed with the rubber material.
摘要:
A composite clay material with the interlayer distance sufficiently expanded by dispersing clay mineral in a low polar polymer on a molecular level and the method for producing the same, blend material and composite clay rubber material using the same and the production method thereof.The composite clay material is formed of a clay mineral rendered compatible with an organic material through ionic bonding to an organic onium ion having 6 or more carbon number and a main guest molecule having a polar group in its main chain and side chain and molecular length equal to or larger than that of said organic onium ion. The main guest molecule is incorporated at least partially into an interlayer section of the clay mineral which has a hydrogen bonding with the polar group of the main guest molecule. The main guest molecule preferably has a molecular weight ranging from about 100 to 100000. Alternatively a first guest molecule having a polar group and molecular length equal to or smaller than that of the organic onium ion and a second guest molecule having no polar group therein and molecular length larger than that of the organic onium ion are incorporated into the interlayer section of the clay mineral instead of the main guest molecule. The above obtained clay composite material may be mixed with the rubber material.
摘要:
A metal ion coordinated complex crystal is composed of cation of a nitrogen-containing heterocyclic aromatic compound, anion of triiodine and metal ion. The complex crystal can be used as light-polarizing particles having a stable and strong polarizability which is resistant to ultra violet, an excellent heat resistance, excellent moisture resistance and excellent insolubility.
摘要:
A liquid crystal composition comprising a liquid crystal and a second substance dispersed therein, the second substance having affinity for the liquid crystal and being composed of particles having a particle size and an aspect ratio of a predetermined value or greater, and a liquid crystal composition comprising a liquid crystal containing electric field sensitive liquid crystal molecules having a positive dielectric anisotropy as the principal component and flat plate-shaped particles having affinity for the liquid crystal being dispersed therein at such a degree of density suitable for effectively forming liquid crystal domains. Also described are a liquid crystal device using the same, a light-controlling element, a recording medium, and a light shutter.
摘要:
Disclosed herein is a polyimide composite material which comprises a polyimide-containing resin and a layered clay mineral which is intercalated with organic onium ions and dispersed in the polyimide. Owing to the intercalated clay mineral, the composite material has improved gas and water vapor barrier properties and a small thermal expansion coefficient. Disclosed also herein is a process for producing a polyimide composite material which comprises the steps of intercalating a layered clay mineral with organic onium ions, adding by mixing the intercalated clay mineral to a solution of a monomer or prepolymer for polyimide, removing the solvent, and forming a polyimide. This process makes the layered clay mineral miscible with and dispersible in polyimide.
摘要:
Composite material with high mechanical strength and excellent high-temperature characteristics comprising a polymer matrix containing polyamide and layers of a silicate uniformly dispersed in the order of molecules in the polymer matrix, each of said silicate layers being 7 to 12 Å thick and the interlayer distance being at least 20 Å; and a process for manufacturing such composite material.