摘要:
A treated refractory material includes a porous refractory material having one or more protective materials disposed within pores of the refractory material. Methods of preparing the treated refractory material are also provided. The treated refractory material provides protection from the penetration of slag and extends the service life of the refractory material.
摘要:
The present invention relates to a corrosion resistant member including: a substrate composed of a ceramic or a metal, and at least one layer of a corrosion resistant film formed on a surface of at least a region of the substrate to be exposed to plasma or a corrosive gas, in which the corrosion resistant film contains yttria as a main component and further also contains at least one of tantalum and niobium in an amount of 0.02 to 10 mol % in terms of pentoxide relative to the yttria, and a non-melted portion is not present in the corrosion resistant film.
摘要:
A bond layer for a silicon based substrate comprises a mixture of a first phase and a second phase, wherein the first phase is selected from the group consisting of refractory metal oxides, refractory metal silicates and mixtures thereof and the second phase is selected from the group consisting of refractory metal oxide forming metals, SiC, Si3N4, and mixtures thereof.
摘要翻译:用于硅基底层的接合层包括第一相和第二相的混合物,其中第一相选自难熔金属氧化物,难熔金属硅酸盐及其混合物,第二相选自 由难熔金属氧化物形成金属,SiC,Si 3 N 4,及其混合物组成。
摘要:
A process for preparing a silicon based substrate with a protective coating having improved thermal resistance at temperature up to at least 1500° C., and the resulting article.
摘要:
An article comprising a substrate formed of a silicon-comprising material, such as an article exposed to the hostile thermal environment of a gas turbine engine. The article further comprises an environmental barrier layer, e.g., an alkaline earth metal aluminosilicate, and a top coat comprising zirconia or hafnia stabilized with an oxide of a metal selected from the group consisting of magnesium, calcium, scandium, yttrium, and lanthanide metals, and mixtures thereof. The article further comprises a transition layer between the environmental barrier layer and the top coat, the transition layer comprising zirconia or hafnia stabilized with an oxide of a metal selected from the group consisting of magnesium, calcium, scandium, yttrium, and lanthanide metals; and a low CTE oxide selected from the group consisting of niobia and tantala; and mixtures thereof. A method for preparing a thermal/environmental barrier coating system on a substrate formed of a silicon-comprising material is also disclosed.
摘要:
A barrier layer for a silicon containing substrate which inhibits the formation of gaseous species of silicon when exposed to a high temperature aqueous environment comprises a barium-strontium aluminosilicate includes an aluminosilicate of Group IIA and/or Group IIIB and a Group VB oxide.
摘要:
An outer peripheral coating member contains first particles containing titanium oxide, second particles containing zirconium oxide, third particles containing niobium oxide or aluminum oxide, and a dispersion medium. It is preferable for the first particles to have at least two peak values R1 in a distribution of particle sizes of the first particles. One of the peak values R1 is within a range of 1 to 50 nm, and the other peak value R1 is within a range of 100 to 500 nm.
摘要:
A method for manufacturing a corrosion resistant member that includes a substrate including a ceramic or a metal, and at least one layer of a corrosion resistant film formed on a surface of at least a region of the substrate to be exposed to plasma or a corrosive gas. The corrosion resistant film contains yttria as a main component and further contains at least one of tantalum and niobium in an amount of 0.02 mol % to 10 mol % in terms of pentoxide relative to the yttria, and a non-melted portion is not present in the corrosion resistant film. The method includes mixing a raw material powder of yttria with a raw material powder of at least one of a tantalum oxide and a niobium oxide, followed by granulating the raw material powders to obtain a granulated powder.
摘要:
An article comprising a substrate formed of a silicon-comprising material, such as an article exposed to the hostile thermal environment of a gas turbine engine. The article further comprises an environmental barrier layer, e.g., an alkaline earth metal aluminosilicate, and a physical barrier layer overlying the environmental barrier layer. The physical barrier layer comprises zirconia or hafnia stabilized with an oxide of a metal selected from the group consisting of magnesium, calcium, scandium, yttrium, and lanthanide metals; and a low CTE oxide selected from the group consisting of niobia and tantala; and mixtures thereof. A method for preparing an environmental barrier coating system on a substrate formed of a silicon-comprising material is also disclosed.
摘要:
A thin film comprising a pyrochlore represented by the formula: (Bi3xZn2−3x)(ZnxNb2−x)O7 wherein x is from about 0.45 to about 0.73 and an article comprising a substrate and, coated on the substrate, a thin film of the pyrochlore are provided. Also provided is a process for depositing on a substrate the above pyrochlore thin film. The process includes the steps of coating the substrate with a composition comprising bismuth carboxylate, zinc carboxylate, niobium alkoxide, an organic solvent, an organic acid and an organic base, heating to remove organic components and annealing at a temperature and for a length of time sufficient to produce the pyrochlore thin film on the substrate.