摘要:
Provided is an ultra-high-strength steel sheet having high phosphatability and hole expandability, including, by wt %, carbon (C): 0.08% to 0.2%, silicon (Si): 0.05% to 1.3%, manganese (Mn): 2.0% to 3.0%, phosphorus (P): 0.001% to 0.10%, sulfur (S): 0.010% or less, aluminum (Al): 0.01% to 0.1%, chromium (Cr): 0.3% to 1.2%, boron (B): 0.0010% to 0.0030%, titanium (Ti): 0.01% to 0.05%, nitrogen (N): 0.001% to 0.01%, and a balance of iron (Fe) and inevitable impurities, satisfying 3.4≤Ti/N≤10, 1.0≤Mn/(Si+Cr), and 0.7≤Mn*/(Si*+Cr*)≤Mn/(Si+Cr) where Ti, N, Mn, Si, and Cr refer to a weight percent (wt %), and Mn*, Si*, and Cr* refer to an average of values obtained by GDS component analysis from the surface to the 0.1 μm position in the thickness direction.
摘要:
A low-alloy and corrosion-resistant steel for a vehicle, may include about 0.001 wt % to about 0.1 wt % of C, about 0.01 wt % to about 0.5 wt % of Si, about 0.1 wt % to about 0.6 wt % of Mn, more than 0 wt % and about 0.18 wt % or less of P, more than 0 wt % and less than about 0.02 wt % of S, about 0.001 wt % to about 0.03 wt % of Nb, more than 0 wt % and about 0.03 wt % or less of Cr, about 0.05 wt % to about 0.3 wt % of Cu, about 0.05 wt % to about 0.2 wt % of Ni, and more than 0 wt % and about 0.2 wt % or less of a combined weight of Sn and Sb, and the balance iron and inevitable impurities.
摘要:
There is provided a separator for polymer electrolyte fuel cells having a substrate of a ferritic, having a chemical composition comprising, in mass %, C: 0.001 to 0.012%, Si: 0.01 to 0.6%, Mn: 0.01 to 0.6%, P: 0.035% or less, S: 0.01% or less, Cr: 22.5 to 35.0%, Mo: 0.01 to 4.5%, Ni: 0.01 to 2.5%, Cu: 0.01 to 0.6%, Sn: 0.01 to 1.0%, In: 0.001 to 0.30%, N: 0.015% or less, V: 0.01 to 0.35%, and Al: 0.001 to 0.050%, and the calculated value of {Content of Cr (%)+3×Content of Mo (%)} being 22.5 to 45.0, and includes a surface modified layer containing O: less than 30% and the balance: Sn and In. A polymer electrolyte fuel cell including the separator is remarkably excellent in corrosion resistance in an in-cell environment.
摘要:
A steel sheet contains C: 0.15% to 0.22%, Si: 1.0% to 2.0%, Mn: 1.7% to 2.5%, P: 0.05% or less, S: 0.02% or less, Al: 0.01% to 0.05%, N: 0.005% or less, O: 0.01% or less, and the balance being iron and unavoidable impurities while satisfying [Si]/[Mn]≧0.5 ([Si] and [Mn] represent Si and Mn contents, wherein the steel sheet has a structure including, in terms of area fraction, 60% to less than 100% of tempered martensite, 5% or less including 0% of untransformed austenite, and the balance being ferrite, and the ferrite has an average crystal grain size of less than 3.5 μm, wherein less than 10 particles/100 μm2 of Si—Mn compound oxide particles having a circle equivalent diameter of 5 μm or less are present on a surface of the steel sheet, and the surface is covered with Si-based oxide at a coverage of 1% or less.
摘要:
A high-strength plated steel sheet has a plated layer on the surface of a base steel sheet and contains predetermined steel components. The steel sheet includes, in the order from the interface of the base steel sheet and the plated layer towards the base steel sheet: a soft layer having a Vickers hardness that is 90% or less of the Vickers hardness at a portion t/4 of the base steel sheet, where t is a sheet thickness of the base steel sheet; and a hard layer containing martensite and bainite, and ferrite in predetermined ranges. The average depth D of the soft layer is 20 μm or greater, and the average depth d of an internal oxide layer is 4 μm or greater and smaller than D.
摘要:
A synthetic acid composition for use in oil industry activities, said composition comprising: urea and hydrogen chloride in a molar ratio of not less than 0.1:1 and formic acid or a derivative thereof.
摘要:
The present invention provides a cold-rolled and annealed steel sheet with a strength greater than 1200 MPa, the composition of which includes, the contents being expressed by weight: 0.10%≦C≦0.25%, 1%≦Mn≦3%, A≧0.010%, Si≦2.990%, S≦0.015%, P≦0.1%, N≦0.008%, it being understood that 1%≦Si+Al≦3%, it being understood that Cr+3Mo≧0.3%, Ti in an amount such that Ti/N≧4 and Ti≦0.040%. A balance of the composition includes iron and inevitable impurities resulting from the smelting. The microstructure of the steel includes 15 to 90% bainite, the remainder includes martensite and residual austenite.
摘要:
A composition including HCl, urea, complex substituted keto-amine-hydrochloride, an alcohol, an ethoxylate, and a ketone is provided in a method for solubilizing calcium carbonate in an aqueous suspension or dispersion of calcium carbonate.
摘要:
The present invention relates to an acidic aqueous solution suitable for the pickling of stainless steel grades that comprises accelerators based on water soluble inorganic compounds comprising at least one nitrogen atom in an oxidation state in the range of −2 to −⅓. The present invention further encompasses a process for the pickling of stainless steel that makes use of a pickling solution comprising the above-mentioned accelerators.
摘要:
A method for coating a hot-rolled or cold-rolled steel flat product, containing 6-30% wt. Mn, with a metallic protective layer by hot-clip coating in a melt bath. The coating, achieved with increased production reliability, is optimised by the steel flat product being subjected to a pickling treatment in which the manganese oxide adhering to the steel flat product is essentially fully removed in the pickling bath before the steel flat product enters the melt bath.