摘要:
A method for producing a steel component with a metallic anti-corrosion coating from a sheet steel product comprising at least 0.4% by weight Mn is disclosed. The sheet steel product is annealed in a continuous furnace under an annealing atmosphere containing up to 25% by volume H2, 0.1% to 10% by volume NH3, H2O, N2, and process-related impurities as the remainder, at a dew point between −50° C. and −5° C. at a temperature of 400 to 1100° C. for 5 to 600 s. The annealed sheet steel product has a 5 to 200 μm thick nitration layer with a particle size finer than the particle size of the inner core layer. Once coated with a metallic protective layer, a blank is separated from the annealed sheet steel product, heated to an austenitising temperature of 780 to 950° C., hot-formed, and cooled so that a hardened structure forms.
摘要:
The present invention relates to a method for the manufacture of galvannealed metal sheet, wherein a hot strip is produced from an IF steel containing 0.01 to 0.1 wt. % silicon, wherein the hot strip is coiled at a coiler temperature no lower than 700° C. and no higher than 750° C., wherein a cold strip is rolled from the coiled hot strip, wherein the cold strip is recrystallization-annealed in an annealing furnace in an annealing gas atmosphere, wherein the cold strip thus annealed is provided with a zinc coating in a zinc bath, and wherein the coated cold strip is post-annealed at a galvannealing temperature no lower than 500° C. and no higher than 540° C. The invention also relates to a galvannealed metal sheet which possesses improved adhesion of the coating layer to the base material and proposes a method which is suited for the manufacture of metal sheet having such properties.
摘要:
A method by which a flat steel product containing 2-35 wt. % of Mn can be provided with a coating of Zn which adheres well by annealing at an annealing temperature Ta of 600-1100° C. for an annealing time of 10-240 s under an annealing atmosphere which has a reducing effect on the FeO present on the flat steel product and an oxidizing effect on the Mn contained in the steel substrate thereby forming a layer of Mn mixed oxide which covers the flat steel product at least in sections and then cooling the flat steel product to a temperature for bath entry and conveying it through a bath of molten Zn saturated within iron at a temperature of 420-520° C., within a dip time of 0.1-10 s.
摘要:
A method by which a flat steel product containing 2-35 wt. % of Mn can be provided with a coating of Zn which adheres well by annealing at an annealing temperature Ta of 600-1100° C. for an annealing time of 10-240 s under an annealing atmosphere which has a reducing effect on the FeO present on the flat steel product and an oxidising effect on the Mn contained in the steel substrate thereby forming a layer of Mn mixed oxide which covers the flat steel product at least in sections and then cooling the flat steel product to a temperature for bath entry and conveying it through a bath of molten Zn saturated within iron at a temperature of 420-520° C., within a dip time of 0.1-10 s.
摘要:
A readily formable flat steel product has a ductile edge layer that is from 10 to 200 μm thick and has a ductility greater than a ductility of an inner core layer of the flat steel product. The readily formable flat steel product is produced by annealing a flat steel product having a C content of from 0.1 to 0.4% by weight in a continuous furnace. The annealing is carried out under an annealing atmosphere that contains from 0.1 to 25% by vol. of H2 and H2O, with the balance being N2 and technically unavoidable impurities. A dew point is between −20° C. and +60° C., and a ratio of H2O/H2 is a maximum of 0.957. In the course of the annealing, the flat steel product is heated to a holding temperature of from 600 to 1100° C. and for a holding time of from 10 to 360 seconds.
摘要:
A readily formable flat steel product has a ductile edge layer that is from 10 to 200 μm thick and has a ductility greater than a ductility of an inner core layer of the flat steel product. The readily formable flat steel product is produced by annealing a flat steel product having a C content of from 0.1 to 0.4% by weight in a continuous furnace. The annealing is carried out under an annealing atmosphere that contains from 0.1 to 25% by vol. of H2 and H2O, with the balance being N2 and technically unavoidable impurities. A dew point is between −20° C. and +60° C., and a ratio of H2O/H2 is a maximum of 0.957. In the course of the annealing, the flat steel product is heated to a holding temperature of from 600 to 1100° C. and for a holding time of from 10 to 360 seconds.
摘要:
A method for producing a steel component provided with a metallic coating which protects against corrosion, in which a steel flat product, produced from an alloyed heat-treated steel, is coated with an Al coating which contains ≧85% wt. Al and optionally ≦15% wt. Si, a Zn coating with ≧90% wt. Zn, and a top layer, the main constituent of which is at least one metal salt of phosphoric acid or diphosphoric acid and which additionally can contain contents of up to 45% of an Al:Zn ratio as well as optionally metal oxides, metal hydroxides and/or sulphur compounds, the steel flat product is heat treated at ≧750° C., and the steel component is hot-formed from the heated steel flat product. The hot-formed steel component is cooled at a cooling rate sufficient to form a tempered or martensitic structure.
摘要:
Coating steel strips comprising, in % by weight, C: ≦1.6%, Mn: 6-30%, Al: ≦10%, Ni: ≦10%, Cr: ≦10%, Si: ≦8%, Cu: ≦3%, Nb: ≦0.6%, Ti: ≦0.3%, V: ≦0.3%, P: ≦0.1%, B: ≦0.01%, the rest being iron and unavoidable impurities, and a method of forming steel strips are described. Up to now, such steel strips were not adequately coatable, with a metal coating ensuring outstanding corrosion-resistance and good welding properties. This is ensured by applying an aluminium layer to the steel strip before final annealing and applying the metal coating to said aluminium layer after final annealing.
摘要:
A method by which a steel component can be produced, which is provided with a metallic coating which adheres well and which provides protection against corrosion, from a flat steel product produced from a steel material containing 0.3-3 wt.-% manganese and having a yield point of 150-1100 MPa and a tensile strength of 300-1200 MPa coated with an anti-corrosion coating which comprises a coating of ZnNi alloy which is electrolytically deposited on the flat steel product, which coating is composed in a single phase of γ-ZnNi phase and which contains, as well as zinc and unavoidable impurities, 7-15 wt.-% nickel.
摘要:
A flat steel product which is provided for forming into a component by hot pressing and which has a base layer of steel on which is applied a Zn or a Zn alloy metallic protective coating for protecting against corrosion. On at least one of the free surfaces of the flat steel product, a separate cover layer is applied which contains an oxide, nitride, sulphide, carbide, hydrate or phosphate compound of a base metal. In addition, a method which allows the production of such a flat steel product, and a method which allows the production of a component from such a flat steel product.