摘要:
A pasty single component polyurethane adhesive is provided. The NCO terminated polyurethane prepolymer is substantially linear, contains from 2.0% to 8.0% based on the weight of the prepolymer, of highly disperse silica and up to 10% by weight, based on the weight of the prepolymer, of additives. The one component adhesive has an Expressed Volume of at least 2,000 g/min measured according to DIN EN 29048 and a Creep Resistance measure according to DIN EN 27390 below 6.0 after 5 minutes.
摘要翻译:提供糊状单组分聚氨酯粘合剂。 NCO封端的聚氨酯预聚物基本上是线性的,含有基于预聚物重量的2.0%至8.0%,高分散二氧化硅和基于预聚物重量的至多10%重量的添加剂。 单组分粘合剂具有根据DIN EN 29048测量的至少2000g / min的表现体积和5分钟后根据DIN EN 27390的蠕变电阻测量值。
摘要:
This invention relates to a jointing compound of an acrylate/acrylonitrile copolymer containing 2 to 8 carbon atoms in the alcohol component as binder and fatty compounds as plasticizer and also fillers and auxiliaries. Epoxystearic acid methyl ester in particular may be used as the fatty compound while a butyl acrylate/acrylonitrile copolymer in particular may be used as the acrylate/acrylonitrile copolymer. The combination of the two substances results in jointing compounds characterized by a dramatic improvement in elasticity (resilience). Accordingly, they are particularly suitable for substrates with different coefficients of thermal expansion.
摘要:
A hydraulic setting composition is provided. The composition when set has improved water absorption properties. The composition contains a hydraulically setting inorganic material such as calcium sulfate and an auxiliary of the formula A(—X[—CH2]p—ZY)k where A can be a linear or branched C1-24 alkyl group, a linlear or branched C2-24 alkenyl group each of which can be unsubstituted or substituted with 1 to 4 OH group, C6-24 aryl group and alkyl substituted C6-24 aryl groups each; having a valance K, Z is SO3 or COO−, Y is a proton, a metal ion or ammonium, P is from 1 to 30 and X is identical or different and can be where n is from 0-30, m is from 2 to 8, K is from 1 to 4, q is from 1-10, L is O, S or UR3, R2 and R3 are identical or different, linear or branched C1-12 alkyl or a polymer having a molecular weight (Mn) of at least 300 and contains anionic, cationic or anionic and cationic monomer units.
摘要:
Polymerization of a fatty acid or fatty acid derivatives containing conjugated double bonds and alkenes or alkynes containing electron acceptor substituents provides compositions useful as coatings, adhesives, sealants, fillers and the like.
摘要:
Described is an NCO-group-containing polyurethane prepolymer madefrom polyisocanyates and polyols derived from natural oils. The invention is characterized in that the polyol is obtained by transesterification in the presence of basic lithium compounds. Together with a tertiary amine used to accelerate the moisture curing, the storage stability is thus increased considerably. Up to 4.0 mmol of the lithium compound is used per kilogram of polyol, and 0.1 to 2.0% by wt. of the amine, relative to the total weight of the composition, is used as the accelerator. The polyurethane prepolymer is suitable not only for the production of adhesives but also for the production of foamed materials, in particular those dispensed from throw-away pressure vessels.
摘要:
The process of curing a radical-polymerizable multicomponent mixture containing an olefinically-unsaturated compound with ambient air by adding to the mixture an alkyl, cycloalkyl or aryl hydrazone of an aliphatic, cycloaliphatic or aromatic aldehyde or ketone which forms a hydroperoxide as an initiator for curing the mixture.
摘要:
The invention relates to polyurethane compositions with a low content of monomeric diisocyanates. Trifunctional isocyanates optionally reduced in their functionality to 3.0.+-.0.7 with a monofunctional terminator are preferably used for this purpose. In this way, the compositions contain considerably smaller quantities of readily volatile isocyanates. The compositions are suitable for use as reactive hotmelt adhesives, lamination adhesives, adhesive/sealing compounds, primers and for the production of foam plastics from non-reusable pressurized containers (aerosol cans). The low content of volatile monomeric diisocyanates enables the need for safety measures in the workplace to be significantly reduced, in addition to which the disposal of residues remaining in the containers is made considerably easier.
摘要:
The invention relates to a process for the production of plastics containing amide groups with elimination of CO.sub.2 by reaction of polyfunctional isocyanates, carboxylic acids and, optionally, alcohols in the presence of tertiary amines, more particularly heteroaromatic amines. The heteroaromatic amines preferably contain another heteroatom and/or substituents having +I and/or +M effects. The reaction preferably starts at room temperature. Fine-cell foams having an acid value of less than 40 and a density of at most 150 g/l can be produced in short reaction times at room temperature without any need for additional blowing agents.
摘要:
The invention relates to an adhesive tape comprising a support that is provided with a first and a second face. Said support is embodied as an acrylate foam tape while the first face and the second face are provided with at least two respective segments which are coated with different adhesives. At least one first adhesive is provided with great initial tack while at least one second adhesive is provided with great final tack.
摘要:
Two-sided adhesive strips for detachable bonding without residue or damage. The strips include a foam backing fixed to at least one essentially non-elastic layer. The bond is detached by rotative or shear force breaking the foam backing in two parts that remain attached to the bonded surfaces. The residues are removable by pulling at an angle greater than 45° from the bond plane. The strips have high load capacity and bearing strength.